Impermeable electroform for hot isostatic pressing
Assignee: RTX Corp
•
Filing: 1979-08-22
•
Granted: 1981-11-17
•
Expires: 1999-08-22
Abstract
Abstract A metal electroform suitable for hot isostatic pressing (HIP) of metal powders and the fabrication process therefor is disclosed. Ordinary nickel electroplate is permeable to gases during HIP, e.g., at 1200° C. and 100 MPa. An exemplary improved container is comprised of a first electroplated layer of nickel, a second layer of copper and a third layer of nickel, wherein the container has been heated to about 1150° C. and then cooled, to cause fusing of the second lower melting point layer. During fusing there is limited alloying between the layers, the first and third layers retaining the desired container shape.
Inventors
- 👤 Peter A. Hurwitz
- 👤 Joseph F. Loersch
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:57
CPC Classifications
B; B22; B22F; B22F3/00; B22F3/12; B22F3/1208; B22F3/1258; B22F3/1275; B22F3/1216; B22F3/1241; C; C25; C25D; C25D1/00; C25D1/003
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
137 words
The method of forming an impermeable free-standing metal structure from deposited metals which comprises: providing a pattern with a conductive surface; depositing a first metal layer with a first melting point on the pattern surface; depositing a second metal layer having a second melting point upon the first layer to create a two-layer metal structure, the layers having the capability of alloying; removing the pattern from the metal structure; heating the metal structure to a temperature of at least 1100° C. to melt at least a portion of one of the layers, the other layer remaining substantially unmelted to provide structural support for the metal structure, to maintain its shape during heating; and cooling the structure to solidify the melted layer and thereby make the structure impermeable to gases at pressure of the order of 100 MPa.
Claim 2
Independent Claim
137 words
The method of forming an impermeable free-standing metal structure from deposited metals which comprises: providing a pattern with a conductive surface; depositing a first metal layer with a first melting point on the pattern surface; depositing a second metal layer having a second melting point upon the first layer to create a two-layer metal structure, the layers having the capability of alloying; removing the pattern from the metal structure; heating the metal structure to a temperature of at least 1100° C. to melt at least a portion of one of the layers, the other layer remaining substantially unmelted to provide structural support for the metal structure, to maintain its shape during heating; and cooling the structure to solidify the melted layer and thereby make the structure impermeable to gases at pressure of the order of 100 MPa.
Claim 3
Independent Claim
219 words
The method of forming an impermable free-standing metal structure from deposited layers which comprises providing a pattern with a conductive surface; depositing a first metal layer with a first melting point on the pattern surface; depositing a second metal layer, having a second melting point upon the first layer; depositing a third metal layer having a third melting point upon the second layer, wherein the first and third melting points are higher than the second melting point, thereby forming a three-layer metal part which is permeable to gases at pressure of the order of 100 MPa; removing the pattern to produce a free-standing metal part consisting only of deposited layers; heating the metal part comprised of the three layers to a temperature of at least 1100° C., sufficient to melt at least a portion of the second layer but insufficient to cause melting of at least a portion of one of the first or third layers, the melting in the second layer occurring at a temperature greater than 1100° C. and causing a degree of alloying between at least two of the adjacent layers, and the unmelted portions thereby maintaining the shape of the part; and then cooling the part to solidify the melted portions, to make it impermeable to gases at pressures of the order of 100 MPa.
Claim 4
Independent Claim
219 words
The method of forming an impermable free-standing metal structure from deposited layers which comprises providing a pattern with a conductive surface; depositing a first metal layer with a first melting point on the pattern surface; depositing a second metal layer, having a second melting point upon the first layer; depositing a third metal layer having a third melting point upon the second layer, wherein the first and third melting points are higher than the second melting point, thereby forming a three-layer metal part which is permeable to gases at pressure of the order of 100 MPa; removing the pattern to produce a free-standing metal part consisting only of deposited layers; heating the metal part comprised of the three layers to a temperature of at least 1100° C., sufficient to melt at least a portion of the second layer but insufficient to cause melting of at least a portion of one of the first or third layers, the melting in the second layer occurring at a temperature greater than 1100° C. and causing a degree of alloying between at least two of the adjacent layers, and the unmelted portions thereby maintaining the shape of the part; and then cooling the part to solidify the melted portions, to make it impermeable to gases at pressures of the order of 100 MPa.
Claim 5
Independent Claim
24 words
The method of claims 1 or 2 wherein the first and third layers are formed of identical material and are about the same thickness.
References Cited (Backward Citations)
US1397785A
Cited
US2280865A
Cited
US2428033A
Cited
US3364064A
Cited
US3708866A
Cited
US3675311A
Cited
US3854194A
Cited
US4065303A
Cited
US4092448A
Cited
US4023966A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-16 | 1985-05-18 | 1985-11-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-16 | 1989-05-18 | 1989-11-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-16 | 1993-05-18 | 1993-11-17 | $7700.00 | Window Closed / Lapsed |