Method of producing Josephson elements of the tunneling junction type
Assignee: Fujitsu Ltd
•
Filing: 1979-12-19
•
Granted: 1981-11-10
•
Expires: 1999-12-19
Abstract
Abstract In a method of producing a Josephson element of the tunneling junction type comprising the steps of forming the first electrode by utilizing a photoresist film, forming a barrier oxide film on the first electrode by an rf oxygen glow discharge process and forming the second electrode, the improvement wherein immediately after depositing a film of super-conductor material to form the first electrode film, the superconducting material film is oxidized in the same apparatus in which the superconducting material was deposited.
Inventors
- 👤 Hideo Suzuki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 18:12
CPC Classifications
H; H10; H10N; H10N60/00; H10N60/10; H10N60/12; H10N60/01; H10N60/0912; Y; Y10; Y10S; Y10S505/00; Y10S505/80; Y10S505/815; Y10S505/816; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49014
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
168 words
In a method of producing a Josephson element of the tunneling junction type comprising the steps of forming a first electrode of the element on a substrate, by deposition of a first superconductor material layer in an evacuated apparatus for film deposition by utilizing a first photoresist film, forming a barrier oxide film on said first electrode, and forming a second electrode of the element by deposition of a second superconductor material layer on said barrier oxide film by utilizing a second photoresist film, the improvement comprising: immediately after the deposition in said deposition apparatus of the first superconducting material film of said first electrode, oxidizing the upper portion of said superconducting material film in the same said deposition apparatus, prior to removing said substrate from said deposition apparatus thereby avoiding exposing said first superconducting material to undesired contamination and oxidation, subsequently controllably forming said barrier oxide film to a predetermined thickness by an rf oxygen glow discharge process having both a sputter-etching effect and an oxidizing effect.
Claim 2
Dependent Claim
168 words
In a method of producing a Josephson element of the tunneling junction type comprising the steps of forming a first electrode of the element on a substrate, by deposition of a first superconductor material layer in an evacuated apparatus for film deposition by utilizing a first photoresist film, forming a barrier oxide film on said first electrode, and forming a second electrode of the element by deposition of a second superconductor material layer on said barrier oxide film by utilizing a second photoresist film, the improvement comprising: immediately after the deposition in said deposition apparatus of the first superconducting material film of said first electrode, oxidizing the upper portion of said superconducting material film in the same said deposition apparatus, prior to removing said substrate from said deposition apparatus thereby avoiding exposing said first superconducting material to undesired contamination and oxidation, subsequently controllably forming said barrier oxide film to a predetermined thickness by an rf oxygen glow discharge process having both a sputter-etching effect and an oxidizing effect.
Claim 3
Dependent Claim
28 words
The method of claim 1 comprising selectively performing said immediate oxidizing of said superconducting material film by thermal oxidation, dc oxygen glow discharge, or rf oxygen glow discharge.
Claim 4
Dependent Claim
59 words
The method of claim 1, wherein said controlled forming of the thickness of said barrier oxide film by said rf oxygen glow discharge is at an oxygen pressure of from 1×10 -3 to 1×10 -1 Torr at an rf power density of from 5×10 -3 to 2×10 -1 W/cm 2 for a period of from 1 to 30 minutes.
Claim 5
Dependent Claim
29 words
The method of claim 1, wherein each said superconducting material includes at least one material selected from the group consisting of lead, niobium, niobium-nitride, indium and a lead-gold alloy.
Claim 6
Dependent Claim
27 words
The method of claim 1, 2 or 3, comprising forming said barrier oxide film to have said predetermined thickness in a range between 10 and 100 angstroms.
Claim 7
Dependent Claim
58 words
The process of claim 1, 2, 3 or 4, comprising depositing the second layer of superconducting material on said barrier oxide film having said predetermined thickness, after its formation by said controllable rf oxygen glow discharge process, prior to removing said substrate from the deposition apparatus thereby avoiding exposing said barrier oxide layer to undesired contamination and oxidation.
Claim 8
Dependent Claim
25 words
The process of claim 6, comprising controllably forming said barrier oxide film to have said predetermined thickness in a range between 10 and 100 angstroms.
Claim 9
Dependent Claim
31 words
The process of claim 6, comprising patterning the second photoresist film before said controllable forming of said barrier oxide film to a predetermined thickness by said rf oxygen glow discharge process.
Claim 10
Dependent Claim
33 words
The process of claim 6, comprising forming said first photoresist with a pattern corresponding to said first electrode, before the deposition of said first layer of the superconducting material of said first electrode.
Claim 11
Dependent Claim
35 words
The process of claim 1, 2, 3 or 4, comprising patterning the second photoresist film before said controllable forming of said barrier oxide film to a predetermined thickness by said rf oxygen glow discharge process.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-09 | 1985-05-11 | 1985-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-09 | 1989-05-11 | 1989-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-09 | 1993-05-11 | 1993-11-10 | $7700.00 | Window Closed / Lapsed |