Minimization of strain in single crystals
Assignee: AT&T Inc
•
Filing: 1979-10-12
•
Granted: 1981-11-10
•
Expires: 1999-10-12
Abstract
Abstract Single crystals are conveniently produced by directional solidification of a liquid body under a pressurized atmosphere and, preferably, under a liquid encapsulating layer to minimize loss due to volatilization. Such fabrication entails a concern with internal stress in a grown crystal in the interest, e.g., of minimization of breakage of wafers cut from a crystal. According to the invention, minimization of stress is accomplished by means of a post-growth annealing step during which pressure is reduced substantially and, in particular, preferably to a pressure which does not exceed 50 percent of a pressure at which a constituent of the liquid body volatilizes. The method may be applied for producing single crystals of semiconductor materials as may be used as device substrates. In particular, the method is beneficial, e.g., for producing high-quality doped or undoped InP, GaP, and GaAs single crystals.
Inventors
- 👤 William A. Bonner
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:24
CPC Classifications
C; C30; C30B; C30B27/00; C30B27/02; C30B33/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
163 words
Method for making a single crystal boule of a material which consists essentially of doped or undoped indium phosphide, said method comprising the steps of (1) heating to produce a liquid body of said material which is provided with an overlying liquid encapsulating layer, (2) providing over said liquid encapsulating layer an atmosphere, (3) pulling said boule from said liquid body through said liquid encapsulating layer while said atmosphere is at a first pressure which is greater than or equal to a critical pressure, said critical pressure being defined as the lowest pressure sufficient to essentially prevent dissociation of said constituents, (4) reducing pressure of said atmosphere from said first pressure to a second pressure which is less than or equal to 50 percent of said critical pressure while temperature of said boule is greater than or equal to 90 percent of the average temperature of said boule upon completion of growth of said boule, and (5) cooling said boule to ambient temperature.
Claim 2
Dependent Claim
163 words
Method for making a single crystal boule of a material which consists essentially of doped or undoped indium phosphide, said method comprising the steps of (1) heating to produce a liquid body of said material which is provided with an overlying liquid encapsulating layer, (2) providing over said liquid encapsulating layer an atmosphere, (3) pulling said boule from said liquid body through said liquid encapsulating layer while said atmosphere is at a first pressure which is greater than or equal to a critical pressure, said critical pressure being defined as the lowest pressure sufficient to essentially prevent dissociation of said constituents, (4) reducing pressure of said atmosphere from said first pressure to a second pressure which is less than or equal to 50 percent of said critical pressure while temperature of said boule is greater than or equal to 90 percent of the average temperature of said boule upon completion of growth of said boule, and (5) cooling said boule to ambient temperature.
Claim 3
Dependent Claim
21 words
Method of claim 1 in which pressure of said atmosphere is reduced further from said second pressure during cooling said boule.
Claim 4
Dependent Claim
15 words
Method of claim 1 in which said liquid body is a melt or a solution.
Claim 5
Dependent Claim
22 words
Method of claim 1 in which cooling said boule is at rates less than or equal to 20 degrees C. per minute.
Claim 6
Dependent Claim
36 words
Method of claim 1 in which said boule is at a temperature at which the material of said layer is soft while pressure of said atmosphere is reduced from said first pressure to said second pressure.
Claim 7
Dependent Claim
61 words
Method of claim 1 in which the material of said layer consists essentially of boron trioxide, in which said first pressure is greater than or equal to 28 atm, and in which said boule is heated at a temperature in a range of 550-650 degrees C. while pressure of said atmosphere is reduced from said first pressure to said second pressure.
References Cited (Backward Citations)
US3647389A
Cited
US4083748A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-09 | 1985-05-11 | 1985-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-09 | 1989-05-11 | 1989-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-09 | 1993-05-11 | 1993-11-10 | $7700.00 | Window Closed / Lapsed |