Method of manufacturing oxygen sensing element
Assignee: Toyota Motor Corp
•
Filing: 1979-09-06
•
Granted: 1981-11-10
•
Expires: 1999-09-06
Abstract
Abstract An oxygen sensing element capable of measuring partial pressures of oxygen in sample gases, which element has a solid electrolyte member having totally embedded therein a means for providing a reference partial pressure of oxygen composed of a sintered product of a finely divided metal or metal-metal oxide mixture and having a lead-out wire connected thereto is prepared by a method wherein: p1 (a) a part of the finely divided solid electrolyte material is compression-molded to form a provisional solid electrolyte member having a hole; (b) a provisional product of the reference oxygen partial pressure-providing means is formed in the hole of the provisional solid electrolyte member from the finely divided metal or metal-metal oxide mixture; (c) the remaining part of the finely divided solid electrolyte material is piled up on the provisional reference oxygen partial pressure-providing means product, followed by compression molding the piled up solid electrolyte material to form an integrated structure comprising the solid electrolyte member having totally embedded therein the provisional reference oxygen partial pressure-providing means; (d) the integrated structure is sintered in a non-oxidizing atmosphere at approximately 1,350 DEG to 1,500 DEG C.; and, (e) a layer or layers of an external conductive metal electrode or electrodes is formed on at least a part of the exterior surface of the sintered product.
Inventors
- 👤 Hiroshi Shinohara
- 👤 Yasuhiro Otsuka
- 👤 Shinichi Matsumoto
- 👤 Toshinobu Furutani
- 👤 Hiroshi Wakizaka
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 02:07
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4073; B; B22; B22F; B22F7/00; B22F7/06; G01N27/4075; G01N27/4076; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12014; Y10T428/12028; Y10T428/12063; Y10T428/1209
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
300 words
A method of manufacturing an oxygen sensing element having a structure such that an external conductive metal electrode or electrodes are mounted on the exterior surface of a solid electrolyte member having totally embedded therein a means for providing a reference partial pressure of oxygen, said reference oxygen partial pressure-providing means being composed of a sintered product of a finely divided metal or metal-metal oxide mixture and having a lead-out wire connected thereto; said method comprising the steps of: (a) compression molding a part of the finely divided solid electrolyte material to form a provisional solid electrolyte member having a hole in which the reference oxygen partial pressure-providing means is to be formed; (b) forming in said hole of the provisional solid electrolyte member a provisional product of the reference oxygen partial pressure-providing means from the finely divided metal or metal-metal oxide mixture, said finely divided metal or metal-metal oxide mixture having incorporated therein an anti-sintering material in an amount sufficient for making the thermal expansion or contraction of the reference oxygen partial pressure means substantially the same as that of the said electrolyte members; (c) piling up the remaining part of the finely divided solid electrolyte material on the upper surface of the provisional reference oxygen partial pressure-providing means product and on the upper surface of the provisional solid electrolyte member, followed by compression molding the piled up solid electrolyte material to form an integrated structure comprising the solid electrolyte member having totally embedded therein the provisional reference oxygen partial pressure-providing means; (d) sintering the integrated structure in non-oxidizing atmosphere at a temperature of from approximately 1,350° to 1,500° C., and; (e) forming a layer or layers of the external conductive metal electrode or electrodes on at least a part of the exterior surface of the sintered integrated structure.
Claim 2
Independent Claim
300 words
A method of manufacturing an oxygen sensing element having a structure such that an external conductive metal electrode or electrodes are mounted on the exterior surface of a solid electrolyte member having totally embedded therein a means for providing a reference partial pressure of oxygen, said reference oxygen partial pressure-providing means being composed of a sintered product of a finely divided metal or metal-metal oxide mixture and having a lead-out wire connected thereto; said method comprising the steps of: (a) compression molding a part of the finely divided solid electrolyte material to form a provisional solid electrolyte member having a hole in which the reference oxygen partial pressure-providing means is to be formed; (b) forming in said hole of the provisional solid electrolyte member a provisional product of the reference oxygen partial pressure-providing means from the finely divided metal or metal-metal oxide mixture, said finely divided metal or metal-metal oxide mixture having incorporated therein an anti-sintering material in an amount sufficient for making the thermal expansion or contraction of the reference oxygen partial pressure means substantially the same as that of the said electrolyte members; (c) piling up the remaining part of the finely divided solid electrolyte material on the upper surface of the provisional reference oxygen partial pressure-providing means product and on the upper surface of the provisional solid electrolyte member, followed by compression molding the piled up solid electrolyte material to form an integrated structure comprising the solid electrolyte member having totally embedded therein the provisional reference oxygen partial pressure-providing means; (d) sintering the integrated structure in non-oxidizing atmosphere at a temperature of from approximately 1,350° to 1,500° C., and; (e) forming a layer or layers of the external conductive metal electrode or electrodes on at least a part of the exterior surface of the sintered integrated structure.
Claim 3
Dependent Claim
64 words
A method according to claim 1 wherein said formation of the provisional product of the reference oxygen partial pressure-providing means is carried out by a process in which the finely divided metal or metal-metal oxide mixture is filled in the hole of the provisional solid electrolyte member in the mold, and then, consolidated; and thereafter, the lead-out wire is fixed in the consolidated material.
Claim 4
Dependent Claim
68 words
A method according to claim 1 wherein said formation of the provisional product of the reference oxygen partial pressure-providing means is carried out by a process in which the finely divided metal or metal-metal oxide mixture is compression molded; the so molded product is inserted into the hole of the provisional solid electrolyte member in the mold; and then, the lead-out wire is fixed in the molded product.
Claim 5
Dependent Claim
61 words
A method according to claim 2 or 3 wherein, the remaining part of the finely divided solid electrolyte mateiral is piled up on the lead-out wire-fixed consolidated or molded product; and then, the piled up solid electrolyte material is compression-molded by thrusting into the mold split plunging rods having a narrow space formed therebetween in which the lead-out wire is fitted.
Claim 6
Dependent Claim
86 words
A method according to claim 1 wherein said steps of (b) and (c) are carried out by a process in which the finely divided metal or metal-metal oxide mixture is filled in the hole of the provisional solid electrolyte member in the mold; the remaining part of the finely divided solid electrolyte mateiral is piled up on the filled finely divided metal or metal-metal oxide mixture; a lead-out wire is inserted in the piled solid electrolyte mateiral; and then, the piled solid electrolyte material is compression-molded.
Claim 7
Dependent Claim
87 words
A method according to claim 1 wherein said steps of (b) and (c) are carried out by a process in which the finely divided metal or metal-metal oxide mixture is compression-molded; the so molded product is inserted in the hole of the provisional solid electrolyte member in the mold; the remianing part of the finely divided solid electrolyte material is piled up on the inserted product; a lead-out wire is inserted in the piled solid electrolyte mateiral; and then, the piled solid electrolyte mateiral is compression molded.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-09 | 1985-05-11 | 1985-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-09 | 1989-05-11 | 1989-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-09 | 1993-05-11 | 1993-11-10 | $7700.00 | Window Closed / Lapsed |