Molybdenum substrate for high power density tungsten focal track X-ray targets
Assignee: General Electric Co
•
Filing: 1980-01-02
•
Granted: 1981-11-03
•
Expires: 2000-01-02
Abstract
Abstract Improved rotary targets for X-ray tubes are provided which include a substrate body of a high strength molybdenum alloy, an intermediate ductile layer of pure molybdenum or a ductile molybdenum alloy affixed to the top surface thereof and an electron receiving layer made of a tungsten-based alloy affixed to at least a portion of the intermediate layer.
Inventors
- 👤 Harold H. Hirsch
- 👤 Melvin R. Jackson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 06:21
CPC Classifications
H; H01; H01J; H01J35/00; H01J35/02; H01J35/04; H01J35/08; H01J35/10; H01J35/108; H01J2235/00; H01J2235/08; H01J2235/083; H01J2235/084
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
162 words
An improved three-layer rotary X-ray target consisting of a substrate body of a molybdenum alloy having a high strength at the elevated operating temperature of the target, an intermediate ductile layer of molybdenum or a ductile molybdenum alloy, and a focal track target layer of a tungsten based alloy, said intermediate layer being contiguous with said substrate body and being situate at least in part between said substrate and said target layer, said molybdenum alloy of said substrate being characterized by a 0.2% yield strength at 1100° C. of at least 9000 psi and said molybdenum or ductile molybdenum alloy of said intermediate layer being characterized by a total elongation or reduction in area over the range of 25°-1100° C. of at least 1.3%, whereby the growth of cracks which originate in said focal track layer upon extended exposure to high energy electrons are terminated in said ductile intermediate layer and are prevented thereby from entering and propagating through said substrate body.
Claim 2
Dependent Claim
162 words
An improved three-layer rotary X-ray target consisting of a substrate body of a molybdenum alloy having a high strength at the elevated operating temperature of the target, an intermediate ductile layer of molybdenum or a ductile molybdenum alloy, and a focal track target layer of a tungsten based alloy, said intermediate layer being contiguous with said substrate body and being situate at least in part between said substrate and said target layer, said molybdenum alloy of said substrate being characterized by a 0.2% yield strength at 1100° C. of at least 9000 psi and said molybdenum or ductile molybdenum alloy of said intermediate layer being characterized by a total elongation or reduction in area over the range of 25°-1100° C. of at least 1.3%, whereby the growth of cracks which originate in said focal track layer upon extended exposure to high energy electrons are terminated in said ductile intermediate layer and are prevented thereby from entering and propagating through said substrate body.
Claim 3
Dependent Claim
21 words
The device of claim 1, wherein said tungsten based alloy consists essentially of tungsten and 3-10 percent by weight of rhenium.
Claim 4
Dependent Claim
90 words
The device of claim 2, wherein said substrate body consists essentially of a high strength alloy of molybdenum and about 0.05-10 percent by weight of a member selected from the group consisting of (a) a metal selected from the group consisting of iron, cobalt, tantalum, niobium, silicon, carbon and hafnium, and (b) an oxide of a metal selected from the group consisting of thorium, zirconium, titanium, aluminum, magnesium, silicon, yttrium, cerium, and the rare earth metals, and (c) mixtures of said metal, said oxide of a metal, and combinations thereof.
Claim 5
Dependent Claim
12 words
The device of claim 3, wherein said intermediate ductile layer is molybdenum.
Claim 6
Dependent Claim
38 words
The device of claim 1, wherein said substrate body has a thickness of about 4-25 mm, said intermediate ductile layer has a thickness of about 1-5 mm, and said focal track has a thickness of about 0.5-3 mm.
Claim 7
Dependent Claim
64 words
The device of claim 5, wherein said substrate body consists essentially of molybdenum plus 0.125 weight percent iron and has a thickness of about 8-15 mm, said intermediate ductile layer consists of molybdenum and has a thickness of about 2-3 mm, and said focal track consists essentially of tungsten and 5 percent by weight of rhenium and has a thickness of about 0.50-1.5 mm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-02 | 1985-05-04 | 1985-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-02 | 1989-05-04 | 1989-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-02 | 1993-05-04 | 1993-11-03 | $7700.00 | Window Closed / Lapsed |