US4298668A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Alkaline battery, electrolyte absorber therefor
Assignee: Kimberly Clark Worldwide Inc
•
Filing: 1980-07-03
•
Granted: 1981-11-03
•
Expires: 2000-07-03
Abstract
Abstract An improved electrolyte absorber for alkaline battery cells has low resistance to electrolyte ion transfer and can hold alkaline electrolyte in contact with an electrode during chemical reactions of the cell. The absorber is formed by depositing an improved wetting compositions to a polyolefin substrate. The substrate, preferably, is a fibrous and porous melt blown thermoplastic web made up of a plurality of physically entangled microfibers, resistant to strong alkali and oxidation. The wetting composition which is deposited over and adhered to external surfaces of said microfibers is comprised of a substantially homogeneous admixture of a polymeric binder, inert hydrophilic filler particles and a phosphate ester wetting agent. Portions of the filler particles in the composition protrude through the binder and are exposed in random distribution. When the absorber is immersed in electrolyte, the phosphate ester wetting agent reacts with the electrolyte to lower the surface tension thereof. The lowered surface tension permits the reacted electrolyte to rapidly wet the exposed filler particles.
Inventors
- 👤 George F. Schmidt
- 👤 Robert E. Weber
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 06:46
CPC Classifications
H; H01; H01M; H01M50/00; H01M50/40; H01M50/489; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
196 words
An improved electrolyte absorber for use in an alkaline battery cell for physically separating electrodes of said cell and for holding alkaline electrolyte in contact with an electrode during chemical reactions of said cell, in which said absorber comprises a flexible and fibrous polyolefin substrate made up of a plurality of physically entangled microfibers, resistant to strong alkali and oxidation with said substrate being permeable to electrolyte ion transfer, said improvement comprising: a wetting composition deposited over and adhered to external surfaces of said microfibers, said composition comprising a substantially homogeneous admixture of: 1. a polymeric binder; 2. inert hydrophilic filler particles; and 3. a phosphate ester wetting agent; the polymeric binder in said composition substantially covering the external surfaces of said microfibers with portions of said filler particles being exposed and protruding through said binder in random distribution, said wetting agent being of the type which when immersed in and in contact with said alkaline electrolyte reacts with said electrolyte to lower the surface tension thereof, said lowered surface tension permitting said reacted electrolyte to rapidly wet said exposed filler particles, the wetting of said filler particles being substantially permanent while immersed in said electrolyte.
Claim 2
Dependent Claim
196 words
An improved electrolyte absorber for use in an alkaline battery cell for physically separating electrodes of said cell and for holding alkaline electrolyte in contact with an electrode during chemical reactions of said cell, in which said absorber comprises a flexible and fibrous polyolefin substrate made up of a plurality of physically entangled microfibers, resistant to strong alkali and oxidation with said substrate being permeable to electrolyte ion transfer, said improvement comprising: a wetting composition deposited over and adhered to external surfaces of said microfibers, said composition comprising a substantially homogeneous admixture of: 1. a polymeric binder; 2. inert hydrophilic filler particles; and 3. a phosphate ester wetting agent; the polymeric binder in said composition substantially covering the external surfaces of said microfibers with portions of said filler particles being exposed and protruding through said binder in random distribution, said wetting agent being of the type which when immersed in and in contact with said alkaline electrolyte reacts with said electrolyte to lower the surface tension thereof, said lowered surface tension permitting said reacted electrolyte to rapidly wet said exposed filler particles, the wetting of said filler particles being substantially permanent while immersed in said electrolyte.
Claim 3
Dependent Claim
24 words
An absorber in accordance with claim 1, wherein said binder is selected from the group consisting of butyl latex rubber and ethylene propylene terpolymer.
Claim 4
Dependent Claim
23 words
An absorber in accordance with claim 1, wherein said phosphate ester wetting agent is a potassium salt of a complex organic polyphosphoric ester.
Claim 5
Dependent Claim
44 words
An absorber in accordance with claim 1, wherein said inert filler particles are powdered or fibrous and are selected from the group consisting of kaolin clays, metallic oxides, titanates and silicates of a suitable size wherein said fillers are substantially insoluble in alkaline electrolyte.
Claim 6
Dependent Claim
49 words
An absorber in accordance with claim 4, wherein said composition is comprised of from about 15 to 18 percent by weight of said binder, from about 61 to 74 percent by weight of said inert filler, and from about 8 to 17 percent by weight of said wetting agent.
Claim 7
Dependent Claim
173 words
An electrolyte absorber for physically separating electrodes immersed in a solution of alkaline electrolyte in a battery cell, and for holding the electrolyte in contact with an electrode during chemical reactions within said cell, comprising: a. a flexible and fibrous polyolefin substrate comprised of a plurality of physically entangled microfibers; b. a wetting composition deposited upon and adhered to external surfaces of said microfibers, said composition comprising of an admixture of: 1. a polymeric binder; 2. inert hydrophilic fillers; and 3. a phosphate ester wetting agent, the polymeric binder in said composition substantially covering the external surfaces of said microfibers with portions of said filler particles being exposed and protruding through said binder in random distribution, said wetting agent being of the type which when immersed in and in contact with said alkaline electrolyte reacts with said electrolyte to lower the surface tension thereof, said lowered surface tension permitting said reacted electrolyte to rapidly wet said exposed filler particles, the wetting of said filler particles being substantially permanent while immersed in said electrolyte.
Claim 8
Dependent Claim
173 words
An electrolyte absorber for physically separating electrodes immersed in a solution of alkaline electrolyte in a battery cell, and for holding the electrolyte in contact with an electrode during chemical reactions within said cell, comprising: a. a flexible and fibrous polyolefin substrate comprised of a plurality of physically entangled microfibers; b. a wetting composition deposited upon and adhered to external surfaces of said microfibers, said composition comprising of an admixture of: 1. a polymeric binder; 2. inert hydrophilic fillers; and 3. a phosphate ester wetting agent, the polymeric binder in said composition substantially covering the external surfaces of said microfibers with portions of said filler particles being exposed and protruding through said binder in random distribution, said wetting agent being of the type which when immersed in and in contact with said alkaline electrolyte reacts with said electrolyte to lower the surface tension thereof, said lowered surface tension permitting said reacted electrolyte to rapidly wet said exposed filler particles, the wetting of said filler particles being substantially permanent while immersed in said electrolyte.
Claim 9
Dependent Claim
60 words
The electrolyte absorber of claim 6, wherein said substrate is a web of entangled microfibers, wherein said wetting composition is adhered to external surfaces of said microfibers, wherein said substrate with said composition adhered thereon is sealed along cut edges with an alkali resistant adhesive, and wherein microscopic interstices between fibers are sufficiently large to be permeable to said electrolyte.
Claim 10
Dependent Claim
46 words
The electrolyte absorber of claim 6, wherein said wetting composition is comprised of from about 15 to 18% by weight of said binder, from about 61 to 74% by weight of said inert filler and from about 8 to 17% by weight of said wetting agent.
Claim 11
Dependent Claim
57 words
The electrolyte absorber of claim 8, wherein said binder is a butyl latex rubber, said phosphate ester wetting agent is a potassium salt of a complex organic polyphosphoric ester while said inert fillers are selected from the group consisting of titanates, silicates and metallic oxides, of a suitable size, said fillers being substantially insoluble in alkaline electrolyte.
Claim 12
Dependent Claim
16 words
An electrolyte absorber in accordance with claim 9, wherein said rubber binder is ethylene propylene terpolymer.
Claim 13
Dependent Claim
57 words
An electrolyte absorber in accordance with claim 7 wherein said substrate is a melt blown polypropylene web having a basis weight of from about 15 grams/m 2 to about 100 grams/m 2 and bonded primarily by physical entanglement to provide a strength of about 1.5 lbs. per inch width in the machine direction while maintaining good flexibility.
References Cited (Backward Citations)
US3849241A
Cited
US3765948A
Cited
US3985580A
Cited
US4085241A
Cited
US4224393A
Cited
US4224394A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-02 | 1985-05-04 | 1985-11-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-02 | 1989-05-04 | 1989-11-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-02 | 1993-05-04 | 1993-11-03 | $7700.00 | Window Closed / Lapsed |