Process for rim elastomers with superior high temperature dimensional stability
Assignee: Huntsman Corp
•
Filing: 1980-02-11
•
Granted: 1981-10-27
•
Expires: 2000-02-11
Abstract
Abstract The invention is a method for making reaction injection molded polyurethane of improved properties. The product ccomprises the reaction product of a high molecular weight polyhydric polyether, a low molecular weight active hydrogen containing compound of at least two functionality and a polyisocyanate wherein at least about 30% of the high molecular weight polyether is first mixed and allowed to react with the polyisocyanate and then the remaining polyhydric polyether and low molecular weight active hydrogen containing compound are added to the polyether and polyisocyanate mixture and allowed to react. Reaction injection molded elastomers are useful as molded articles of commerce including, but not limited to, vehicle body parts.
Inventors
- 👤 Richard J. Gilbert
- 👤 Doris M. Rice
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-29 09:30
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/10; C08G2120/00
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
117 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises mixing at least 30% of said polyether polyol with the entire amount of polyisocyanate and allowing them to react, adding the remaining polyether polyol and low molecular weight active hydrogen containing compound to the polyol and polyisocyanate reacted mixture and injecting this entire mixture into the mold cavity where it is allowed to react.
Claim 2
Dependent Claim
117 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises mixing at least 30% of said polyether polyol with the entire amount of polyisocyanate and allowing them to react, adding the remaining polyether polyol and low molecular weight active hydrogen containing compound to the polyol and polyisocyanate reacted mixture and injecting this entire mixture into the mold cavity where it is allowed to react.
Claim 3
Dependent Claim
22 words
A method as in claim 1 wherein the polyol comprises a polyether of about 5000 molecular weight based on a trihydric initiator.
Claim 4
Dependent Claim
12 words
A method as in claim 1 wherein the polyisocyanate comprises 4,4'diphenylmethane diisocyanate.
Claim 5
Dependent Claim
15 words
A method as in claim 1 wherein the elastomer is postcured at about 325° F.
Claim 6
Dependent Claim
24 words
A method as in claim 1 wherein all of the polyol is prereacted with polyisocyanate prior to injecting the entire mixture into the mold.
Claim 7
Dependent Claim
109 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises mixing all of said polyether polyol with the entire amount of polyisocyanate and allowing them to react then adding the low molecular weight active hydrogen containing compound to the polyol-polyisocyanate reaction product and injecting this mixture into the mold cavity where it is allowed to react.
Claim 8
Dependent Claim
109 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises mixing all of said polyether polyol with the entire amount of polyisocyanate and allowing them to react then adding the low molecular weight active hydrogen containing compound to the polyol-polyisocyanate reaction product and injecting this mixture into the mold cavity where it is allowed to react.
Claim 9
Dependent Claim
120 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing a compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises prereacting at least about 30% of said polyether polyol with a portion of the polyisocyanate and allowing them to react and mixing with this reaction product the remaining polyisocyanate, the remaining polyether polyol and the low molecular weight active hydrogen containing compound and injecting this mixture into the mold cavity where it is allowed to react.
Claim 10
Dependent Claim
120 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing a compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises prereacting at least about 30% of said polyether polyol with a portion of the polyisocyanate and allowing them to react and mixing with this reaction product the remaining polyisocyanate, the remaining polyether polyol and the low molecular weight active hydrogen containing compound and injecting this mixture into the mold cavity where it is allowed to react.
Claim 11
Dependent Claim
22 words
A method as in claim 7 wherein the polyol comprises a polyether of about 5000 molecular weight based on a trihydric initiator.
Claim 12
Dependent Claim
12 words
A method as in claim 7 wherein the polyisocyanate comprises 4,4'diphenylmethane diisocyanate.
Claim 13
Dependent Claim
15 words
A method as in claim 7 wherein the elastomer is postcured at about 325° F.
Claim 14
Dependent Claim
24 words
A method as in claim 7 wherein all of the polyol is prereacted with polyisocyanate prior to injecting the entire mixture into the mold.
Claim 15
Dependent Claim
113 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing a compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises prereacting all of said polyether polyol with a portion of the polyisocyanate and allowing them to react and mixing with this reaction product the remaining polyisocyanate and the low molecular weight active hydrogen containing compound and injecting this mixture into the mold cavity where it is allowed to react.
Claim 16
Dependent Claim
113 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing a compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises prereacting all of said polyether polyol with a portion of the polyisocyanate and allowing them to react and mixing with this reaction product the remaining polyisocyanate and the low molecular weight active hydrogen containing compound and injecting this mixture into the mold cavity where it is allowed to react.
Claim 17
Dependent Claim
134 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing a compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises prereacting at least about 30% of said polyether polyol with a portion of the polyisocyanate and allowing them to react, adding this reaction product to the remaining polyisocyanate to form an A component, mixing the remaining polyol and low molecular weight active hydrogen containing compound to form a B component, mixing the A and B components and injecting the mixture into the mold cavity where it is allowed to react.
Claim 18
Dependent Claim
134 words
In a method for making a polyurethane elastomer wherein an aromatic polyisocyanate, a polyether polyol based on trihydric initiators of about 4000 molecular weight and above and a chain extending agent comprising a low molecular weight active hydrogen containing a compound of at least 2 functionality is injected via a RIM machine into a mold cavity of the desired configuration the improvement which comprises prereacting at least about 30% of said polyether polyol with a portion of the polyisocyanate and allowing them to react, adding this reaction product to the remaining polyisocyanate to form an A component, mixing the remaining polyol and low molecular weight active hydrogen containing compound to form a B component, mixing the A and B components and injecting the mixture into the mold cavity where it is allowed to react.
Claim 19
Dependent Claim
22 words
A method as in claim 13 wherein the polyol comprises a polyether of about 5000 molecular weight based on a trihydric initiator.
Claim 20
Dependent Claim
12 words
A method as in claim 13 wherein the polyisocyanate comprises 4,4'diphenylmethane diisocyanate.
Claim 21
Dependent Claim
15 words
A method as in claim 13 wherein the elastomer is postcured at about 325° F.
Claim 22
Dependent Claim
24 words
A method as in claim 13 wherein all of the polyol is prereacted with polyisocyanate prior to injecting the entire mixture into the mold.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-26 | 1985-04-27 | 1985-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-26 | 1989-04-27 | 1989-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-26 | 1993-04-27 | 1993-10-27 | $7700.00 | Window Closed / Lapsed |