Process for producing carbon-carbon fiber composites suitable for use as aircraft brake discs

Claim 2

A process for producing carbon-carbon fiber composites of high strength which comprises forming an aqueous gelled mixture containing between about 5 and 15% by weight chopped carbonaceous fibers and a water-soluble binder-thickening agent selected from the group consisting of polyethylene oxide, ethyl methyl cellulose, hydroxyethyl cellulose, hydroxyethyl methyl cellulose, hydroxyproply methyl cellulose, methyl cellulose, polyacrylamid, polyvinyl alcohol, polyvinyl methyl ether, starch and gelatin, said binder-thickening agent having a viscosity of at least about 10,000 centipoises at 25° C., extruding the gelled mixture into the form of a continuous elongated ribbon wherein the individual carbon fibers are aligned substantially in the direction of fluid flow, arranging said elongated ribbon in a spiral pattern to form a flat disc shaped article, drying said article to remove water, heating the dried article to a temperature of at least about 300° C. and then impregnating said article with a liquid thermosetting resin binder followed by heating said article under pressure in a mold to a temperature of at least about 1200° C.

Claim 3

A process for producing carbon-carbon fiber composites of high strength which comprises forming an aqueous gelled mixture containing between about 5 and 15% by weight chopped carbonaceous fibers and a water-soluble binder-thickening agent selected from the group consisting of polyethylene oxide, ethyl methyl cellulose, hydroxyethyl cellulose, hydroxyethyl methyl cellulose, hydroxypropyl methyl cellulose, methyl cellulose, polyacrylamid, polyvinyl alcohol, polyvinyl methyl ether, starch and gelatin, said binder-thickening agent having a viscosity of at least about 10,000 centipoises at 25° C., extruding the gelled mixture into the form of a continuous elongated ribbon wherein the individual carbon fibers are aligned substantially in the direction of fluid flow, arranging said elongated ribbon in a circular pattern to form a flat disc shaped article, drying said article to remove water, heating the dried article to a sufficiently high temperature to at least carbonize the binder in said mixture and then impregnating said article with a liquid carbonaceous binder material followed by heating said article under pressure in a mold to at least carbonizing temperatures in order to densify the article.

Claim 4

A process for producing carbon-carbon fiber composites of high strength which comprises forming an aqueous gelled mixture containing between about 5 and 15% by weight chopped carbonaceous fibers and a water-soluble binder-thickening agent selected from the group consisting of polyethylene oxide, ethyl methyl cellulose, hydroxyethyl cellulose, hydroxyethyl methyl cellulose, hydroxypropyl methyl cellulose, methyl cellulose, polyacrylamid, polyvinyl alcohol, polyvinyl methyl ether, starch and gelatin, said binder-thickening agent having a viscosity of at least about 10,000 centipoises at 25° C., extruding the gelled mixture into the form of a continuous elongated ribbon wherein the individual carbon fibers are aligned substantially in the direction of fluid flow, arranging said elongated ribbon in a circular pattern to form a flat disc shaped article, drying said article to remove water, heating the dried article to a sufficiently high temperature to at least carbonize the binder in said mixture and then impregnating said article with a liquid carbonaceous binder material followed by heating said article under pressure in a mold to at least carbonizing temperatures in order to densify the article.

Claim 5

A process as defined by claim 2 wherein said chopped carbonaceous fibers have a length within the range of from about 12 mils to about 3 inches.

Claim 6

A process as defined by claim 3 wherein said chopped carbonaceous fibers have a length within the range of from about 1/4 to about 2 inches.

Claim 7

A process as defined by claim 4 wherein said chopped carbonaceous fibers have a length of about 1 inch and a diameter of 10 microns.

Claim 8

A process as defined by claim 3 wherein said chopped carbonaceous fibers are selected from the group consisting of carbonized carbon fibers, uncarbonized thermoset pitch fibers and graphite fibers.

Claim 9

A process as defined by claim 6 wherein said chopped carbonaceous fibers are uncarbonized thermoset mesophase pitch fibers.

Claim 10

A process as defined by claim 6 wherein said dried article is heated to temperatures of at least about 300° C. when said mixture contains carbonized fibers.

Claim 11

A process as defined by claim 6 wherein said dried article is heated to temperatures of at least about 800° C. when said mixture contains uncarbonized, thermoset pitch fibers.

Claim 12

A processs as defined by claim 2 wherein said elongated ribbon is guided onto a rotating disc platform in a spiral pattern to form said flat disc shaped article.

Claim 13

A process as defined by claim 2 wherein said carbonaceous binder material is a liquid thermosetting resin.

Claim 14

A process as defined by claim 11 wherein said liquid thermosetting resin is a 50% solution of phenolic resin in acetone.

Claim 15

A process as defined by claim 2 wherein said article after impregnation is heated to temperatures of at least about 1200° C.

Claim 16

A process as defined by claim 2 wherein said article after heating to carbonizing temperatures is impregnated using a high coking value liquid impregnant followed by heating in an inert atmosphere to temperatures within the range of from about 2200° C. to about 3000° C.

Claim 17

A process for producing carbon-carbon fiber composites of high strength which comprises forming an aqueous gelled mixture containing between about 5 and 15% by weight chopped, uncarbonized, thermoset pitch fibers and a water-soluble binder-thickening agent selected from the group consisting of polyethylene oxide, ethyl methyl cellulose, hydroxyethyl celluolose, hydroxyethy methyl cellulose, hydroxypropyl methyl cellulose, methyl cellulose, polyacrylamid, polyvinyl alcohol, polyvinyl methyl ether, starch, and gelatin, said binder-thickening agent having a viscosity of at least about 10,000 centipoises at 25° C., extruding the gelled mixture into the form of a continuous elongated ribbon wherein the individual carbon fibers are aligned substantially in the direction of fluid flow, arranging said elongated ribbon in a circular pattern to from a flat disc shaped article, drying said article to remove water, heating the dried article to a temperature of at least about 800° C. and then impregnating said article with a liquid thermosetting resin binder followed by heating said article under pressure in a mold to a temperature of at least about 1200° C.

Claim 18

A process for producing carbon-carbon fiber composites of high strength which comprises forming an aqueous gelled mixture containing between about 5 and 15% by weight chopped, uncarbonized, thermoset pitch fibers and a water-soluble binder-thickening agent selected from the group consisting of polyethylene oxide, ethyl methyl cellulose, hydroxyethyl celluolose, hydroxyethy methyl cellulose, hydroxypropyl methyl cellulose, methyl cellulose, polyacrylamid, polyvinyl alcohol, polyvinyl methyl ether, starch, and gelatin, said binder-thickening agent having a viscosity of at least about 10,000 centipoises at 25° C., extruding the gelled mixture into the form of a continuous elongated ribbon wherein the individual carbon fibers are aligned substantially in the direction of fluid flow, arranging said elongated ribbon in a circular pattern to from a flat disc shaped article, drying said article to remove water, heating the dried article to a temperature of at least about 800° C. and then impregnating said article with a liquid thermosetting resin binder followed by heating said article under pressure in a mold to a temperature of at least about 1200° C.

Claim 19

A process for producing carbon-carbon fiber composites of high strength which comprises forming an aqueous gelled mixture containing between about 5 and 15% by weight chopped carbonaceous fibers, between about 0 and 5% by weight thermal black, and between about 3 and 10% by weight of a water-soluble binder-thickening agent composed of a mixture of polyethylene oxide and hydroxyethyl cellulose, said binder-thickening agent having a viscosity of at least about 10,000 centipoises at 25° C., extruding the gelled mixture into the form of a continuous elongated ribbon wherein the individual carbon fibers are aligned substantially in the direction of fluid flow, arranging said elongated ribbon in a circular pattern to form a flat disc shaped article, drying said article to remove water, heating the dried article to a sufficiently high temperature to at least carbonize the binder in said mixture and then impregnating said article with a liquid carbonaceous binder material followed by heating said article under pressure in a mold to at least carbonizing temperatures in order to densify the article.

Claim 20

A process for producing carbon-carbon fiber composites of high strength which comprises forming an aqueous gelled mixture containing between about 5 and 15% by weight chopped carbonaceous fibers, between about 0 and 5% by weight thermal black, and between about 3 and 10% by weight of a water-soluble binder-thickening agent composed of a mixture of polyethylene oxide and hydroxyethyl cellulose, said binder-thickening agent having a viscosity of at least about 10,000 centipoises at 25° C., extruding the gelled mixture into the form of a continuous elongated ribbon wherein the individual carbon fibers are aligned substantially in the direction of fluid flow, arranging said elongated ribbon in a circular pattern to form a flat disc shaped article, drying said article to remove water, heating the dried article to a sufficiently high temperature to at least carbonize the binder in said mixture and then impregnating said article with a liquid carbonaceous binder material followed by heating said article under pressure in a mold to at least carbonizing temperatures in order to densify the article.