US4296177A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Flexible graphite sheet, material or layer containing metal molybdate
Assignee: SIGRI ELEKTROGRAPHIT GmbH
•
Filing: 1979-12-21
•
Granted: 1981-10-20
•
Expires: 1999-12-21
Abstract
Abstract Flexible graphite layer material containing at least one metal moylbdate with a solubility in water of 10-2 to 10-4 g/100 ml to inhibit corrosion. The corrosion inhibitor may be incorporated by first immersing the graphite layer material in a solution of an alkali metal molybdate, drying, and then immersing in a solution of very soluble metal salt in which the metal when combined with molybdate to form metal molybdate has the defined solubility. The graphite layer material is then dried and contains the desired molybdate corrosion inhibitor.
Inventors
- 👤 Ernst Freundlinger
- 👤 Alfred Hirschvogel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 08:55
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/10; C09K3/1003; C04; C04B; C04B35/00; C04B35/515; C04B35/52; C04B35/536; F; F16; F16J; F16J15/00; F16J15/02; F16J15/06; F16J15/10; F16J15/102; C09K2200/00; C09K2200/02; C09K2200/0204; C09K2200/0208; C09K2200/0239; Y; Y10; Y10T; Y10T428/00; Y10T428/30
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
24 words
Flexible graphite layer material containing a metal molybdate with a solubility in water of 10 -2 to 10 -4 g/100 ml to inhibit corrosion.
Claim 2
Dependent Claim
24 words
Flexible graphite layer material containing a metal molybdate with a solubility in water of 10 -2 to 10 -4 g/100 ml to inhibit corrosion.
Claim 3
Dependent Claim
21 words
Flexible graphite layer material according to claim 1, wherein said material contains a plurality of said metal molybdates having said solubility.
Claim 4
Dependent Claim
22 words
Flexible graphite layer material containing a metal molybdate selected from the group consisting of silver-, calcium- and barium molybdate and mixtures thereof.
Claim 5
Dependent Claim
22 words
Flexible graphite layer material containing a metal molybdate selected from the group consisting of silver-, calcium- and barium molybdate and mixtures thereof.
Claim 6
Dependent Claim
24 words
Flexible graphite layer material according to claim 1 or claim 2 or claim 3, wherein the molybdate content is 0.5 to 1.0% by weight.
Claim 7
Dependent Claim
103 words
Method for the manufacture of a graphite layer material to incorporate a corrosion inhibitor which comprises immersing the graphite layer material in a first solution containing an alkali metal molybdate, subsequently drying the immersed layer material, immersing the dried material in a second solution containing at least one highly soluble metal salt selected from the group of silver-, calcium- and barium soluble salts to produce a molybdate of said metal from said soluble salt, and subsequently drying the graphite layer material leaving incorporated therein a molybdate of a metal selected from the group consisting of silver, calcium and barium as a corrosion inhibitor.
Claim 8
Dependent Claim
103 words
Method for the manufacture of a graphite layer material to incorporate a corrosion inhibitor which comprises immersing the graphite layer material in a first solution containing an alkali metal molybdate, subsequently drying the immersed layer material, immersing the dried material in a second solution containing at least one highly soluble metal salt selected from the group of silver-, calcium- and barium soluble salts to produce a molybdate of said metal from said soluble salt, and subsequently drying the graphite layer material leaving incorporated therein a molybdate of a metal selected from the group consisting of silver, calcium and barium as a corrosion inhibitor.
Claim 9
Dependent Claim
105 words
Method for the manufacture of a graphite layer material to incorporate a corrosion inhibitor which comprises immersing the graphite layer material in a first solution containing an alkali metal molybdate, subsequently drying the immersed layer material, immersing the dried material in a second solution containing a highly soluble salt of a metal to produce a molybdate of said metal from said soluble salt, said metal being selected that the metal molybdate has a solubility in water of 10 -2 to 10 -4 g/100 ml, and subsequently drying the graphite layer material leaving incorporated therein a metal molybdate of said defined solubility as a corrosion inhibitor.
Claim 10
Dependent Claim
105 words
Method for the manufacture of a graphite layer material to incorporate a corrosion inhibitor which comprises immersing the graphite layer material in a first solution containing an alkali metal molybdate, subsequently drying the immersed layer material, immersing the dried material in a second solution containing a highly soluble salt of a metal to produce a molybdate of said metal from said soluble salt, said metal being selected that the metal molybdate has a solubility in water of 10 -2 to 10 -4 g/100 ml, and subsequently drying the graphite layer material leaving incorporated therein a metal molybdate of said defined solubility as a corrosion inhibitor.
Claim 11
Dependent Claim
27 words
Method according to claim 5 or claim 6, wherein the molybdate content remaining in the graphite layer material as corrosion inhibitor is 0.5 to 1.0% by weight.
References Cited (Backward Citations)
DE2748135A1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-19 | 1985-04-20 | 1985-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-19 | 1989-04-20 | 1989-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-19 | 1993-04-20 | 1993-10-20 | $7700.00 | Window Closed / Lapsed |