Sizing composition and glass fibers treated with the aid of such composition
Assignee: Saint Gobain Industries SA
•
Filing: 1979-04-02
•
Granted: 1981-10-20
•
Expires: 1999-04-02
Abstract
Abstract Sizing compositions comprising a combination of several adhesive agents capable of being cross-linked, an acrylic polymer and a coupling agent, are used to treat glass fibers in order to provide improved plastic reinforcing fibers especially suited to use in sheet molding compounds whereby molded articles, particularly large pieces formed therefrom, will have improved reinforcement and surface characteristics.
Inventors
- 👤 Michel Droux
- 👤 Gilbert Bocquet
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 14:26
CPC Classifications
C; C03; C03C; C03C25/00; C03C25/10; C03C25/24; C03C25/26; C08; C08J; C08J5/00; C08J5/24; C08J5/248; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2938
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
137 words
In a method of manufacturing coated glass fiber comprising the following operations in sequence: (a) mechanically drawing filaments of molten glass at high speed (b) coating said filaments with an aqueous sizing composition (c) collecting said coated glass filaments during the drawing operation in the form of strands which are wound into cakes, dried and then collected into roving slivers in the shape of a ball, or directly collected into ball-shaped rovings and dried; the improvement which comprises coating the filaments with an aqueous sizing composition comprising a system of cross-linking adhesive agents consisting essentially of at least one compound having a number of functional groups which are N-methylol functions or N-CH 2 OR functions or both, with R being an alkyl radical, at least one acrylic polymer which may be modified or unmodified, and an amino-alkoxy-silane.
Claim 2
Dependent Claim
137 words
In a method of manufacturing coated glass fiber comprising the following operations in sequence: (a) mechanically drawing filaments of molten glass at high speed (b) coating said filaments with an aqueous sizing composition (c) collecting said coated glass filaments during the drawing operation in the form of strands which are wound into cakes, dried and then collected into roving slivers in the shape of a ball, or directly collected into ball-shaped rovings and dried; the improvement which comprises coating the filaments with an aqueous sizing composition comprising a system of cross-linking adhesive agents consisting essentially of at least one compound having a number of functional groups which are N-methylol functions or N-CH 2 OR functions or both, with R being an alkyl radical, at least one acrylic polymer which may be modified or unmodified, and an amino-alkoxy-silane.
Claim 3
Dependent Claim
98 words
The method of claim 1 wherein the ingredients in said aqueous sizing composition consist essentially of: polyacrylamide in an amount equivalent to 4 to 15% by weight of a 30% polyacrylamide solution, melamine-formaldehyde in an amount equivalent to 1.5 to 6% by weight of a 70% melamine-formaldehyde solution, a copolymer of vinyl acetate and N-methylolacrylamide in an amount equivalent to 4 to 15% by weight of an emulsion of 50% of said copolymer, 0.01 to 1% by weight of Gamma aminopropyltriethoxysilane, 0 to 1% by weight of N-methylolacrylamide, monomer, and 0 to 1% by weight of lithium chloride.
Claim 4
Dependent Claim
83 words
The method of claim 1 wherein the ingredients in said aqueous sizing composition consist essentially of: 4% by weight of an aqueous solution of melamine formaldehyde (70% solids), 10% by weight of an emulsion (50% solids) of a copolymer prepared from vinyl acetate (97 parts) and N-methylolacrylamide (3 parts), 10% by weight of an aqueous solution containing 33% of a copolymer prepared from 22% acrylic acid, 16% acrylonitrile and 62% ethylacrylate, 0.3% by weight of Gamma-aminopropyltriethoxysilane, and 0.3% by weight of lithium chloride.
Claim 5
Dependent Claim
74 words
The method of claim 1 wherein the ingredients in said aqueous sizing composition consist essentially of: polyacrylamide in an amount equivalent to 4 to 15% by weight of a 30% polyacrylamide solution, melamine-formaldehyde in an amount equivalent to 1.5 to 6% by weight of a 70% melamine formaldehyde solution, a copolymer of vinyl acetate and N-methylolacrylamide in an amount equivalent to 4 to 15% by weight of an emulsion of 50% of said copolymer,
Claim 6
Dependent Claim
33 words
01 to 1% by weight of Gamma aminopropyltriethoxysilane, 0 to 1% by weight of N-methylolacrylamide, monomer, and 0 to 1% by weight of lithium chloride, and contains free formaldehyde and crystallizable acetic acid.
Claim 7
Dependent Claim
33 words
01 to 1% by weight of Gamma aminopropyltriethoxysilane, 0 to 1% by weight of N-methylolacrylamide, monomer, and 0 to 1% by weight of lithium chloride, and contains free formaldehyde and crystallizable acetic acid.
References Cited (Backward Citations)
FR683E
Cited
GB802549A
Cited
GB919318A
Cited
US3116192A
Cited
US3168389A
Cited
FR1490767A
Cited
FR2186440B1
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-19 | 1985-04-20 | 1985-10-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-19 | 1989-04-20 | 1989-10-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-19 | 1993-04-20 | 1993-10-20 | $7700.00 | Window Closed / Lapsed |