Surface coating method employing a temporary bonding
Assignee: Saab Bofors AB
•
Filing: 1976-04-05
•
Granted: 1981-10-06
•
Expires: 1996-04-05
Abstract
Abstract A method of coating which involves applying to a surface a dispersion containing a main bonding agent and a temporary bonding agent. The main bonding agent is not film forming at room temperature. Next the continuous phase of the dispersion is permitted to evaporate or is driven off, followed by precipitation of the main bonding agent and the temporary bonding agent to form a porous powder layer on the surface. The temporary bonding agent bonds the main bonding agent to the surface. The porous layer is then exposed to a solvent which causes the particles of the bonding agents to flow together, and any excess solvent is removed.
Inventors
- 👤 Allan R. B. Furendal
- 👤 Bernt Larsson
- 👤 Erik R. Nilsson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:52
CPC Classifications
B; B05; B05D; B05D3/00; B05D3/06; B05D3/061; B05D3/065; B05D3/067; B05D3/04; B05D3/0466
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
309 words
A method of coating a surface with a coherent coating containing a polymeric material as the main bonding agent wherein said main bonding agent is not film forming at room temperature, but forms the coherent phase of the finished coating which comprises: A. applying to said surface a dispersion containing said main bonding agent dispersed in an inert liquid forming the continuous phase in relation to the dispersed main bonding agent, said dispersion also containing a second and temporary bonding agent in an amount of 0.5-25% by volume based upon the total quantity of solids in the dispersion; B. then allowing the continuous phase of the dispersion to evaporate or be driven off; C. causing said main bonding agent to precipitate in the form of polymer particles having a diameter of 0.1-30 μm wherein the minimum film forming temperature (MFT) of said bonding agent is at least 20° C. above the temperature prevailing in the coating during step B above; D. causing said temporary bonding agent to precipitate at the same time as said main bonding agent to form a porous powder layer on said surface, and wherein the minimum film forming temperature (MFT) of said temporary bonding agent is at least 20° C. below the MFT for said main bonding agent and is below the temperature prevailing in the coating during step B above, and wherein said temporary bonding agent is present in an amount sufficient to bond the particles of said main bonding agent to said surface with sufficiently strong adhesion forces to permit a certain handling of the porous powder layer thus obtained; E. then exposing said porous powder layer to a solvent capable of dissolving said main bonding agent and causing the bonding agent particles to flow together to form a coherent coating; F. then driving off any excess solvent and drying said coherent coating.
Claim 2
Independent Claim
309 words
A method of coating a surface with a coherent coating containing a polymeric material as the main bonding agent wherein said main bonding agent is not film forming at room temperature, but forms the coherent phase of the finished coating which comprises: A. applying to said surface a dispersion containing said main bonding agent dispersed in an inert liquid forming the continuous phase in relation to the dispersed main bonding agent, said dispersion also containing a second and temporary bonding agent in an amount of 0.5-25% by volume based upon the total quantity of solids in the dispersion; B. then allowing the continuous phase of the dispersion to evaporate or be driven off; C. causing said main bonding agent to precipitate in the form of polymer particles having a diameter of 0.1-30 μm wherein the minimum film forming temperature (MFT) of said bonding agent is at least 20° C. above the temperature prevailing in the coating during step B above; D. causing said temporary bonding agent to precipitate at the same time as said main bonding agent to form a porous powder layer on said surface, and wherein the minimum film forming temperature (MFT) of said temporary bonding agent is at least 20° C. below the MFT for said main bonding agent and is below the temperature prevailing in the coating during step B above, and wherein said temporary bonding agent is present in an amount sufficient to bond the particles of said main bonding agent to said surface with sufficiently strong adhesion forces to permit a certain handling of the porous powder layer thus obtained; E. then exposing said porous powder layer to a solvent capable of dissolving said main bonding agent and causing the bonding agent particles to flow together to form a coherent coating; F. then driving off any excess solvent and drying said coherent coating.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein the major portion of said polymer particles formed in step C have a diameter between 0.2 and 2 μm.
Claim 4
Dependent Claim
29 words
The method of claim 1 wherein said temporary bonding agent is present in an amount of 1-12% by volume based upon the total quantity of solids in the dispersion.
Claim 5
Dependent Claim
15 words
The method of claim 1 wherein said solvent has a boiling point of 0°-300° C.
Claim 6
Dependent Claim
15 words
The method of claim 1 wherein said solvent has a boiling point of 20°-140° C.
Claim 7
Dependent Claim
15 words
The method of claim 1 wherein said solvent has a boiling point of 35°-120° C.
Claim 8
Dependent Claim
19 words
The method of claim 1 wherein said temporary bonding agent precipitates in the form of particles of 0.1-1 μm.
Claim 9
Dependent Claim
19 words
The method of claim 1 wherein said temporary bonding agent precipitates in the form of particles of 0.05-0.5 μm.
Claim 10
Dependent Claim
21 words
The method of claim 1 wherein said main bonding agent contains reactive groups for cross-linking after being exposed to said solvent.
Claim 11
Dependent Claim
51 words
The method of claim 9 wherein said main bonding agent is comprised of at least two parts in the form of separate particles in the dispersion and each containing reactive groups for interreacting with each other after being exposed to said solvent and upon flowing together to form said coherent coating.
Claim 12
Dependent Claim
15 words
The method of claim 1 wherein said main bonding agent contains ultraviolet light absorbing groups.
Claim 13
Dependent Claim
14 words
The method of claim 1 wherein said main bonding agent contains corrosion inhibiting groups.
Claim 14
Dependent Claim
29 words
The method of claim 9 wherein said temporary bonding agent comprises reactive groups for interreacting with the reactive groups in said main bonding agent after exposure to said solvent.
Claim 15
Dependent Claim
34 words
The method of claim 1 wherein said temporary bonding agent is chemically unreactive with said main bonding agent and is elastomeric to a degree sufficient to improve the impact strength of the coherent coating.
Claim 16
Dependent Claim
15 words
The method of claim 1 wherein said inert liquid forming the continuous phase is water.
Claim 17
Dependent Claim
13 words
The method of claim 15 wherein said temporary bonding agent is water soluble.
Claim 18
Dependent Claim
19 words
The method of claim 16 wherein said temporary bonding agent further provides for conrolling the consistency of the dispersion.
Claim 19
Dependent Claim
40 words
The method of claim 9 wherein a consistency controlling agent is added to said dispersion and wherein said consistency controlling agent comprises reactive groups for interreacting with the reactive groups of said main bonding agent after exposure to said solvent.
Claim 20
Dependent Claim
40 words
The method of claim 13 wherein as consistency controlling agent is added to said dispersion and wherein said consistency controlling agent comprises reactive groups for interreacting with the reactive groups of said main bonding agent after exposure to said solvent.
Claim 21
Dependent Claim
53 words
The method of claim 1 wherein said dispersion further comprises a pigment in an amount up to 50% concentration of pigment volume (CPV) and wherein the major portion of the size of the particles of said main bonding agent formed in step C does not substantially exceed the grain size of the pigment.
Claim 22
Dependent Claim
47 words
The method of claim 1 wherein said dispersion further comprises a pigment in an amount 5-25% CPV and wherein the major portion of the size of the particles of said main bonding agent formed in step C does not substantially exceed the grain size of the pigment.
Claim 23
Dependent Claim
33 words
The method of claim 1 wherein said dispersion further comprises large grains of up to 5 mm in a maximum amount not substantially exceeding 50% of the total volume of the coherent coating.
Claim 24
Dependent Claim
11 words
The method of claim 22 wherein said grains are abrasive grains.
Claim 25
Dependent Claim
34 words
The method of claim 1 wherein said dispersion further comprises an acid-emitting acid selected from the group consisting of potassium chlorate, potassium perchlorate or mixtures thereof, or further comprises an explosive nitro containing compound.
Claim 26
Dependent Claim
23 words
The method of claim 9 wherein said solvent contains catalyst for promoting the reaction of said reactive groups of said main bonding agent.
Claim 27
Dependent Claim
13 words
The method of claim 1 wherein said solvent comprises a polymer dissolved therein.
Claim 28
Dependent Claim
27 words
The method of claim 9 wherein said solvent comprises a polymer dissolved therein containing reactive groups for reacting with said reactive groups of said main bonding agent.
Claim 29
Dependent Claim
24 words
The method of claim 1 wherein said solvent comprises monomer capable of polymerizing in the presence of an initiator or heat or ultraviolet light.
Claim 30
Dependent Claim
18 words
The method of claim 1 wherein the MFT of said main bonding agent is greater than 45° C.
Claim 31
Dependent Claim
19 words
The method of claim 1 wherein said main bonding agent has a molecular weight of between 500,000 and 1,000,000.
References Cited (Backward Citations)
US1141224A
Cited
US2748019A
Cited
US3288624A
Cited
US3565665A
Cited
US3383775A
Cited
US3676172A
Cited
FR2176395A5
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-05 | 1985-04-06 | 1985-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-05 | 1989-04-06 | 1989-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-05 | 1993-04-06 | 1993-10-06 | $7700.00 | Window Closed / Lapsed |