Grain-oriented electromagnetic steel sheet with improved watt loss
Assignee: Nippon Steel Corp
•
Filing: 1979-07-19
•
Granted: 1981-10-06
•
Expires: 1999-07-19
Abstract
Abstract In a method of producing a grain-oriented electromagnetic steel sheet, a laser beam is irradiated onto the steel sheet, which has been subjected to a final high temperature annealing in order to approximate the crystal orientation of the sheet in a (110), [001] orientation. Because of the laser beam irradiation, regions of high dislocation density are locally formed in the steel sheet and subdivide the magnetic domains, with the result that a low watt loss is achieved.
Inventors
- 👤 Tadashi Ichiyama
- 👤 Shigehiro Yamaguchi
- 👤 Tohru Iuchi
- 👤 Katsuro Kuroki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 22:39
CPC Classifications
C; C21; C21D; C21D9/00; C21D9/46; C21D10/00; C21D8/00; C21D8/12; C21D8/1294; H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/14766; H01F1/14775
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
101 words
In a method of producing a grain-oriented silicon-steel electrical sheet by cold rolling a silicon-steel sheet, with intermediate annealing if necessary, to a standard electrical sheet thickness, decarbonizing the sheet if necessary, and subjecting the sheet to a final high-temperature anneal, so as to produce a grain-oriented silicon-steel electrical sheet having a plurality of magnetic domains; wherein the improvement comprises momentarily irradiating the finally annealed sheet by a laser beam so as to subdivide said domains to an extent appreciably improving the watt loss of the finally annealed sheet as compared to the watt loss it had prior to said irradiating.
Claim 2
Dependent Claim
101 words
In a method of producing a grain-oriented silicon-steel electrical sheet by cold rolling a silicon-steel sheet, with intermediate annealing if necessary, to a standard electrical sheet thickness, decarbonizing the sheet if necessary, and subjecting the sheet to a final high-temperature anneal, so as to produce a grain-oriented silicon-steel electrical sheet having a plurality of magnetic domains; wherein the improvement comprises momentarily irradiating the finally annealed sheet by a laser beam so as to subdivide said domains to an extent appreciably improving the watt loss of the finally annealed sheet as compared to the watt loss it had prior to said irradiating.
Claim 3
Dependent Claim
54 words
A method according to claim 1, wherein said laser beam is irradiated in such a manner that the irradiation satisfies the condition: ##EQU7## wherein d is the width of the laser beam in mm, P is the energy density of the laser beam in J/cm 2 and l is the irradiation distance in mm.
Claim 4
Dependent Claim
12 words
A method according to claim 2, wherein said irradiation condition is: ##EQU8##
Claim 5
Dependent Claim
12 words
A method according to claim 3, wherein said irradiation condition is: ##EQU9##
Claim 6
Dependent Claim
12 words
A method according to claim 4, wherein said irradiation condition is: ##EQU10##
Claim 7
Dependent Claim
21 words
A method according to claim 1, wherein, the irradiation time of said laser beam is from 1 nanosecond to 10 milliseconds.
Claim 8
Dependent Claim
26 words
A method according to claim 1, wherein the irradiation energy of said laser beam is in the range of from 0.5 to 2.5 J/cm 2 .
Claim 9
Dependent Claim
24 words
A method according to claim 1, wherein said laser beam is irradiated onto the steel sheet, on which an insulating film has been applied.
Claim 10
Dependent Claim
35 words
A method according to claim 1, wherein the direction of laser beam irradiation crosses the rolling direction of said steel sheet and its direction of grain orientation, at an angle of from 30° to 90°.
Claim 11
Independent Claim
31 words
The method of claims 2, 3, 4, 5, 6, 7, 8, or 1 in which said laser beam is caused to traverse the sheet at an angle across its grain orientation.
Claim 12
Independent Claim
92 words
A method for improving the watt loss of a silicon-steel electrical sheet of the grain-oriented type produced by a process comprising cold-rolling the sheet completely to a commercial standard electrical sheet thickness and a final high-temperature anneal so as to provide the sheet with a substantially (110) [001] structure having a plurality of magnetic domains; said method comprising irradiating said sheet with laser beam energy so as to subdivide said magnetic domains to a degree improving the watt loss of the sheet without any change in the shape of the sheet surface.
Claim 13
Independent Claim
92 words
A method for improving the watt loss of a silicon-steel electrical sheet of the grain-oriented type produced by a process comprising cold-rolling the sheet completely to a commercial standard electrical sheet thickness and a final high-temperature anneal so as to provide the sheet with a substantially (110) [001] structure having a plurality of magnetic domains; said method comprising irradiating said sheet with laser beam energy so as to subdivide said magnetic domains to a degree improving the watt loss of the sheet without any change in the shape of the sheet surface.
Claim 14
Dependent Claim
23 words
The method of claim 11 in which said irradiating is done is a series of interspaced substantially parallel zones of the sheet's surface.
Claim 15
Dependent Claim
17 words
The method of claim 12 in which said zones are oriented across the grain-orientation of the sheet.
Claim 16
Dependent Claim
51 words
The method of claim 13 in which said irradiating is via a pulsed laser beam having a time period of from 1 NS to 10 ms and a width of from about 0.1 to 1.0 mm, and so that the interspacing distance between adjacent zones ranges from 2.5 to 30 mm.
Claim 17
Dependent Claim
17 words
The method of claim 14 in which said zones are substantially perpendicular to the sheet's grain orientation.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-05 | 1985-04-06 | 1985-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-05 | 1989-04-06 | 1989-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-05 | 1993-04-06 | 1993-10-06 | $7700.00 | Window Closed / Lapsed |