Abstract
Abstract A process of coating glass with tin oxide by exposing the glass to a gaseous medium containing tin tetrachloride vapor under conditions causing formation of the oxide coating by chemical reaction and/or decomposition. The glass is moved continuously through the coating zone and in order to promote a high optical quality of the coating the gaseous medium is formed with a tin tetrachloride concentration corresponding to a partial pressure of at least 2.5×10 -3 atm. and contains water vapor in a concentration corresponding to a partial pressure of at least 10×10 -3 atm. and the gaseous medium contacts the glass face to be coated while said medium is at a temperature of at least 300° C. and such face is at a temperature above 550° C.
Inventors
- 👤 Robert Terneu
- 👤 Albert Van Cauter
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 01:15
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/245; C03C17/2453; C03C17/001; C03C17/002
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
126 words
A process for forming a tin oxide coating on a face of a glass substrate or of a previously formed coating thereon, comprising contacting said face, while said face is at elevated temperature, with a gaseous medium containing tin tetrachloride which undergoes chemical reaction and/or decomposition to form said tin oxide coating, wherein said gaseous medium contains tin tetrachloride in a concentration corresponding to a partial pressure of at least 2.5×10 -3 atm. and contains water vapour in a concentration corresponding to a partial pressure of between 50×10 -3 and 200×10 -3 atm. and is caused to contact said face while the temperature of the gaseous medium is at least 300° C. and the temperature of the glass where said contact occurs is above 550° C.
Claim 2
Dependent Claim
126 words
A process for forming a tin oxide coating on a face of a glass substrate or of a previously formed coating thereon, comprising contacting said face, while said face is at elevated temperature, with a gaseous medium containing tin tetrachloride which undergoes chemical reaction and/or decomposition to form said tin oxide coating, wherein said gaseous medium contains tin tetrachloride in a concentration corresponding to a partial pressure of at least 2.5×10 -3 atm. and contains water vapour in a concentration corresponding to a partial pressure of between 50×10 -3 and 200×10 -3 atm. and is caused to contact said face while the temperature of the gaseous medium is at least 300° C. and the temperature of the glass where said contact occurs is above 550° C.
Claim 3
Dependent Claim
20 words
A process according to claim 1, wherein the gaseous medium is caused to flow along the substrate face being coated.
Claim 4
Dependent Claim
57 words
A process according to claim 2, wherein the gaseous medium is caused to flow along the substrate face being coated, as a substantially turbulence-free layer along a flow passage which is defined in part by the face of the glass and which leads to an exhaust ducting via which residual medium is drawn away from said face.
Claim 5
Dependent Claim
32 words
A process according to claim 3, wherein the height of said flow passage is at no point in excess of 40 mm, said flow passage being measured normally to said substrate face.
Claim 6
Dependent Claim
40 words
A process according to claim 3 or 4, wherein the height of said flow passage decreases in the gas flow direction, at least over an end portion of the length of said flow passage leading up to the exhaust ducting.
Claim 7
Dependent Claim
41 words
A process according to claim 3 or 4, wherein at least over the greater part of the length of said flow passage, said flow passage tapers in the direction of gas flow therethrough, its angle of taper being 10° or less.
Claim 8
Dependent Claim
48 words
A process according to any of claims 2 to 4, wherein the gaseous medium flowing along the substrate face derives at least in part from a gas stream which approaches said face along a path which is at an angle of 45° or less to the substrate face.
Claim 9
Dependent Claim
36 words
A process according to any of claims 1 to 4 wherein the partial pressure of tin tetrachloride in the gaseous medium in contact with the face being coated is from 2.5×10 -3 to 10 -2 atm.
Claim 10
Dependent Claim
42 words
A process according to any of claims 1 to 4 wherein the tin tetrachloride and water vapour are supplied to the coating zone in separate gas streams so that they come into contact in the vicinity of the substrate face being coated.
Claim 11
Dependent Claim
29 words
A process according to any of claims 1 to 4 wherein the tin tetrachloride vapour is delivered to the glass substrate in a stream of nitrogen as carrier gas.
Claim 12
Dependent Claim
54 words
A process according to claim 10, wherein a stream of nitrogen containing tin tetrachloride vapour is caused to flow along the face being coated and a stream of air containing water vapour is delivered into said stream of nitrogen at a position where the stream of nitrogen is in flow along the said face.
Claim 13
Dependent Claim
26 words
A process according to any of claims 1 to 4 wherein a doping agent mixed with moist air is fed to the substrate face being coated.
Claim 14
Dependent Claim
40 words
A process according to any of claims 1 to 4 wherein the concentrations of tin tetrachloride and water vapour in the coating zone are such that a tin oxide coating is formed at a rate of at least 800 A/sec.
Claim 15
Dependent Claim
25 words
A process according to any of claims 1 to 4, wherein the glass substrate is a ribbon of float glass travelling from a float tank.
Claim 16
Dependent Claim
92 words
A process according to claim 14, wherein the ribbon of float glass is contacted with the gaseous medium at a region along the glass ribbon path where the temperature of the glass is in the range 550° to 650° C., the glass ribbon having a speed of at least 6 m/min, and the instantaneous amounts and concentrations of tin tetrachloride and water vapour in the gaseous medium from which the tin oxide deposition takes place being such that the coating forms on the substrate at a rate of at least 800 A/sec.
Claim 17
Dependent Claim
31 words
A process according to any of claims 1 to 4, wherein the tin oxide coating is formed on a previously formed relatively thin coating of another material on the glass substrate.
Claim 18
Dependent Claim
27 words
A process according to claim 1 wherein said gaseous medium contains tin tetrachloride in a concentration corresponding to a partial pressure of at least 5×10 -3 atm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-05 | 1985-04-06 | 1985-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-05 | 1989-04-06 | 1989-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-05 | 1993-04-06 | 1993-10-06 | $7700.00 | Window Closed / Lapsed |