Aluminum based alloy pistons for internal combustion engines
Assignee: Mazda Motor Corp
•
Filing: 1979-05-15
•
Granted: 1981-10-06
•
Expires: 1999-05-15
Abstract
Abstract A piston for internal combustion engines has piston ring grooves at least one of which is totally or partly defined by an embedded body of a Fe based sintered material containing Ni and Cu. The sintered material is of a density of 5.5 to 6.8 g/cm 3 .
Inventors
- 👤 Tuyoshi Morishita
- 👤 Kenji Miyake
- 👤 Kouji Tobita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 20:31
CPC Classifications
C; C22; C22C; C22C38/00; C22C38/08; B; B22; B22F; B22F7/00; B22F7/06; B22F7/08; F; F02; F02F; F02F3/00; F16; F16J; F16J9/00; F16J9/12; F16J9/22; F02B; F02B3/00; F02B3/06; F05; F05C; F05C2201/00; F05C2201/02; F05C2201/021; F05C2201/04; F05C2201/0433; F05C2201/0436; F05C2201/0466; F05C2201/0469; F05C2201/0475; F05C2251/00; F05C2251/04; F05C2251/042; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49229; Y10T29/49249; Y10T29/49265
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
133 words
A piston for internal combustion engines including a crown and peripheral wall, said piston being formed at the peripheral wall with a plurality of piston ring grooves including a top ring groove which is located closest to the crown among the piston ring grooves, insert means being casted in the piston to define at least partly at least said top ring groove, said insert means being made of a sintered particulate homogeneous alloy comprising in weight 8 to 25% of Ni, 4.5 to 7.5% of Cu, less than 2% of C and the balance substantially of Fe and having a density of 5.5 to 6.8 g/cm 3 and a coefficient of thermal expansion of 17 to 23×10 -6 cm/°c.cm, and total amount of Ni and Cu being not less than 15% in weight.
Claim 2
Dependent Claim
133 words
A piston for internal combustion engines including a crown and peripheral wall, said piston being formed at the peripheral wall with a plurality of piston ring grooves including a top ring groove which is located closest to the crown among the piston ring grooves, insert means being casted in the piston to define at least partly at least said top ring groove, said insert means being made of a sintered particulate homogeneous alloy comprising in weight 8 to 25% of Ni, 4.5 to 7.5% of Cu, less than 2% of C and the balance substantially of Fe and having a density of 5.5 to 6.8 g/cm 3 and a coefficient of thermal expansion of 17 to 23×10 -6 cm/°c.cm, and total amount of Ni and Cu being not less than 15% in weight.
Claim 3
Dependent Claim
104 words
A piston for internal combustion engines including a crown and a peripheral wall, said piston being formed at the peripheral wall with a plurality of piston ring grooves including a top ring groove which is located closest to the crown among the piston ring grooves, insert means being casted in the piston to define at least partly at least said top ring groove, said insert means being made of a sintered particulate homogeneous alloy comprising in weight 8 to 25% of Ni, 3.5 to 7.5% of Cu and the balance substantially of Fe and having a density of 5.5 to 6.8 g/cm 3 .
Claim 4
Dependent Claim
104 words
A piston for internal combustion engines including a crown and a peripheral wall, said piston being formed at the peripheral wall with a plurality of piston ring grooves including a top ring groove which is located closest to the crown among the piston ring grooves, insert means being casted in the piston to define at least partly at least said top ring groove, said insert means being made of a sintered particulate homogeneous alloy comprising in weight 8 to 25% of Ni, 3.5 to 7.5% of Cu and the balance substantially of Fe and having a density of 5.5 to 6.8 g/cm 3 .
Claim 5
Dependent Claim
20 words
A piston in accordance with claim 2 in which said insert means contains less than 2% in weight of C.
Claim 6
Dependent Claim
24 words
A piston in accordance with claim 2 in which said insert means has a coefficient of thermal expansion of 17 to 23×10 -6 cm/°C.cm.
Claim 7
Dependent Claim
43 words
The piston of claim 2, wherein said particulate homogeneous alloy consists of by weight 8 to 25% of Ni, 3.5 to 7.5% Cu, less than 0.3% S, less than 2.0% Cr, less than 2% Si, less than 2% C, and the balance Fe.
Claim 8
Dependent Claim
24 words
A piston in accordance with claim 2 or 5 in which total amount of Ni and Cu is not less than 15% in weight.
Claim 9
Dependent Claim
22 words
A piston in accordance with claim 2 or 5 in which said sintered material is applied with a coining process after sintering.
Claim 10
Dependent Claim
21 words
The piston of claim 2 or 5, wherein the Cu content is the particulate between about 4.5 to 7.5% by weight.
Claim 11
Dependent Claim
38 words
The piston of claim 2 or 5, wherein the total amount of Ni and Cu is not less than 15% in weight and wherein said insert has a coefficient of thermal expansion of 17 to 23×10 6 cm/°c.cm.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-05 | 1985-04-06 | 1985-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-05 | 1989-04-06 | 1989-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-05 | 1993-04-06 | 1993-10-06 | $7700.00 | Window Closed / Lapsed |