US4292388A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Image-forming material of aluminum-iron alloy
Assignee: Fujifilm Holdings Corp
•
Filing: 1978-11-14
•
Granted: 1981-09-29
•
Expires: 1998-11-14
Abstract
Abstract A metal image-forming material comprising a base, a photosensitive resin layer formed thereon, and a layer of an aluminum/iron alloy formed between the base and the resin layer. The aluminum/iron alloy layer has superior etchability, and the image-forming material affords images having high contrast and resolving power. The image-forming material is especially suitable for linework and dot etching.
Inventors
- 👤 Tomoaki Ikeda
- 👤 Masamiti Sigyoo
- 👤 Sadaharu Ikeda
- 👤 Satoshi Yoshida
- 👤 Takeshi Tomotsu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:13
CPC Classifications
G; G03; G03F; G03F1/00; G03F1/54
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
111 words
A metal image-forming material for line work and halftone dot images comprising a base, a resist-forming photosensitive resin layer formed thereon, said photosensitive resin layer comprising a monomer, a prepolymer or a polymer, which, when exposed to radiation, chemically changes in its molecular structure and thereby changes in its solvent solubility, and a layer ranging in the thickness from about 300 A to about 1500 A of an aluminum/iron alloy consisting essentially of aluminum and iron, said alloy containing from about 0.2 to about 10 atomic % of iron, formed between said base and said photosensitive resin layer said alloy being entirely removed in areas where exposed to an etching solution.
Claim 2
Dependent Claim
111 words
A metal image-forming material for line work and halftone dot images comprising a base, a resist-forming photosensitive resin layer formed thereon, said photosensitive resin layer comprising a monomer, a prepolymer or a polymer, which, when exposed to radiation, chemically changes in its molecular structure and thereby changes in its solvent solubility, and a layer ranging in the thickness from about 300 A to about 1500 A of an aluminum/iron alloy consisting essentially of aluminum and iron, said alloy containing from about 0.2 to about 10 atomic % of iron, formed between said base and said photosensitive resin layer said alloy being entirely removed in areas where exposed to an etching solution.
Claim 3
Dependent Claim
16 words
The metal image-forming material of claim 1 wherein said aluminum/iron alloy is formed by vacuum deposition.
Claim 4
Dependent Claim
17 words
The metal image-forming material of claim 1, wherein said base comprises a transparent high molecular weight material.
Claim 5
Dependent Claim
33 words
A metal image-forming material as claimed in claim 1 wherein said aluminum/iron alloy consists essentially of from 0.3 to 7 atomic % of iron and from 99.7 to 93 atomic % of aluminum.
Claim 6
Dependent Claim
35 words
The metal image-forming material of claim 1, wherein said photosensitive resin layer comprises a positive working photosensitive resin selected from the group consisting of quinone diazides and a mixture of quinone diazides and phenolic resins.
Claim 7
Dependent Claim
31 words
The metal image-forming material of claim 5, wherein said quinone diazide is a 1,2-naphthoquinone diazide selected from the group consisting of 2,3,4-trihydorxybenzophenone-bis[naphthoquinone-1,2-diazide-5,5-sulfonic acid esters], 2-[naphthoquinone-1,2-diazide-5-sulfonyloxyl]-hydroxy-7-naphthalenes, naphthoquinone-1,2-diazide-5-sulfanilide and naphthoquinone-1,2-diazide-5-sulfonic acid novolac esters.
Claim 8
Dependent Claim
42 words
The metal image-forming material of claim 1, wherein said photosensitive resin layer comprises a negative working photosensitive resin selected from the group consisting of a diazonium salt, an azide compound, a compound containing a cinnamoyl group, an acrylamide and an acrylic ester.
Claim 9
Dependent Claim
35 words
The metal image-forming material of claim 7, wherein said negative working resin is a diazonium salt and a member selected from the group consisting of paraformaldehyde condensate of p-diazodiphenylamine, 1-diazo-4-dimethyl-aminobenzene.sup.. hydrofluoborate, 1-diazo-3-methyl-4-dimethylaniline.sup.. sulfate and 1-diazo-3-monoethylnaphthylamine.
Claim 10
Dependent Claim
44 words
The metal image-forming material of claim 7, wherein said negative working resin is an azide compound and is a member selected from the group consisting of p-phenylenebisazide, p-azidobenzophenone, 4,4'-diazidobenzophenone, 4,4'-diazidodiphenylmethane, 4,4'-diazidostilbene, 4,4'-diazidochalcone, 2,6-bis(p-azidobenzal)cyclohexanone, 2,6-di-(4'-azidebenzal)-4-methylcyclohexanone, polyazide vinyl benzoate, polyazide vinyl phthalate, and polyvinylazide benzal acetal.
Claim 11
Dependent Claim
23 words
The metal image-forming material of claim 9, wherein said azide compound is used as a mixture with a natural or synthetic rubber solution.
Claim 12
Dependent Claim
51 words
The metal image-forming material of claim 7, wherein said negative working photosensitive resin is a compound containing a cinnamoyl group and a member selected from the group consisting of polyvinyl cinnamate, cinnamylidene acetic acid ester derivatives of polyvinyl alcohol, polyvinyl cinnamate.sup.. cinnamylidene acetate, polyvinylcarbethoxymethylcarbamate cinnamylidene acetate, and polyvinyl acetic cinnamylidene acetate.
Claim 13
Dependent Claim
24 words
The metal image-forming material of claim 1, wherein an undercoat layer or intermediate adhesive layer is provided between various layers formed on the base.
Claim 14
Dependent Claim
26 words
The metal image-forming material of claim 1, wherein a protective layer is formed on top of and is directly in contact with the photosensitive resin layer.
Claim 15
Dependent Claim
21 words
The metal image-forming material of claim 1, wherein the optical density of the aluminum/iron alloy layer is at least about 2.0.
References Cited (Backward Citations)
US2965457A
Cited
US3356550A
Cited
US3607484A
Cited
US3715250A
Cited
US3960560A
Cited
US4008084A
Cited
US4098712A
Cited
US4124516A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-28 | 1985-03-30 | 1985-09-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-28 | 1989-03-30 | 1989-09-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-28 | 1993-03-30 | 1993-09-29 | $7700.00 | Window Closed / Lapsed |