Speaker diaphragm and method of preparation of the same
Assignee: Panasonic Holdings Corp
•
Filing: 1979-10-16
•
Granted: 1981-09-29
•
Expires: 1999-10-16
Abstract
Abstract A diaphragm for a speaker which is prepared by heating a conjugated sheet obtained by paper-making polyethylene short fibers with other short fibers which have a high modulus of elasticity, such as carbon fiber, to melt and solidify polyethylene short fibers in the conjugated sheet; the process for the production thereof. The diaphragm for a speaker of the invention has a high modulus of elasticity and a high internal loss and a speaker prepared with such a diaphragm has the advantage of having a wider reproducing frequency response and lower distortion. Furthermore, the process for production of the invention possesses another advantage in that diaphragms for speakers can be produced in a continuous process of successively pressing out the speaker diaphragm with a cold mold press.
Inventors
- 👤 Hirotoshi Niguchi
- 👤 Mitsuru Ieki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:07
CPC Classifications
D; D06; D06M; D06M17/00; D06M17/04; D06M17/06; D06M23/00; D06M23/14; H; H04; H04R; H04R31/00; H04R31/003; H04R7/00; H04R7/02; H04R7/04; H04R7/06; H04R7/10; H04R7/12; H04R7/122; H04R7/125
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
111 words
A diaphragm for a speaker, comprising a sheet, paper-made of polyethylene short fibres being present in an amount of 70% by weight or more, said polyethylene short fibers having a degree of beating of 250 ml (Canadian Freeness), a melt index of not more than 2 g/min. and being not more than 1 millimeter in length and other short fibres between 3 and 10 millimeters in length which have a modulus of elasticity of at least 1.1×10 10 dyne/cm 2 , said polyethylene short fibers being melted to bond with said other short fibres in said sheet; and said diaphragm having a cone or dome shape imparted by pressing while hot.
Claim 2
Dependent Claim
111 words
A diaphragm for a speaker, comprising a sheet, paper-made of polyethylene short fibres being present in an amount of 70% by weight or more, said polyethylene short fibers having a degree of beating of 250 ml (Canadian Freeness), a melt index of not more than 2 g/min. and being not more than 1 millimeter in length and other short fibres between 3 and 10 millimeters in length which have a modulus of elasticity of at least 1.1×10 10 dyne/cm 2 , said polyethylene short fibers being melted to bond with said other short fibres in said sheet; and said diaphragm having a cone or dome shape imparted by pressing while hot.
Claim 3
Dependent Claim
49 words
A diaphragm for a speaker according to claim 1, said other short fibres comprising at least one kind of short fibre selected from the group consisting of aromatic polyamide fibre, glass fibre, silicon fibre, alumina fibre, carbon fibre, boron coated tungsten fibre, boron coated carbon fibre, and phenol fibre.
Claim 4
Dependent Claim
36 words
A diaphragm for a speaker according to claim 1, further comprising at least one kind of emulsion, selected from the group consisting of ethylene-vinyl acetate emulsion, ionomer resin emulsion and polyurethane emulsion, impregnated in said sheet.
Claim 5
Dependent Claim
112 words
A diaphragm for a speaker, comprising laminated plural sheets, paper-made of polyethylene short fibres being present in an amount of 70% by weight or more, said polyethylene short fibers having a degree of beating of 250 ml (Canadian Freeness), a melt index of not more than 2 g/min. and being not more than 1 millimeter in length and other short fibres between 3 and 10 millimeters in length which have a modulus of elasticity of at least 1.1×10 10 dyne/cm 2 , said polyethylene short fibres being melted to bond with said other short fibres in said sheets; and said diaphragm having a cone or dome shape imparted by pressing while hot.
Claim 6
Dependent Claim
112 words
A diaphragm for a speaker, comprising laminated plural sheets, paper-made of polyethylene short fibres being present in an amount of 70% by weight or more, said polyethylene short fibers having a degree of beating of 250 ml (Canadian Freeness), a melt index of not more than 2 g/min. and being not more than 1 millimeter in length and other short fibres between 3 and 10 millimeters in length which have a modulus of elasticity of at least 1.1×10 10 dyne/cm 2 , said polyethylene short fibres being melted to bond with said other short fibres in said sheets; and said diaphragm having a cone or dome shape imparted by pressing while hot.
Claim 7
Dependent Claim
19 words
A diaphragm for a speaker according to claim 4, further comprising a thermoplastic resin film interposed between said sheets.
Claim 8
Dependent Claim
20 words
A diaphragm for a speaker according to claim 5, in which said thermoplastic resin film comprises a modified polyamide film.
Claim 9
Dependent Claim
20 words
A diaphragm for a speaker according to claim 5, in which said thermoplastic resin film comprises an epoxy resin film.
Claim 10
Dependent Claim
126 words
A diaphragm for a speaker comprising sheets, paper-made of polyethylene short fibres being present in an amount of 70% by weight or more, said polyethylene short fibers having a degree of beating of 250 ml (Canadian Freeness), a melt index of not more than 2 g/min. and being not more than 1 millimeter in length and other short fibres between 3 and 10 millimeters in length which have a modulus of elasticity of at least 1.1×10 10 dyne/cm 2 , said polyethylene short fibers being melted to bond with said other short fibres in said sheets; said sheets being thermoadhered on the surface of a core material having a high internal loss; and said diaphragm having a cone or dome shape imparted by pressing while hot.
Claim 11
Dependent Claim
126 words
A diaphragm for a speaker comprising sheets, paper-made of polyethylene short fibres being present in an amount of 70% by weight or more, said polyethylene short fibers having a degree of beating of 250 ml (Canadian Freeness), a melt index of not more than 2 g/min. and being not more than 1 millimeter in length and other short fibres between 3 and 10 millimeters in length which have a modulus of elasticity of at least 1.1×10 10 dyne/cm 2 , said polyethylene short fibers being melted to bond with said other short fibres in said sheets; said sheets being thermoadhered on the surface of a core material having a high internal loss; and said diaphragm having a cone or dome shape imparted by pressing while hot.
Claim 12
Dependent Claim
26 words
A diaphragm for a speaker according to claim 1, further comprising a ring-shaped edge part adhered to the conical or dome shaped part of the diaphragm.
References Cited (Backward Citations)
US3253970A
Cited
US3265557A
Cited
US3256138A
Cited
US3907063A
Cited
US3960794A
Cited
US3930130A
Cited
US3935924A
Cited
US3946832A
Cited
JPS5184248A
Cited
SU562604A1
Cited
US4096313A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-28 | 1985-03-30 | 1985-09-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-28 | 1989-03-30 | 1989-09-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-28 | 1993-03-30 | 1993-09-29 | $7700.00 | Window Closed / Lapsed |