Unsaturated polyester resins and molding compositions containing same
Assignee: Goodrich Corp
•
Filing: 1980-03-27
•
Granted: 1981-09-22
•
Expires: 2000-03-27
Abstract
Abstract The novel aspect of this invention resides in co-reacting a toughening agent with components of an unsaturated polyester resin in order to introduce the toughening agent into the backbone of the unsaturated polyester resin and thus produce a toughened stable resin. Suitable toughening agents are carboxyl and hydroxyl terminated reactive liquid polymers which are used in amount of 1 to 30, preferably 1 to 15 parts by weight per 100 parts by weight of reactant monomers used to prepare the polyester resin.
Inventors
- 👤 Robert J. Bertsch
- 👤 Changkiu K. Riew
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 08:50
CPC Classifications
C; C08; C08G; C08G63/00; C08G63/02; C08G63/12; C08G63/52; C08G63/54
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
54 words
In the process for preparing polyester resins which involves the reaction of an acid and/or anhydride with a hydroxyl-containing compound which forms ester groups upon reaction with the acid and/or anhydride, the improvement comprising co-reacting a carboxyl or a hydroxyl terminated reactive liquid polymer with said acid and/or anhydride and the hydroxyl containing compound.
Claim 2
Dependent Claim
54 words
In the process for preparing polyester resins which involves the reaction of an acid and/or anhydride with a hydroxyl-containing compound which forms ester groups upon reaction with the acid and/or anhydride, the improvement comprising co-reacting a carboxyl or a hydroxyl terminated reactive liquid polymer with said acid and/or anhydride and the hydroxyl containing compound.
Claim 3
Dependent Claim
85 words
Process of claim 1 wherein amount of the reactive liquid polymer is 1 to 30 parts by weight per 100 parts of said acid and/or anhydride and said hydroxyl-containing compound, said carboxyl terminated liquid polymer has a viscosity of 500 to 2,500,000 cps at 25° C. with an average carboxyl group per molecule of 1.5 to 4, and said hydroxyl terminated liquid polymer has a viscosity of 500 to about 100,000,000 cps at 25° C. and a number average molecular weight of 1,000 to 6,000.
Claim 4
Dependent Claim
48 words
Process of claim 2 wherein said acid is a diacid and said acid and said anhydride are unsaturated and contain 4 to 9 carbon atoms per molecule, and said hydroxyl-containing compound is a polyol selected from dihydroxyl and trihydroxyl compounds containing 2 to 12 carbon atoms per molecule.
Claim 5
Dependent Claim
64 words
Process of claim 3 wherein the polyol contains 4 to 6 carbon atoms per molecule, said carboxyl terminated liquid polymer has a viscosity of 5000 to 1,200,000 cps with average number of carboxyl groups per molecule of 1.7 to 3, and the hydroxyl terminated liquid polymer has a viscosity of 5,000 to 2,000,000 cps and a number average molecular weight of 2,000 to 4,000.
Claim 6
Dependent Claim
124 words
Process of claim 1 wherein amount of the liquid polymer is 1 to 30 parts by weight per 100 parts of said acid and/or anhydride and said hydroxyl-containing compound; said acid is a diacid and said acid and said anhydride are unsaturated and contain 4 to 9 carbon atoms per molecule; said hydroxyl-containing compound is a polyol selected from dihydroxyl and trihydroxyl compounds containing 2 to 12 carbon atoms per molecule; the hydroxyl terminated liquid polymer comprises epihalohydrin polymer which has a number average molecular weight of about 800 to 50,000 and viscosity of about 500 to 50,000,000 cps; and the carboxyl terminated liquid polymer has a viscosity of 500 to 2,500,000 cps with an average carboxyl group per molecule of 1.5 to 4.
Claim 7
Dependent Claim
71 words
Process of claim 5 wherein the hydroxyl terminated liquid polymer has molecular weight of about 2,000 to 15,000 and amount of the carboxyl and hydroxyl terminated liquid polymer is about 1 to 15 parts per 100 parts of the diacid and/or anhydride and the polyol, said epihalohydrin polymer is selected from homopolymers of epihalohydrin monomer, copolymers of epihalohydrin monomer and an oxide monomer containing a cyclic oxy ring, and mixtures thereof.
Claim 8
Dependent Claim
35 words
Modified polyester resin which is a reaction product of an acid and/or anhydride, hydroxyl-containing compound which forms ester groups upon reaction with the acid and/or anhydride, and a carboxyl or hydroxyl terminated reactive liquid polymer.
Claim 9
Dependent Claim
35 words
Modified polyester resin which is a reaction product of an acid and/or anhydride, hydroxyl-containing compound which forms ester groups upon reaction with the acid and/or anhydride, and a carboxyl or hydroxyl terminated reactive liquid polymer.
Claim 10
Dependent Claim
78 words
Resin of claim 7 wherein amount of the liquid polymer is 1 to 30 parts by weight per 100 parts of said acid and/or anhydride and said hydroxyl-containing compound, said carboxyl terminated liquid polymer has a viscosity of 500 to 2,500,000 cps with an average carboxyl group per molecule of 1.5 to 4, and said hydroxyl terminated liquid polymer has a viscosity of 500 to about 100,000,000 cps and a number average molecular weight of 1,000 to 6,000.
Claim 11
Dependent Claim
48 words
Resin of claim 8 wherein said acid is a diacid and said acid and said anhydride are unsaturated and contain 4 to 8 carbon atoms per molecule, and said hydroxyl-containing compound is a polyol selected from dihydroxyl and trihydroxyl compounds containing 2 to 12 carbon atoms per molecule.
Claim 12
Dependent Claim
64 words
Resin of claim 9 wherein the polyol contains 4 to 6 carbon atoms per molecule, said carboxyl terminated liquid polymer has a viscosity of 5000 to 1,200,000 cps with average number of carboxyl groups per molecule of 1.7 to 3, and the hydroxyl terminated liquid polymer has a viscosity of 5,000 to 2,000,000 cps and a number average molecular weight of 2,000 to 4,000.
Claim 13
Dependent Claim
124 words
Resin of claim 7 wherein amount of the liquid polymer is 1 to 30 parts by weight per 100 parts of said acid and/or anhydride and said hydroxyl-containing compound; said acid is a diacid and said acid and said anhydride are unsaturated and contain 4 to 9 carbon atoms per molecule; said hydroxyl-containing compound is a polyol selected from dihydroxyl and trihydroxyl compounds containing 2 to 12 carbon atoms per molecule; the hydroxyl terminated liquid polymer comprises epihalohydrin polymer which has a number average molecular weight of about 800 to 50,000 and viscosity of about 500 to 50,000,000 cps; and the carboxyl terminated liquid polymer has a viscosity of 500 to 2,500,000 cps with an average carboxyl group per molecule of 1.5 to 4.
Claim 14
Dependent Claim
83 words
Resin of claim 11 in a solution of polymerizable monomer containing about 20 to 80% solids, wherein the hydroxyl terminated liquid polymer has molecular weight of about 2,000 to 15,000 and amount of the carboxyl and hydroxyl terminated liquid polymer is about 1 to 15 parts per 100 parts of the diacid and/or anhydride and the polyol, said epihalohydrin polymer is selected from homopolymers of epihalohydrin monomer, copolymers of epihalohydrin monomer and an oxide monomer containing a cyclic oxy ring, and mixtures thereof.
Claim 15
Dependent Claim
57 words
Molding composition comprising polyester resin and a particulate filler, said polyester resin being the reaction of an acid and/or anhydride with a hydroxyl-containing compound which forms ester groups upon reaction with the acid and/or anhydride, the improvement comprising co-reacting a carboxyl or a hydroxyl terminated liquid polymer with said acid or anhydride and the hydroxyl containing compound.
Claim 16
Dependent Claim
57 words
Molding composition comprising polyester resin and a particulate filler, said polyester resin being the reaction of an acid and/or anhydride with a hydroxyl-containing compound which forms ester groups upon reaction with the acid and/or anhydride, the improvement comprising co-reacting a carboxyl or a hydroxyl terminated liquid polymer with said acid or anhydride and the hydroxyl containing compound.
Claim 17
Dependent Claim
91 words
Composition of claim 13 wherein amount of the liquid polymer is 1 to 15 parts by weight per 100 parts of said acid and/or anhydride and said hydroxyl-containing compound, said carboxyl terminated liquid polymer has a viscosity of 500 to 4, and said hydroxyl terminated liquid polymer has a viscosity of 500 to 2,500,000 cps with an average carboxyl group per molecule of 1.5 to 4, and said hydroxyl terminated liquid polymer has a viscosity of 500 to about 100,000,000 cps and a number average molecular weight of 1,000 to 6,000.
Claim 18
Dependent Claim
48 words
Composition of claim 14 wherein said acid is a diacid and said acid and said anhydride are unsaturated and contain 4 to 9 carbon atoms per molecule, and said hydroxyl-containing compound is a polyol selected from dihydroxyl and trihydroxyl compounds containing 2 to 12 carbon atoms per molecule.
Claim 19
Dependent Claim
64 words
Composition of claim 15 wherein the polyol contains 4 to 6 carbon atoms per molecule, said carboxyl terminated liquid polymer has a viscosity of 5000 to 1,200,000 cps with average number of carboxyl groups per molecule of 1.7 to 3, and the hydroxyl terminated liquid polymer has a viscosity of 5,000 to 2,000,000 cps and a number average molecular weight of 2,000 to 4,000.
Claim 20
Dependent Claim
124 words
Composition of claim 13 wherein amount of the liquid polymer is 1 to 30 parts by weight per 100 parts of said acid and/or anhydride and said hydroxyl-containing compound; said acid is a diacid and said acid and said anhydride are unsaturated and contain 4 to 9 carbon atoms per molecule; said hydroxyl-containing compound is a polyol selected from dihydroxyl and trihydroxyl compounds containing 2 to 12 carbon atoms per molecule; the hydroxyl terminated liquid polymer comprises epihalohydrin polymer which has a number average molecular weight of about 800 to 50,000 and viscosity of about 500 to 50,000,000 cps; and the carboxyl terminated liquid polymer has a viscosity of 500 to 2,500,000 cps with an average carboxyl group per molecule of 1.5 to 4.
Claim 21
Dependent Claim
44 words
Composition of claim 17 wherein the hydroxyl terminated liquid polymer has molecular weight of about 2,000 to 15,000, said epihalohydrin polymer is selected from homopolymers of epihalohydrin monomer, copolymers of epihalohydrin monomer and an oxide monomer containing a cyclic oxy ring, and mixtures thereof.
Claim 22
Dependent Claim
21 words
Composition of claim 17 wherein said polyester resin is in a solution of a polymerizable monomer containing 20 to 80% solids.
Claim 23
Dependent Claim
60 words
Composition of claim 15 containing a catalytic amount of a catalyst selected from the group consisting of benzoyl peroxide, tertiary butyl perbenzoate, cyclohexanone peroxide, tertiary butyl peroxide, tertiary butyl peroctoate, azoisobutyrodinitrile, and cumene hydroperoxide; and 5 to 70% fibers, based on the total weight of the composition, said fibers are selected from glass, nylon, polyester, aromatic polyamide, and mixtures thereof.
Claim 24
Dependent Claim
60 words
A shaped article comprising an unsaturated polyester resin and a polymerizable monomer, said resin being a reaction product of an acid and/or anhydride with a hydroxyl-containing compound which forms ester groups upon reaction with the acid and/or anhydride, the improvement comprising co-reacting a carboxyl or a hydroxyl terminated liquid polymer with said acid or anhydride and the hydroxyl containing compound.
Claim 25
Dependent Claim
60 words
A shaped article comprising an unsaturated polyester resin and a polymerizable monomer, said resin being a reaction product of an acid and/or anhydride with a hydroxyl-containing compound which forms ester groups upon reaction with the acid and/or anhydride, the improvement comprising co-reacting a carboxyl or a hydroxyl terminated liquid polymer with said acid or anhydride and the hydroxyl containing compound.
Claim 26
Dependent Claim
78 words
Article of claim 21 wherein amount of the liquid polymer is 1 to 15 parts by weight per 100 parts of said acid and/or anhydride and said hydroxyl-containing compound, said carboxyl terminated liquid polymer has a viscosity of 500 to 2,500,000 cps with an average carboxyl group per molecule of 1.5 to 4, and said hydroxyl terminated liquid polymer has a viscosity of 500 to about 100,000,000 cps and a number average molecular weight of 1,000 to 6,000.
Claim 27
Dependent Claim
64 words
Article of claim 22 wherein the polyol contains 4 to 6 carbon atoms per molecule, said carboxyl terminated liquid polymer has a viscosity of 5000 to 1,200,000 cps with average number of carboxyl groups per molecule of 1.7 to 3, and the hydroxyl terminated liquid polymer has a viscosity of 5,000 to 2,000,000 cps and a number average molecular weight of 2,000 to 4,000.
Claim 28
Dependent Claim
100 words
Article of claim 21 wherein said acid is a diacid and said acid and said anhydride are unsaturated and contain 4 to 9 carbon atoms per molecule; said hydroxyl-containing compound is a polyol selected from dihydroxyl and trihydroxyl compounds containing 2 to 12 carbon atoms per molecule; the hydroxyl terminated liquid polymer comprises epihalohydrin polymer which has a number average molecular weight of about 800 to 50,000 and viscosity of about 500 to 50,000,000 cps; and the carboxyl terminated liquid polymer has a viscosity of 500 to 2,500,000 cps with an average carboxyl group per molecule of 1.5 to 4.
References Cited (Backward Citations)
US3431235A
Cited
US3850856A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-21 | 1985-03-23 | 1985-09-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-21 | 1989-03-23 | 1989-09-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-21 | 1993-03-23 | 1993-09-22 | $7700.00 | Window Closed / Lapsed |