US4290819A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method and composition for the removal of phenolic resin coatings from aluminum
Assignee: Boeing Co
•
Filing: 1980-01-03
•
Granted: 1981-09-22
•
Expires: 2000-01-03
Abstract
Abstract A composition and process for the removal of phenolic resin composites from aluminum and its alloys which results in a minimum of corrosion to said metals. The process uses a solvent solution of nitric acid, a hexavalent chromium and incidental water in the proportions of about 0.01-0.12 moles of hexavalent chromium and 1-1.7 moles of H2O per mole HNO3.
Inventors
- 👤 Edwin P. Cornwall
- 👤 Walter Batiuk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 20:33
CPC Classifications
C; C09; C09D; C09D9/00; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31652; Y10T428/31942
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
83 words
A process for removing the phenolic resin coating from a phenolic resin coated aluminum object, comprising the steps of: applying an aqueous solvent solution consisting essentially of from 60 to 76% by weight of HNO 3 and from 2 to 11% by weight of CrO 3 to the phenolic resin coating, maintaining said solvent solution at a temperature of about 160° to 170° F. for a sufficient time to dissolve said phenolic coating, and rinsing with water to remove the solution and drying.
Claim 2
Dependent Claim
83 words
A process for removing the phenolic resin coating from a phenolic resin coated aluminum object, comprising the steps of: applying an aqueous solvent solution consisting essentially of from 60 to 76% by weight of HNO 3 and from 2 to 11% by weight of CrO 3 to the phenolic resin coating, maintaining said solvent solution at a temperature of about 160° to 170° F. for a sufficient time to dissolve said phenolic coating, and rinsing with water to remove the solution and drying.
Claim 3
Dependent Claim
20 words
The process of claim 1 wherein said phenolic resin coating comprises an asbestos impregnated phenolic resin liner for a conduit.
Claim 4
Dependent Claim
24 words
The process of claim 1 wherein said phenolic resin coating comprises a heat and pressure laminated asbestos impregnated phenolic resin liner for a conduit.
Claim 5
Dependent Claim
22 words
The process of claim 1 wherein the phenolic resin coating is first machined to a thickness of about 0.005 inch or under.
Claim 6
Dependent Claim
23 words
The process of claim 2 wherein any grease or oil present on said phenolic resin coating is first removed with sulfate-free cleaning agent.
Claim 7
Dependent Claim
29 words
The process of claim 1 wherein a chemical maskant resistant to said solvent solution is used to mask surfaces and small holes on which no phenolic resin coating exists.
Claim 8
Dependent Claim
22 words
The process of claim 2 wherein said object is immersed for one hour in a solution maintained at 160° to 170° F.
Claim 9
Dependent Claim
49 words
The process of claim 2 and the steps of: removing said object from said solvent solution after about one hour, rinsing said solution from the surface of said object, and removing any remaining residue from the surface of said object by impinging a high pressure stream of water thereon.
Claim 10
Dependent Claim
85 words
A process for removing a phenolic coating from an aluminum substrate, comprising the steps of: applying an aqueous acidic solvent solution consisting essentially of from about 0.01 to 0.12 moles hexavalent chromium, and from about 1 to 1.7 moles water for each mole HNO 3 to the phenolic coating, maintaining said solution in contact with said phenolic coating at a temperature in the range of 100° to 180° F. for a time sufficient to remove said coating, and rinsing said solution from the aluminum substrate.
Claim 11
Dependent Claim
85 words
A process for removing a phenolic coating from an aluminum substrate, comprising the steps of: applying an aqueous acidic solvent solution consisting essentially of from about 0.01 to 0.12 moles hexavalent chromium, and from about 1 to 1.7 moles water for each mole HNO 3 to the phenolic coating, maintaining said solution in contact with said phenolic coating at a temperature in the range of 100° to 180° F. for a time sufficient to remove said coating, and rinsing said solution from the aluminum substrate.
References Cited (Backward Citations)
US3349036A
Cited
US3676219A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-21 | 1985-03-23 | 1985-09-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-21 | 1989-03-23 | 1989-09-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-21 | 1993-03-23 | 1993-09-22 | $7700.00 | Window Closed / Lapsed |