US4289538A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Sealing glass-ceramic articles
Assignee: Corning Glass Works
•
Filing: 1978-09-13
•
Granted: 1981-09-15
•
Expires: 1998-09-13
Abstract
Abstract The method of providing a mechanically strong, hermetic seal, for sealing glass-ceramic articles particularly MACOR® brand machinable glass-ceramics, which seal is capable of withstanding heating in a vacuum to a temperature of up to 900° C. without foaming. The forming of the seal comprises reacting from 0.5-3.0 wt.% antimony metal powder with a devitrifiable glass frit having a coefficient of thermal expansion compatible with the materials being sealed and a melting point of >930° C.
Inventors
- 👤 Francis L. Orso
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 17:45
CPC Classifications
C; C03; C03C; C03C27/00; C03C8/00; C03C8/24; C04; C04B; C04B37/00; C04B37/02; C04B37/023; C04B37/025; C04B37/04; C04B37/045; C04B2235/00; C04B2235/02; C04B2235/50; C04B2235/54; C04B2235/5418; C04B2235/60; C04B2235/604; C04B2235/65; C04B2235/656; C04B2235/6562; C04B2235/6565; C04B2235/6567; C04B2237/00; C04B2237/02; C04B2237/10; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; C04B2237/50; C04B2237/52; C04B2237/70; C04B2237/704
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
141 words
A sealing mixture for forming a seal between glass-ceramic materials, which seal is to be mechanically and dielectrically strong, hermetic and stable without foaming when reheated in vacuum to temperature of 900° C, and which mixture consists of a devitrifiable glass frit having a melting point greater than 930° C., antimony metal powder and sufficient vehicle to provide a sealing mixture with viscosity to effect coating of the materials, the glass frit having a coefficient of thermal expansion sufficiently compatible with the materials being sealed and the antimony metal powder being combined with the frit in an effective amount such that, when reacted with the frit, they will yield a seal characterized by a coefficient of thermal expansion matching those of the materials being sealed and by stability without foaming when heated in a vacuum to a temperature of 900° C.
Claim 2
Dependent Claim
141 words
A sealing mixture for forming a seal between glass-ceramic materials, which seal is to be mechanically and dielectrically strong, hermetic and stable without foaming when reheated in vacuum to temperature of 900° C, and which mixture consists of a devitrifiable glass frit having a melting point greater than 930° C., antimony metal powder and sufficient vehicle to provide a sealing mixture with viscosity to effect coating of the materials, the glass frit having a coefficient of thermal expansion sufficiently compatible with the materials being sealed and the antimony metal powder being combined with the frit in an effective amount such that, when reacted with the frit, they will yield a seal characterized by a coefficient of thermal expansion matching those of the materials being sealed and by stability without foaming when heated in a vacuum to a temperature of 900° C.
Claim 3
Dependent Claim
25 words
The sealing mixture of claim 1 wherein the amount of antimony metal powder is from 0.5 wt.%-3 wt.% of the glass frit plus metal powder.
Claim 4
Dependent Claim
24 words
The sealing mixture of claim 2 wherein the amount of antimony metal powder is preferably from 1-2 wt.% of the frit plus metal powder.
Claim 5
Dependent Claim
15 words
The sealing mixture of claim 1 wherein the glass frit melts at about 950° C.
Claim 6
Dependent Claim
63 words
The mixture of claim 1 wherein the frit consists essentially by weight of 60-85% SiO 2 , 5.5-15% Li 2 O, 2-25% Al 2 O 3 , and proportions of a photosensitive metal selected from the group consisting of about 0.001-0.03% of gold computed as Au, about 0.001-0.3% of silver computed as AgCl, and about 0.001-1% of copper computed as Cu 2 O.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-14 | 1985-03-16 | 1985-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-14 | 1989-03-16 | 1989-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-14 | 1993-03-16 | 1993-09-15 | $7700.00 | Window Closed / Lapsed |