Lightweight materials having a high dielectric constant and their method of manufacture
Assignee: Tokyo Keiki Inc
•
Filing: 1979-08-31
•
Granted: 1981-09-08
•
Expires: 1999-08-31
Abstract
Abstract A lightweight mixed dielectric and a manufacturing method thereof is described, which is prepared by mixing metal-coated expanded particles of plastic, glass or silica, thin-wall metal pipes or metal coated thin-wall plastic pipes and uncoated expanded particles of plastic, glass or silica and then forming the resulting mixture into a desired shape by thermal expansion or by the use of binder with the provision that these uncoated expanded particles are only made of plastic when the forming step is carried out by thermal expansion.
Inventors
- 👤 Hiroshi Ota
- 👤 Noboru Sakuma
- 👤 Takeki Takarabe
- 👤 Isao Takiguchi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 14:52
CPC Classifications
H; H01; H01Q; H01Q15/00; H01Q15/23; H01Q15/02; H01Q15/08; Y; Y10; Y10S; Y10S264/00; Y10S264/06; Y10S264/10; Y10S264/17; Y10T; Y10T428/00; Y10T428/29; Y10T428/2982; Y10T428/2991; Y10T428/2993; Y10T428/2996
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
79 words
A mixed dielectric obtained by mixing the expanded particles selected from the group consisting of expanded polystyrols, expanded polyethylenes, expanded polyurethanes, glass balloons and silica balloons, with metal-coated particles consisting of said expanded particles whose surfaces have been coated with a thin film selected from the group of chromium, aluminum, copper, nickel, gold, silver and magnesium in proper proportions to obtain a desired dielectric constant and then forming the same to a desired shape by the use of binder.
Claim 2
Dependent Claim
79 words
A mixed dielectric obtained by mixing the expanded particles selected from the group consisting of expanded polystyrols, expanded polyethylenes, expanded polyurethanes, glass balloons and silica balloons, with metal-coated particles consisting of said expanded particles whose surfaces have been coated with a thin film selected from the group of chromium, aluminum, copper, nickel, gold, silver and magnesium in proper proportions to obtain a desired dielectric constant and then forming the same to a desired shape by the use of binder.
Claim 3
Dependent Claim
21 words
A mixed dielectric according to claim 1, wherein the metal films of said metal-coated particles are 2μ to 6μ in thickness.
Claim 4
Dependent Claim
19 words
A mixed dielectric according to claim 1, wherein said expanded particles are 0.5 mm to 3.0 mm in diameter.
Claim 5
Dependent Claim
25 words
A mixed dielectric according to claim 1, wherein the binder is selected from the group consisting of vinyl acetic polymer, silicone rubber, and epoxy resin.
Claim 6
Dependent Claim
33 words
A mixed dielectric according to claim 1, wherein the binder is present in an amount of 0.03 to 0.08 grams per unit volume as expressed in cm 3 , of the mixed dielectric.
Claim 7
Dependent Claim
90 words
A mixed dielectric obtained by mixing the expanded particles selected from the group consisting of expanded polystyrenes, expanded polyethylenes, expanded polyurethanes, glass balloons and silica balloons, with thin-wall tubes selected from the group consisting of aluminum, copper and plastic tubes coated with a thin film selected from the group of chromium, aluminum, copper, nickel, gold, silver and magnesium in proper proportions to obtain a desired dielectric constant and forming the same to a desired shape by the use of binder, said plastic tubes formed from polyvinyl chloride, polystyrene or polyethylene.
Claim 8
Dependent Claim
90 words
A mixed dielectric obtained by mixing the expanded particles selected from the group consisting of expanded polystyrenes, expanded polyethylenes, expanded polyurethanes, glass balloons and silica balloons, with thin-wall tubes selected from the group consisting of aluminum, copper and plastic tubes coated with a thin film selected from the group of chromium, aluminum, copper, nickel, gold, silver and magnesium in proper proportions to obtain a desired dielectric constant and forming the same to a desired shape by the use of binder, said plastic tubes formed from polyvinyl chloride, polystyrene or polyethylene.
Claim 9
Dependent Claim
23 words
A mixed dielectric according to claim 6, wherein the metal film of said metal-coated plastic tubes is from 2μ to 6μ in thickness.
Claim 10
Dependent Claim
32 words
A mixed dielectric according to claim 6, wherein said thin-wall aluminum, copper and plastic tubes are from 0.1 mm to 1 mm in diameter and 2 mm to 5 mm in length.
Claim 11
Dependent Claim
19 words
A mixed dielectric according to claim 6, wherein said expanded particles are 0.5 mm to 3.0 mm in diameter.
Claim 12
Dependent Claim
21 words
A mixed dielectric according to claim 6, wherein vinyl acetate polymer, silicone rubber or epoxy resin is used as the binder.
Claim 13
Dependent Claim
22 words
A mixed dielectric according to claim 6, wherein the binder is mixed at a rate of 0.03 to 0.08 g/cm 3 .
Claim 14
Dependent Claim
146 words
A manufacturing method of a mixed dielectric obtained by mixing and forming expanded plastic particles selected from the group consisting of expanded polystyrols, expanded polyethylenes and expanded polyurethanes, with metal coated particles consisting of said expanded plastic particles whose surfaces have been coated with a thin film selected from the group of chromium, aluminum, copper, nickel, gold, silver and magnesium, comprising the steps of: pre-expanding plastic crude particles selected from the group consisting of polystyrols, polyethylenes, polyurethanes by adjusting the expansion ratio in such a manner that the resulting pre-expanded plastic particles have the same specific gravity as said metal-coated particles, and mixing said pre-expanded particles and said metal-coated particles in proper proportions to obtain a desired dielectric constant and then forming the same to a desired shape by thermal expansion or by the use of a binder to obtain a material having homogeneous dielectric constant.
Claim 15
Dependent Claim
146 words
A manufacturing method of a mixed dielectric obtained by mixing and forming expanded plastic particles selected from the group consisting of expanded polystyrols, expanded polyethylenes and expanded polyurethanes, with metal coated particles consisting of said expanded plastic particles whose surfaces have been coated with a thin film selected from the group of chromium, aluminum, copper, nickel, gold, silver and magnesium, comprising the steps of: pre-expanding plastic crude particles selected from the group consisting of polystyrols, polyethylenes, polyurethanes by adjusting the expansion ratio in such a manner that the resulting pre-expanded plastic particles have the same specific gravity as said metal-coated particles, and mixing said pre-expanded particles and said metal-coated particles in proper proportions to obtain a desired dielectric constant and then forming the same to a desired shape by thermal expansion or by the use of a binder to obtain a material having homogeneous dielectric constant.
References Cited (Backward Citations)
US2716190A
Cited
US2883347A
Cited
US3079289A
Cited
US3088713A
Cited
US3243483A
Cited
US3256373A
Cited
US3255453A
Cited
US3470561A
Cited
US3507940A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-07 | 1985-03-09 | 1985-09-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-07 | 1989-03-09 | 1989-09-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-07 | 1993-03-09 | 1993-09-08 | $7700.00 | Window Closed / Lapsed |