Thermosetting powder based on an unsaturated polyester resin
Assignee: DSM BV
•
Filing: 1980-04-24
•
Granted: 1981-09-01
•
Expires: 2000-04-24
Abstract
Abstract A thermosetting powder based on a homogeneous mixture containing 50 to 92% by weight of an unsaturated polyester resin having a softening temperature of at least 50° C. 50 to 30% bij weight of a prepolymer of a diallylester of an aromatic dicarboxylic acid, 3 to 20% by weight of a high boiling, crosslinking monomer and 0.1 to 5% by weight of hardening catalyst, all weight percentages relating to the overall quantity of the polymerizable components. A process for the preparation of the thermosetting powder by melting and mixing the polyester resin and at least the greater part of the other polymerizable components except the catalyst subsequently the catalyst and the remaining portion of the polymerizable components is rapidly admixed to the melt at a temperature that is at least 20° lower than the temperature corresponding to a half life time of 1 minute in which operation the time during which the catalyst is exposed to the higher temperature is max. 30 sec. after which the mixture is rapidly cooled and ground.
Inventors
- 👤 Rene L. E. Van Gasse
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 19:35
CPC Classifications
C; C08; C08F; C08F299/00; C08F299/02; C08F299/04; C08F299/0478; C08L; C08L67/00; C08L67/06
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
102 words
A thermosetting powder based on an unsaturated polyester resin having a softening temperature of at least 50° C. wherein said powder comprises a homogeneous mixture containing 50 to 92% by weight of unsaturated polyester resin, 5 to 30% by weight of a prepolymer of a diallylester of an aromatic dicarboxylic acid, 3 to 20% by weight of high-boiling, cross-linking monomer having a boiling point greater than 200° C. and a vapor pressure less than 10 mm mercury at 150° C., and 0.1 to 5% by weight of hardening catalyst, these weight percentages relating to the overall quantity of the abovementioned polymerizable components.
Claim 2
Dependent Claim
102 words
A thermosetting powder based on an unsaturated polyester resin having a softening temperature of at least 50° C. wherein said powder comprises a homogeneous mixture containing 50 to 92% by weight of unsaturated polyester resin, 5 to 30% by weight of a prepolymer of a diallylester of an aromatic dicarboxylic acid, 3 to 20% by weight of high-boiling, cross-linking monomer having a boiling point greater than 200° C. and a vapor pressure less than 10 mm mercury at 150° C., and 0.1 to 5% by weight of hardening catalyst, these weight percentages relating to the overall quantity of the abovementioned polymerizable components.
Claim 3
Dependent Claim
55 words
A thermosetting powder according to claim 1, wherein said powder contains 57.5 to 84% by weight of polyester resin, 7.5 to 25% by weight of a prepolymer of a diallylester of an aromatic dicarboxylic acid, 5 to 15% by weight of said high-boiling cross-linking monomer, and 1.0 to 2.5% by weight of said hardening catalyst.
Claim 4
Dependent Claim
30 words
A thermosetting powder according to claims 1 and 2, wherein said hardening catalyst has a half-life value of one minute at a temperature of between 115° C. and 150° C.
Claim 5
Dependent Claim
188 words
A process for the preparation of a thermosetting fiberless coating powder based on an unsaturated polyester resin having a softening temperature of at least 50° C. comprising the steps of: (a) admixing to a melt a homogeneous mixture consisting essentially of 50 to 92 weight percent of an unsaturated polyester resin, 5 to 30 weight percent prepolymer of a diallylester of an aromatic dicarboxylic acid, and from 3 to 20 weight percent of a high-boiling point, cross-linking monomer having a boiling point greater than 200° C. and a vapor pressure less than 10 mm mercury at 150° C., in the absence of the hardening catalyst; and (b) admixing to the mixture of step (a), the hardening catalyst and the remaining portion, if any, of the components other than the polyester resin at a temperature that is at least 20° C. lower than the temperature at which the half-life value of the hardening catalyst is 1 minute, in which operation the time during which the hardening catalyst is exposed to the higher temperature is a maximum of 30 seconds, after which the mixture is rapidly cooled and then ground.
Claim 6
Dependent Claim
188 words
A process for the preparation of a thermosetting fiberless coating powder based on an unsaturated polyester resin having a softening temperature of at least 50° C. comprising the steps of: (a) admixing to a melt a homogeneous mixture consisting essentially of 50 to 92 weight percent of an unsaturated polyester resin, 5 to 30 weight percent prepolymer of a diallylester of an aromatic dicarboxylic acid, and from 3 to 20 weight percent of a high-boiling point, cross-linking monomer having a boiling point greater than 200° C. and a vapor pressure less than 10 mm mercury at 150° C., in the absence of the hardening catalyst; and (b) admixing to the mixture of step (a), the hardening catalyst and the remaining portion, if any, of the components other than the polyester resin at a temperature that is at least 20° C. lower than the temperature at which the half-life value of the hardening catalyst is 1 minute, in which operation the time during which the hardening catalyst is exposed to the higher temperature is a maximum of 30 seconds, after which the mixture is rapidly cooled and then ground.
Claim 7
Dependent Claim
48 words
A process for the preparation of a thermosetting powder according to claim 4, wherein said hardening catalyst is admixed at a temperature of between 85° and 110° C., with the time during which said hardening catalyst is exposed to the higher temperature being a maximum of 15 seconds.
References Cited (Backward Citations)
US3926902A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-31 | 1985-03-02 | 1985-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-31 | 1989-03-02 | 1989-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-31 | 1993-03-02 | 1993-09-01 | $7700.00 | Window Closed / Lapsed |