Flash resistant epoxy encapsulating composition and process for preparing same
Assignee: Cookson Singapore Pte Ltd
•
Filing: 1980-01-14
•
Granted: 1981-09-01
•
Expires: 2000-01-14
Abstract
Abstract A flash resistant epoxy encapsulating composition and its process of manufacture. The composition comprises a blend of from about 15 to about 80 weight percent epoxy resin, from about 9 to about 82 weight percent filler, from about 0.01 to about 2 percent catalyst by weight of resin, from about 10 to about 50 percent hardener by weight of resin, from about 3 to about 12 percent flash retardant by combined weight of resin and hardener and up to about 1.5 weight percent lubricant. The cured blend physically consists essentially of particles intimately and entirely embedded in a matrix. The process comprises blending the components of the above blend followed by milling the resulting blend between the rolls of a differential roll mill equipped with plows where the rolls have different surface temperatures, the hotter of the rolls being near the melting temperature of the resin.
Inventors
- 👤 Robert K. Rosler
- 👤 Donald B. Gore
- 👤 Malcolm N. Riddell
- 👤 Earl R. Hunt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 15:02
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/20; C08J3/201; B; B29; B29B; B29B7/00; B29B7/002; B29B7/007; B29B7/30; B29B7/34; B29B7/52; B29B7/56; B29B7/562; H; H10; H10W; H10W74/00; H10W74/40; H10W74/47; H10W74/473; B29K; B29K2063/00; C08J2363/00
Claims Analysis
Total Claims: 83
Claim 1
Independent Claim
281 words
A process for the preparation of a flash resistant epoxy encapsulating composition comprising: (a) blending a flash retarding composition with at least one each of an epoxy resin, a resin hardener, and a catalyst to obtain at least one resulting blend; (b) milling each resulting blend between rolls of a differential roll mill which comprises a hot roller and a cold roller spaced between one and six millimeters apart along the lengths thereof, said rollers being rotated in opposite directions toward each other at their upper portions at different surface velocities about their respective longitudinal axes, which are approximately horizontally disposed, the surface temperature of said hot roller being near the melting temperature of said resin for a blend containing resin but at a temperature insufficient to cure said resin within the residence time of the resin on the hot roller of the mill, said mill being further supplied with a series of plows having edges, each of said plows being mounted approximately above the hot roller about a 10° to 50° angle to planes perpendicular to the longitudinal axis of said hot roller, said edges being shaped and said plows being mounted such that each of the edges are within 2 millimeters of the surface of the hot roller for a distance equal to at least 5% of the circumference of the hot roller, said plows being positioned such that each such blend introduced at a feed position of said differential roll mill is forced by said plows along said rotating hot roller to a discharge position of said differential roll mill; and (c) when more than one blend is made, mixing said milled blends to form the encapsulating composition.
Claim 2
Dependent Claim
281 words
A process for the preparation of a flash resistant epoxy encapsulating composition comprising: (a) blending a flash retarding composition with at least one each of an epoxy resin, a resin hardener, and a catalyst to obtain at least one resulting blend; (b) milling each resulting blend between rolls of a differential roll mill which comprises a hot roller and a cold roller spaced between one and six millimeters apart along the lengths thereof, said rollers being rotated in opposite directions toward each other at their upper portions at different surface velocities about their respective longitudinal axes, which are approximately horizontally disposed, the surface temperature of said hot roller being near the melting temperature of said resin for a blend containing resin but at a temperature insufficient to cure said resin within the residence time of the resin on the hot roller of the mill, said mill being further supplied with a series of plows having edges, each of said plows being mounted approximately above the hot roller about a 10° to 50° angle to planes perpendicular to the longitudinal axis of said hot roller, said edges being shaped and said plows being mounted such that each of the edges are within 2 millimeters of the surface of the hot roller for a distance equal to at least 5% of the circumference of the hot roller, said plows being positioned such that each such blend introduced at a feed position of said differential roll mill is forced by said plows along said rotating hot roller to a discharge position of said differential roll mill; and (c) when more than one blend is made, mixing said milled blends to form the encapsulating composition.
Claim 3
Dependent Claim
251 words
A process for the preparation of a flash resistant epoxy encapsulating composition comprising: (a) blending components comprising at least one each of an epoxy resin, a resin hardener, a catalyst and a flash retarding composition; and (b) milling the resulting blend between rolls of a differential roll mill which comprises a hot roller and a cold roller spaced between one and four millimeters apart along the lengths thereof, said rollers being rotated in opposite directions at different surface velocities about their respective longitudinal axes, which are approximately horizontally disposed, the surface temperature of said hot roller being near the melting temperature of said resin for a blend containing resin but at a temperature insufficient to cure said resin within the residence time of the resin on the hot roller of the mill, said mill being further supplied with a series of plows having edges, each of said plows being mounted approximately above the hot roller at a 10° to 50° angle to planes perpendicular to the longitudial axis of said hot roller, said edges being shaped and said plows being mounted such that each of the edges are within 2 millimeters of the surface of the hot roller for a distance equal to at least 5% of the circumference of the hot roller, said plows being positioned such that each such blend introduced at a feed position of said differential roll mill is forced by said plows along said rotating hot roller to a discharge position of said differential roll mill.
Claim 4
Dependent Claim
251 words
A process for the preparation of a flash resistant epoxy encapsulating composition comprising: (a) blending components comprising at least one each of an epoxy resin, a resin hardener, a catalyst and a flash retarding composition; and (b) milling the resulting blend between rolls of a differential roll mill which comprises a hot roller and a cold roller spaced between one and four millimeters apart along the lengths thereof, said rollers being rotated in opposite directions at different surface velocities about their respective longitudinal axes, which are approximately horizontally disposed, the surface temperature of said hot roller being near the melting temperature of said resin for a blend containing resin but at a temperature insufficient to cure said resin within the residence time of the resin on the hot roller of the mill, said mill being further supplied with a series of plows having edges, each of said plows being mounted approximately above the hot roller at a 10° to 50° angle to planes perpendicular to the longitudial axis of said hot roller, said edges being shaped and said plows being mounted such that each of the edges are within 2 millimeters of the surface of the hot roller for a distance equal to at least 5% of the circumference of the hot roller, said plows being positioned such that each such blend introduced at a feed position of said differential roll mill is forced by said plows along said rotating hot roller to a discharge position of said differential roll mill.
Claim 5
Dependent Claim
46 words
The process of claim 1 wherein from 2 to 16 plows are used, the rollers are spaced between 1 and 4 millimeters apart and the majority of the plows are at approximately the same angle to planes perpendicular to the rotational axis of the hot roller.
Claim 6
Dependent Claim
26 words
The process of claim 1 wherein from about 15 to about 80 percent epoxy resin by weight of finished composition is used in a blending step.
Claim 7
Dependent Claim
26 words
The process of claim 3 wherein from about 20 to about 65 percent epoxy resin by weight of finished composition is used in a blending step.
Claim 8
Dependent Claim
28 words
The process of claim 4 wherein from about 9 to about 82 percent filler by weight of finished composition is included as a component in a blending step.
Claim 9
Dependent Claim
24 words
The process of claim 1 wherein from about 0.01 to about 2 percent catalyst is used by weight of resin in the finished composition.
Claim 10
Dependent Claim
24 words
The process of claim 3 wherein from about 0.01 to about 2 percent catalyst is used by weight of resin in the finished composition.
Claim 11
Dependent Claim
24 words
The process of claim 4 wherein from about 0.01 to about 2 percent catalyst is used by weight of resin in the finished composition.
Claim 12
Dependent Claim
24 words
The process of claim 6 wherein from about 0.01 to about 2 percent catalyst is used by weight of resin in the finished composition.
Claim 13
Dependent Claim
35 words
The process of claim 1 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by combined weight of resin and hardener in the finished composition.
Claim 14
Dependent Claim
35 words
The process of claim 3 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by combined weight of resin and hardener in the finished composition.
Claim 15
Dependent Claim
35 words
The process of claim 4 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by combined weight of resin and hardener in the finished composition.
Claim 16
Dependent Claim
35 words
The process of claim 5 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by combined weight of resin and hardener in the finished composition.
Claim 17
Dependent Claim
35 words
The process of claim 6 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by combined weight of resin and hardener in the finished composition.
Claim 18
Dependent Claim
35 words
The process of claim 7 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by combined weight of resin and hardener in the finished composition.
Claim 19
Dependent Claim
35 words
The process of claim 8 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by combined weight of resin and hardener in the finished composition.
Claim 20
Dependent Claim
35 words
The process of claim 9 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by combined weight of resin and hardener in the finished composition.
Claim 21
Dependent Claim
24 words
The process of claim 2 wherein from 2 to 16 plows are used and the rollers are spaced between 1 and 4 millimeters apart.
Claim 22
Dependent Claim
23 words
The process of claim 19 wherein adjacent plows intersect at least one common plane perpendicular to the rotational axis of the hot roller.
Claim 23
Dependent Claim
28 words
The process of claim 19 wherein adjacent plows are each within 4 centimeters of at least one identical plane perpendicular to the rotational axis of the hot roller.
Claim 24
Dependent Claim
28 words
The process of claim 19 wherein adjacent plows are each within 12 centimeters of at least one identical plane perpendicular to the rotational axis of the hot roller.
Claim 25
Dependent Claim
28 words
The process of claim 22 wherein the majority of the plows are at approximately the same angle to planes perpendicular to the rotational axis of the hot roller.
Claim 26
Dependent Claim
30 words
The process of claim 2 wherein from about 9 to about 82 percent of a filler by weight of finished composition is included as a component in the blending step.
Claim 27
Dependent Claim
30 words
The process of claim 19 wherein from about 9 to about 82 percent of a filler by weight of finished composition is included as a component in the blending step.
Claim 28
Dependent Claim
30 words
The process of claim 23 wherein from about 9 to about 82 percent of a filler by weight of finished composition is included as a component in the blending step.
Claim 29
Dependent Claim
25 words
The process of claim 2 wherein from about 15 to about 80 percent resin by weight of finished composition is used in the blending step.
Claim 30
Dependent Claim
25 words
The process of claim 19 wherein from about 15 to about 80 percent resin by weight of finished composition is used in the blending step.
Claim 31
Dependent Claim
25 words
The process of claim 23 wherein from about 15 to about 80 percent resin by weight of finished composition is used in the blending step.
Claim 32
Dependent Claim
25 words
The process of claim 24 wherein from about 15 to about 80 percent resin by weight of finished composition is used in the blending step.
Claim 33
Dependent Claim
25 words
The process of claim 25 wherein from about 15 to about 80 percent resin by weight of finished composition is used in the blending step.
Claim 34
Dependent Claim
25 words
The process of claim 26 wherein from about 15 to about 80 percent resin by weight of finished composition is used in the blending step.
Claim 35
Dependent Claim
25 words
The process of claim 2 wherein from about 20 to about 65 percent resin by weight of finished composition is used in the blending step.
Claim 36
Dependent Claim
25 words
The process of claim 19 wherein from about 20 to about 65 percent resin by weight of finished composition is used in the blending step.
Claim 37
Dependent Claim
25 words
The process of claim 23 wherein from about 20 to about 65 percent resin by weight of finished composition is used in the blending step.
Claim 38
Dependent Claim
25 words
The process of claim 24 wherein from about 20 to about 65 percent resin by weight of finished composition is used in the blending step.
Claim 39
Dependent Claim
25 words
The process of claim 25 wherein from about 20 to about 65 percent resin by weight of finished composition is used in the blending step.
Claim 40
Dependent Claim
25 words
The process of claim 26 wherein from about 20 to about 65 percent resin by weight of finished composition is used in the blending step.
Claim 41
Dependent Claim
23 words
The process of claim 2 wherein from about 0.01 to about 2 percent catalyst by weight of resin is used in the blend.
Claim 42
Dependent Claim
23 words
The process of claim 19 wherein from about 0.01 to about 2 percent catalyst by weight of resin is used in the blend.
Claim 43
Dependent Claim
23 words
The process of claim 23 wherein from about 0.01 to about 2 percent catalyst by weight of resin is used in the blend.
Claim 44
Dependent Claim
23 words
The process of claim 29 wherein from about 0.01 to about 2 percent catalyst by weight of resin is used in the blend.
Claim 45
Dependent Claim
23 words
The process of claim 38 wherein from about 0.01 to about 2 percent catalyst by weight of resin is used in the blend.
Claim 46
Dependent Claim
31 words
The process of claim 2 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by weight of resin in the blend.
Claim 47
Dependent Claim
31 words
The process of claim 19 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by weight of resin in the blend.
Claim 48
Dependent Claim
31 words
The process of claim 23 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by weight of resin in the blend.
Claim 49
Dependent Claim
31 words
The process of claim 29 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by weight of resin in the blend.
Claim 50
Dependent Claim
31 words
The process of claim 42 wherein the flash retarding composition is fumed silica in a quantity of from about 3 to about 12 percent by weight of resin in the blend.
Claim 51
Dependent Claim
21 words
The process of claim 2 wherein up to about 1.5 percent lubricant by weight of blend is included in the blend.
Claim 52
Dependent Claim
21 words
The process of claim 19 wherein up to about 1.5 percent lubricant by weight of blend is included in the blend.
Claim 53
Dependent Claim
21 words
The process of claim 23 wherein up to about 1.5 percent lubricant by weight of blend is included in the blend.
Claim 54
Dependent Claim
21 words
The process of claim 29 wherein up to about 1.5 percent lubricant by weight of blend is included in the blend.
Claim 55
Dependent Claim
21 words
The process of claim 42 wherein up to about 1.5 percent lubricant by weight of blend is included in the blend.
Claim 56
Dependent Claim
21 words
The process of claim 48 wherein up to about 1.5 percent lubricant by weight of blend is included in the blend.
Claim 57
Dependent Claim
27 words
The process of claim 2 wherein from about 10 to about 50 percent hardener by weight of resin in the finished composition is incorporated into the blend.
Claim 58
Dependent Claim
27 words
The process of claim 19 wherein from about 10 to about 50 percent hardener by weight of resin in the finished composition is incorporated into the blend.
Claim 59
Dependent Claim
27 words
The process of claim 23 wherein from about 10 to about 50 percent hardener by weight of resin in the finished composition is incorporated into the blend.
Claim 60
Dependent Claim
27 words
The process of claim 29 wherein from about 10 to about 50 percent hardener by weight of resin in the finished composition is incorporated into the blend.
Claim 61
Dependent Claim
27 words
The process of claim 42 wherein from about 10 to about 50 percent hardener by weight of resin in the finished composition is incorporated into the blend.
Claim 62
Dependent Claim
27 words
The process of claim 48 wherein from about 10 to about 50 percent hardener by weight of resin in the finished composition is incorporated into the blend.
Claim 63
Dependent Claim
27 words
The process of claim 54 wherein from about 10 to about 50 percent hardener by weight of resin in the finished composition is incorporated into the blend.
Claim 64
Dependent Claim
21 words
The process of any of claims 55 through 61 in the alternative wherein the resin is an epoxidized aromatic alcohol novolac.
Claim 65
Dependent Claim
20 words
The process of any of claims 55 through 61 in the alternative wherein the resin is an epoxidized phenol novolac.
Claim 66
Dependent Claim
12 words
The process of claim 62 wherein the hardener is a phenol-derived hardener.
Claim 67
Dependent Claim
12 words
The process of claim 63 wherein the hardener is a phenol-derived hardener.
Claim 68
Dependent Claim
14 words
The process of claim 18 wherein the resin is an epoxidized aromatic alcohol novolac.
Claim 69
Dependent Claim
13 words
The process of claim 18 wherein the resin is an epoxidized phenol novolac.
Claim 70
Dependent Claim
12 words
The process of claim 66 wherein the hardener is a phenol-derived hardener.
Claim 71
Dependent Claim
21 words
The process of any of claims 1 through 61 in the alternative wherein the blending is done in a ball mill.
Claim 72
Dependent Claim
36 words
The process of any of claims 55 through 61 in the alternative wherein from about 0.01 to about 3 percent of colorant by weight of resulting blend is included as a component in the blending step.
Claim 73
Dependent Claim
39 words
The process of any of claims 55 through 61 in the alternative wherein from about 0.5 to about 10 percent of a flame retardant composition by weight of resulting blend is included as a component in the blending step.
Claim 74
Dependent Claim
25 words
The process of any of claims 1 through 61 in the alternative wherein the relative rotational speed of the rollers is between 1.1:1 and 1.3:1.
Claim 75
Dependent Claim
19 words
The process of claim 72 wherein the rotational speed of the hot roller is from 10 to 30 rpm.
Claim 76
Dependent Claim
26 words
The process of any of claims 55 through 61 in the alternative wherein the surface temperature of the hot roller is between 65° and 95° C.
Claim 77
Dependent Claim
19 words
The process of claim 18 wherein the surface temperature of the hot roller is between 65° and 95° C.
Claim 78
Dependent Claim
19 words
The process of claim 18 wherein the residence time from inlet to outlet is between 15 and 120 seconds.
Claim 79
Dependent Claim
26 words
The process of any of claims 55 through 61 in the alternative wherein the residence time from inlet to outlet is between 15 and 120 seconds.
Claim 80
Dependent Claim
36 words
The process of claim 18 wherein prior to milling, each blend is compacted into particles having an average particle size of from 3 to 6 millimeters in diameter and from 3 to 12 centimeters in length.
Claim 81
Dependent Claim
41 words
The process of any of claims 55 through 61 in the alternative wherein prior to milling, the blend is compacted into particles having an average particle size of from 3 to 6 millimeters and from 3 to 12 centimeters in length.
Claim 82
Dependent Claim
97 words
A flash resistant epoxy encapsulating composition comprising a blend of from about 15 to about 80 weight percent epoxy resin, from about 9 to about 82 weight percent filler, from about 0.01 to about 2 percent catalyst by weight of resin, from about 10 to about 50 percent resin hardener by weight of resin in the composition, from about 3 to about 12 percent flash retardant by combined weight of resin and hardener; and up to about 1.5 weight percent lubricant wherein the cured composition physically consists essentially of particles intimately and entirely embedded in a matrix.
Claim 83
Dependent Claim
97 words
A flash resistant epoxy encapsulating composition comprising a blend of from about 15 to about 80 weight percent epoxy resin, from about 9 to about 82 weight percent filler, from about 0.01 to about 2 percent catalyst by weight of resin, from about 10 to about 50 percent resin hardener by weight of resin in the composition, from about 3 to about 12 percent flash retardant by combined weight of resin and hardener; and up to about 1.5 weight percent lubricant wherein the cured composition physically consists essentially of particles intimately and entirely embedded in a matrix.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-31 | 1985-03-02 | 1985-09-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-31 | 1989-03-02 | 1989-09-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-31 | 1993-03-02 | 1993-09-01 | $7700.00 | Window Closed / Lapsed |