US4285846A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Flatted water-reducible coating compositions and method for producing same
Assignee: Cabot Corp
•
Filing: 1980-04-28
•
Granted: 1981-08-25
•
Expires: 2000-04-28
Abstract
Abstract Disclosed herein are flatted water-reducible coating compositions of the varnish, paint or enamel types, which compositions comprise a water-miscible film forming resin, water as the predominant solvent and a particulate finely-divided silica flatting agent. The method of the invention involves the initial production of a mill paste formulation containing the film forming resin followed by a let-down step employing water as the predominant solvent. The silica flatting agent is introduced into the composition as an aqueous dispersion thereof during or after said let-down step.
Inventors
- 👤 John F. Hardy
- 👤 Donald P. Kintz
- 👤 Vaughn W. Taylor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 05:48
CPC Classifications
C; C08; C08K; C08K3/00; C08K3/34; C08K3/36; C08K3/18; C08K3/20; C08K3/22; C09; C09D; C09D167/00; C09D167/08; C09D7/00; C09D7/40; C09D7/42
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
101 words
In a method for preparing a water-reducible coating composition comprising the steps of preparing a mill paste of the coating solids, including a water-miscible film forming resin, and thereafter letting down said mill paste with a predominantly aqueous solvent comprising at least 75 percent by weight of water, the improvement which comprises: flatting the composition by admixing therewith an aqueous dispersion of a finely-divided particulate silica flatting agent during or subsequent to said let-down of said mill paste, the quantity of said silica flatting agent so admixed being between about 0.25 and about 5 percent by weight of the total composition.
Claim 2
Dependent Claim
101 words
In a method for preparing a water-reducible coating composition comprising the steps of preparing a mill paste of the coating solids, including a water-miscible film forming resin, and thereafter letting down said mill paste with a predominantly aqueous solvent comprising at least 75 percent by weight of water, the improvement which comprises: flatting the composition by admixing therewith an aqueous dispersion of a finely-divided particulate silica flatting agent during or subsequent to said let-down of said mill paste, the quantity of said silica flatting agent so admixed being between about 0.25 and about 5 percent by weight of the total composition.
Claim 3
Dependent Claim
14 words
The method of claim 1 wherein said silica flatting agent is a pyrogenic silica.
Claim 4
Dependent Claim
20 words
The method of claim 2 wherein said pyrogenic silica is produced by vapor phase flame hydrolysis of silicon halide feedstock.
Claim 5
Dependent Claim
33 words
The method of claim 3 wherein the quantity of pyrogenic silica flatting agent employed is sufficient to provide a concentration thereof of from 0.3 to 2 percent by weight of the total composition.
Claim 6
Dependent Claim
30 words
The method of claim 1 wherein said aqueous dispersion of finely-divided particulate silica flatting agent is prepared by intensive mixing of said silica flatting agent with a volume of water.
Claim 7
Dependent Claim
23 words
The method of claim 1 wherein, in addition, there is incorporated into the water-reducible coating composition a minor amount of a nonionic surfactant.
Claim 8
Dependent Claim
28 words
The method of claim 1 wherein the amount of said nonionic surfactant is between about 10 and about 30% of the dry weight of the silica flatting agent.
Claim 9
Dependent Claim
107 words
A flatted water-reducible coating composition comprising a water-miscible film forming resin, water as the predominant solvent therefor and finely-divided particulate silica flatting agent, said composition having been prepared by forming a mill paste of the composition solids, including said water-miscible film forming resin, thereafter letting down said mill paste with an aqueous solvent comprising at least 75% by weight water and during said let-down, or later, admixing said composition with an aqueous dispersion of said silica flatting agent, the quantity of said silica flatting agent so admixed being sufficient to provide a concentration thereof of between about 0.25 and about 5% by weight of the total composition.
Claim 10
Dependent Claim
107 words
A flatted water-reducible coating composition comprising a water-miscible film forming resin, water as the predominant solvent therefor and finely-divided particulate silica flatting agent, said composition having been prepared by forming a mill paste of the composition solids, including said water-miscible film forming resin, thereafter letting down said mill paste with an aqueous solvent comprising at least 75% by weight water and during said let-down, or later, admixing said composition with an aqueous dispersion of said silica flatting agent, the quantity of said silica flatting agent so admixed being sufficient to provide a concentration thereof of between about 0.25 and about 5% by weight of the total composition.
Claim 11
Dependent Claim
15 words
The flatted composition of claim 8 in the nature of a pigmented paint or enamel.
Claim 12
Dependent Claim
13 words
The flatted composition of claim 8 in the nature of an unpigmented varnish.
Claim 13
Dependent Claim
15 words
The flatted composition of claim 8 wherein said silica flatting agent is a pyrogenic silica.
Claim 14
Dependent Claim
21 words
The flatted composition of claim 11 wherein said pyrogenic silica is produced by vapor phase flame hydrolysis of silicon halide feedstock.
Claim 15
Dependent Claim
29 words
The flatted composition of claim 11 wherein said pyrogenic silica flatting agent is present in the amount of between 0.3 to 2 percent by weight of the total composition.
Claim 16
Dependent Claim
16 words
The flatted composition of claim 8 comprising, in addition, a minor amount of a nonionic surfactant.
Claim 17
Dependent Claim
29 words
The flatted composition of claim 8 wherein the amount of said nonionic surfactant is between about 10 and about 30% of the dry weight of said silica flatting agent.
References Cited (Backward Citations)
US2598066A
Cited
US2625492A
Cited
US3354084A
Cited
US4001379A
Cited
US3737402A
Cited
US4051094A
Cited
US4095994A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-24 | 1985-02-23 | 1985-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-24 | 1989-02-23 | 1989-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-24 | 1993-02-23 | 1993-08-25 | $7700.00 | Window Closed / Lapsed |