Production of a porous aluminum matrix for the negative electrode of a galvanic lithium aluminum metal sulfide element
Assignee: Battelle-Institut
•
Filing: 1979-06-04
•
Granted: 1981-08-25
•
Expires: 1999-06-04
Abstract
Abstract Process for the production of a porous aluminum matrix for the negative electrode of a galvanic cell, in the charged state, having lithium aluminum and metal sulfide elements (or electrodes). Aluminum powder is thoroughly mixed, e.g., by grinding, with a fine salt, which is soluble in water and which serves as an expanding agent. Coarser particles of the same expanding agent (about 100 to 500 μm in size) are then added. The matrix is finally completed by hot pressing at a temperature of 150° to 300° C. and a pressure of at least 500 bar and by the expanding agent being subsequently dissolved out of the matrix using water.
Inventors
- 👤 Reinhard Knodler
- 👤 Gotthold Bohme
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 18:09
CPC Classifications
H; H01; H01M; H01M10/00; H01M10/36; H01M10/39; H01M10/399; H01M4/00; H01M4/02; H01M4/64; H01M4/70; H01M4/80; Y; Y02; Y02E; Y02E60/00; Y02E60/10; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12479
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
144 words
Process for the production of a porous aluminum matrix for the negative electrode of a galvanic cell, in the unchanged state, having aluminum and metal lithium sulfide elements or electrodes, which comprises thoroughly mixing aluminum powder with a salt, which is soluble in water and which serves as an expanding agent, the grain size of the mixture of aluminum powder and fine expanding agent being less than or equal to 50 μm, then adding coarser particles having a particle size of about 100 to 500 μm of the expanding agent to the mixture of aluminum powder and fine salt, hot pressing the resultant mixture at a temperature of 150° to 300° C. and a pressure of at least 500 bar, an aluminum matrix forming, and dissolving the expanding agent out of the resultant aluminum matrix with water, whereby the porous aluminum matrix is formed.
Claim 2
Dependent Claim
144 words
Process for the production of a porous aluminum matrix for the negative electrode of a galvanic cell, in the unchanged state, having aluminum and metal lithium sulfide elements or electrodes, which comprises thoroughly mixing aluminum powder with a salt, which is soluble in water and which serves as an expanding agent, the grain size of the mixture of aluminum powder and fine expanding agent being less than or equal to 50 μm, then adding coarser particles having a particle size of about 100 to 500 μm of the expanding agent to the mixture of aluminum powder and fine salt, hot pressing the resultant mixture at a temperature of 150° to 300° C. and a pressure of at least 500 bar, an aluminum matrix forming, and dissolving the expanding agent out of the resultant aluminum matrix with water, whereby the porous aluminum matrix is formed.
Claim 3
Dependent Claim
20 words
Process as claimed in claim 1 wherein NaCl or KCl powder is used as the expanding agent and fine salt.
Claim 4
Dependent Claim
29 words
Process as claimed in claim 2 wherein the ratio of the weight of the fine expanding agent to that of the coarse expanding agent is between 1:2 and 2:1.
Claim 5
Dependent Claim
35 words
Process as claimed in claim 3 wherein the total powder mixture, including the coarse portion of the expanding agent, is hot pressed at a temperature of 200° C. and a pressure of 1 k bar.
Claim 6
Dependent Claim
29 words
Process as claimed in claim 1 wherein the ratio of the weight of the fine expanding agent to that of the coarse expanding agent is between 1:2 and 2:1.
Claim 7
Dependent Claim
35 words
Process as claimed in claim 1 wherein the total powder mixture, including the coarse portion of the expanding agent, is hot pressed at a temperature of 200° C. and a pressure of 1 k bar.
Claim 8
Dependent Claim
22 words
Process as claimed in claim 1 wherein the thorough mixing is achieved by grinding together the aluminum powder and the fine salt.
References Cited (Backward Citations)
US3887396A
Cited
US3957532A
Cited
US3947291A
Cited
US3933520A
Cited
US4143217A
Cited
US4144383A
Cited
US4158720A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-24 | 1985-02-23 | 1985-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-24 | 1989-02-23 | 1989-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-24 | 1993-02-23 | 1993-08-25 | $7700.00 | Window Closed / Lapsed |