Magnetic recording medium and method of manufacturing the same
Assignee: TDK Corp
•
Filing: 1979-03-13
•
Granted: 1981-08-18
•
Expires: 1999-03-13
Abstract
Abstract A magnetic recording medium, consisting of a base coated with a magnetic coating material, contains finely divided particles of at least either nickel or copper uniformly dispersed in the magnetic coating, in the form of primary particles obtained by pulverization of the skeletal structure of a mother salt or of an aggregated structure. In a method of manufacturing the medium, an antistatic additive, prepared by pulverizing and dispersing at least either Ni powder or Cu powder which retains the skeletal structure of a mother salt or having an aggregated structure, in the presence of a polymeric material, is mixed in the magnetic coating material.
Inventors
- 👤 Yuichi Kubota
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 10:25
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/708; Y; Y10; Y10T; Y10T428/00; Y10T428/25; Y10T428/256; Y10T428/31504; Y10T428/31511; Y10T428/31529; Y10T428/31678; Y10T428/31692; Y10T428/31696; Y10T428/31699
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
101 words
A method of manufacturing a magnetic recording medium by applying a magnetic coating material containing a magnetic powder and a binder on a base, characterized in that an antistatic additive, prepared by pulverizing and dispersing at least either nickel powder or copper powder which has the skeletal structure of a mother salt or having an aggregated structure, in the presence of a polymeric material, said pulverizing being effected by the exertion of a shearing force of a sufficient magnitude such that the skeletal structure is no longer retained or the aggregated structure is disintegrated, is mixed in said magnetic coating material.
Claim 2
Independent Claim
101 words
A method of manufacturing a magnetic recording medium by applying a magnetic coating material containing a magnetic powder and a binder on a base, characterized in that an antistatic additive, prepared by pulverizing and dispersing at least either nickel powder or copper powder which has the skeletal structure of a mother salt or having an aggregated structure, in the presence of a polymeric material, said pulverizing being effected by the exertion of a shearing force of a sufficient magnitude such that the skeletal structure is no longer retained or the aggregated structure is disintegrated, is mixed in said magnetic coating material.
Claim 3
Dependent Claim
25 words
A method according to claim 1, in which said antistatic additive is dissolved in a solvent and is added in the form of a lacquer.
Claim 4
Dependent Claim
25 words
A method according to claim 1, in which said metal powder accounts for from 50 to 95% of the total weight of said antistatic additive.
Claim 5
Dependent Claim
56 words
A method according to claim 1, in which the starting powder for the preparation of said antistatic additive is formed by hydrogen reduction of an organic nickel salt, thermal decomposition of nickel carbonyl gas, recovery of a dendritic powder deposited on plates by electrolysis, shotting, spraying, or electrochemical precipitation from a Ni or Cu salt solution.
Claim 6
Dependent Claim
27 words
A method according to claim 1, in which the pulverizing and dispersing action is given by a grinding and dispersing apparatus capable of exerting strong shearing forces.
Claim 7
Dependent Claim
35 words
A method according to claim 5, in which said grinding and dispersing apparatus is selected from among a hot two-roll mill, pressure kneader, Banbury mixer, and the combination of a kneader and a three-roll mill.
Claim 8
Dependent Claim
11 words
A magnetic recording medium made by the process of claim 6.
Claim 9
Dependent Claim
18 words
A magnetic recording medium according to claim 7 wherein said magnetic powder comprises particles of a magnetic oxide.
Claim 10
Dependent Claim
20 words
A magnetic recording medium according to claim 7 wherein said polymeric material is of the type used for paint coating.
Claim 11
Dependent Claim
34 words
A magnetic recording medium according to claim 7 wherein said nickel powder or copper powder is in the form of finely divided particles having particle diameters predominantly in the range of about 500-1000 A.
Claim 12
Dependent Claim
17 words
A magnetic recording medium made according to the process of claims 2, 3, 4, 5 or 6.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-17 | 1985-02-16 | 1985-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-17 | 1989-02-16 | 1989-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-17 | 1993-02-16 | 1993-08-18 | $7700.00 | Window Closed / Lapsed |