BN Bonded BN fiber article and method of manufacture
Assignee: Stemcor Corp
•
Filing: 1979-03-20
•
Granted: 1981-08-18
•
Expires: 1999-03-20
Abstract
Abstract A boron nitride bonded boron nitride fiber article and the method for its manufacture which comprises forming a shaped article with a composition comprising a bonding compound selected from boron oxide and boric acid and a structural fiber selected from the group consisting of boron oxide, boron nitride and partially nitrided boron oxide fibers, heating the composition in an anhydrous gas to a temperature above the melting point of the compound and nitriding the resulting article in ammonia gas.
Inventors
- 👤 Robert S. Hamilton
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 21:13
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/583; C04B35/71; C04B35/78; C04B35/80; H; H01; H01M; H01M50/00; H01M50/40; H01M50/409; H01M50/431; H01M50/434; H01M50/44; H01M50/489; H01M2300/00; H01M2300/0017; H01M2300/0048; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 31
Claim 1
Independent Claim
216 words
A method for manufacturing a boron nitride article comprising: (a) blending from about 0.5 to about 40 weight percent of a bonding compound selected from the group consisting of boron oxide, boric acid and mixtures thereof with from about 60 to about 99.5 weight percent of structural fiber manufactured from boron oxide, partially nitrided boron oxide, boron nitride or mixtures of such fibers in an anhydrous fluid vehicle in which the bonding compound and the structural fiber are insoluble, the bonding compound having a lower melting temperature than the melting or decomposition temperature of the structural fiber; (b) forming a shaped article with the resulting blend and removing sufficient fluid vehicle to permit intimate contact of the structural fiber with the bonding compound; (c) heating the shaped article in an anhydrous gas selected from the group consisting of inert gases, nitrogen, ammonia, carbon dioxide and mixtures thereof to a temperature above the melting temperature of the bonding compound and below the melting or decomposition temperature of the structural fiber for a time sufficient to melt at least some of the bonding compound to the structural fibers; and (d) heating the shaped article in an ammonia atmosphere to a sufficient temperature and for a sufficient time to convert the bonding compound and structural fibers to boron nitride.
Claim 2
Independent Claim
216 words
A method for manufacturing a boron nitride article comprising: (a) blending from about 0.5 to about 40 weight percent of a bonding compound selected from the group consisting of boron oxide, boric acid and mixtures thereof with from about 60 to about 99.5 weight percent of structural fiber manufactured from boron oxide, partially nitrided boron oxide, boron nitride or mixtures of such fibers in an anhydrous fluid vehicle in which the bonding compound and the structural fiber are insoluble, the bonding compound having a lower melting temperature than the melting or decomposition temperature of the structural fiber; (b) forming a shaped article with the resulting blend and removing sufficient fluid vehicle to permit intimate contact of the structural fiber with the bonding compound; (c) heating the shaped article in an anhydrous gas selected from the group consisting of inert gases, nitrogen, ammonia, carbon dioxide and mixtures thereof to a temperature above the melting temperature of the bonding compound and below the melting or decomposition temperature of the structural fiber for a time sufficient to melt at least some of the bonding compound to the structural fibers; and (d) heating the shaped article in an ammonia atmosphere to a sufficient temperature and for a sufficient time to convert the bonding compound and structural fibers to boron nitride.
Claim 3
Dependent Claim
30 words
The method claimed in claim 1 wherein the fluid vehicle is a liquid selected from the group consisting of hydrocarbons and mono hydroxy alcohols having three or more carbon atoms.
Claim 4
Dependent Claim
37 words
The method of claim 1 wherein from about 0.5 kilograms per square centimeter to about 2.5 kilograms per square centimeter of absolute pressure is applied to said shaped article during said heating to melt the bonding compound.
Claim 5
Dependent Claim
14 words
The method of claim 1 wherein the shaped article is a porous fiber mat.
Claim 6
Dependent Claim
17 words
The method claimed in claim 2 wherein the fluid vehicle is kerosene which is removed by evaporation.
Claim 7
Dependent Claim
17 words
The method of claim 1 wherein the structural fiber comprises boron nitride or partially nitrided boron oxide.
Claim 8
Dependent Claim
15 words
The method of claim 6 wherein the bonding compound is boron oxide in particulate form.
Claim 9
Dependent Claim
40 words
The method claimed in claim 6 wherein the heating to melt the boron oxide bonding compound and the heating to convert the boron oxide bonding compound and the structural fibers to boron nitride are done sequentially in an ammonia atmosphere.
Claim 10
Dependent Claim
13 words
The method of claim 6 wherein the shaped article is a fiber mat.
Claim 11
Dependent Claim
32 words
The method of claim 6 wherein from about 0.5 kilograms per square centimeter to about 2.5 kilograms per square centimeter of absolute pressure is applied to said shaped article during said heating.
Claim 12
Dependent Claim
26 words
The method of claim 6 wherein the fluid vehicle is selected from the group consisting of hydrocarbons and monohydroxy alcohols having three or more carbon atoms.
Claim 13
Dependent Claim
36 words
The method of claim 1 wherein from about 5 to about 20 weight percent of boron oxide fiber bonding compound is blended with from about 80 to about 95 weight percent of boron nitride structural fiber.
Claim 14
Dependent Claim
15 words
The method of claim 12 wherein the boron oxide bonding compound is in particulate form.
Claim 15
Dependent Claim
35 words
The method claimed of claim 12 wherein from about 80 to about 90 weight percent boron nitride structural fiber is blended with from about 10 to about 20 weight percent of boron oxide bonding compound.
Claim 16
Dependent Claim
29 words
The method claimed in claim 12 wherein the fluid vehicle is a liquid selected from the group consisting of hydrocarbons and monohydroxy alcohols having three or more carbon atoms.
Claim 17
Dependent Claim
21 words
The method claimed in claim 15 wherein the structural fibers are blended with boron oxide bonding compound in the fluid vehicle.
Claim 18
Dependent Claim
27 words
The method claimed in claim 12 wherein the structural fibers and boron oxide bonding compound are blended by blowing them randomly into a container with anhydrous gas.
Claim 19
Dependent Claim
34 words
The method claimed in claim 12 wherein the structural fibers and boron oxide bonding compound are blended by mixing them in a fluidized bed in which the fluid vehicle is either gas or liquid.
Claim 20
Dependent Claim
39 words
The method of claim 12 wherein said shaped article is pressed between plates at from about 0.5 kilograms per square centimeter to about 2.5 kilograms per square centimeter of gauge pressure during said heating to melt the bonding compound.
Claim 21
Dependent Claim
13 words
The method of claim 12 wherein the shaped article is a fiber mat.
Claim 22
Dependent Claim
44 words
The method of claim 12 wherein said article is heated to between about 460° C. and about 1400° C. for from about three minutes to about six hours to melt the boron oxide bonding compound and said gas is an inert gas or nitrogen.
Claim 23
Dependent Claim
37 words
The method of claim 12 wherein the sufficient temperature to convert boron oxide to boron nitride is from about 200° to about 900° C. and the sufficient conversion time is from about 2 to about 18 hours.
Claim 24
Dependent Claim
81 words
An article having sufficient flexibility that samples 3 mm thick show no apparent cracking or deterioration when bent around a 1.5 cm diameter rod; said article comprising boron nitride fibers bonded together with from about 5 to 30 percent by weight of article of discrete boron nitride bonds, said discrete bonds between crossed fibers having an average maximum dimension of up to ten times the diameter of the boron nitride fiber and essentially all of said bonds having smooth non-porous surfaces.
Claim 25
Dependent Claim
81 words
An article having sufficient flexibility that samples 3 mm thick show no apparent cracking or deterioration when bent around a 1.5 cm diameter rod; said article comprising boron nitride fibers bonded together with from about 5 to 30 percent by weight of article of discrete boron nitride bonds, said discrete bonds between crossed fibers having an average maximum dimension of up to ten times the diameter of the boron nitride fiber and essentially all of said bonds having smooth non-porous surfaces.
Claim 26
Dependent Claim
57 words
An article having sufficient flexibility that samples 3 mm thick show no apparent cracking or deterioration when bent around a 1.5 cm diameter rod; said article comprising boron nitride fibers bonded together with from about 25 to about 70 percent by weight of article of boron nitride bonds, essentially all of said bonds having smooth non-porous surfaces.
Claim 27
Dependent Claim
57 words
An article having sufficient flexibility that samples 3 mm thick show no apparent cracking or deterioration when bent around a 1.5 cm diameter rod; said article comprising boron nitride fibers bonded together with from about 25 to about 70 percent by weight of article of boron nitride bonds, essentially all of said bonds having smooth non-porous surfaces.
Claim 28
Dependent Claim
12 words
The article of claim 23 wherein the article is a fiber mat.
Claim 29
Dependent Claim
18 words
An electric cell incorporating molten lithium chloride and the fiber mat of claim 25 as a cell separator.
Claim 30
Dependent Claim
12 words
The article of claim 24 wherein the article is a fiber mat.
Claim 31
Dependent Claim
18 words
An electric cell incorporating molten lithium chloride and the fiber mat of claim 27 as a cell separator.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-17 | 1985-02-16 | 1985-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-17 | 1989-02-16 | 1989-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-17 | 1993-02-16 | 1993-08-18 | $7700.00 | Window Closed / Lapsed |