Patterned chemical etching of high temperature resistant metals
Assignee: ANADITE Inc A NV CORP
•
Filing: 1979-07-27
•
Granted: 1981-08-18
•
Expires: 1999-07-27
Abstract
Abstract An improved process for providing a design within a metallic surface by composite photoresist techniques in which the composite photoresist has sufficient chemical resistance to permit etching the design, with an aqua-regia or aqua-regia fluoride system in the most commercially available corrosion resistant and high temperature resistant alloys and metals. The process consists in applying a first coating of epoxy resin or other resin to the metal substrate or surface to be etched; subsequently applying a conventional photoresist material upon the cured resin; applying a photomask to said photoresist in a desired pattern; exposing the photomask to a light source to actuate the photoresist; chemically removing the photoresist in the non-activated areas; subsequently removing the epoxy or other resin underlying the non-activated areas preferably by means of a concentrated solution of sulfuric acid, which dissolves the resin but does not attack the photoresist and thereby exposing the metallic substrate in the same pattern as that developed upon the photoresist, and subsequently etching the metal by means of a mixture of acids capable of reacting with the metallic surface under the reaction conditions chosen, but not with the resin layer.
Inventors
- 👤 Llewelyn Stearns
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 13:02
CPC Classifications
C; C23; C23F; C23F1/00; C23F1/02; H; H05; H05K; H05K3/00; H05K3/02; H05K3/06; H05K3/061; H05K3/44
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
242 words
A process for the chemical milling, to a predetermined pattern, of high temperature resistant metal material including those selected from the group consisting of high temperature resistant alloys including combination alloys of two or more of chromium, nickel, molybdenum, cobalt, iron, Niobium, Titanium and Tungsten, and refractory elements which comprises: coating the exposed surfaces of said metal material with a polymerizable resin composition; curing said polymerizable resin composition to form a coated metal material that is coated with a layer of cured resin material; applying a coating of light sensitive photoresist composition upon said coated metal material; exposing said light-sensitive photoresist composition to a light source in said predetermined pattern; chemically removing only said photoresist composition in accordance with said predetermined pattern to thereby expose cured resin material in those same areas where said photoresist material has been removed; chemically removing only said exposed cured resin material without removal of metal or photoresist material to thereby expose metal material in those same areas where said photoresist and resin materials have been previously removed; chemically etching said exposed metal material in the said predetermined pattern with an etchant selected from the group consisting predominately of aqua regia and aqua regia plus hydrofluoric acid at temperatures of between about 140° F. to 180° F. but without removal of cured resin material by said etchant; and stripping said photoresist composition and cured resin material to completely expose said metal material etched in said predetermined pattern.
Claim 2
Dependent Claim
242 words
A process for the chemical milling, to a predetermined pattern, of high temperature resistant metal material including those selected from the group consisting of high temperature resistant alloys including combination alloys of two or more of chromium, nickel, molybdenum, cobalt, iron, Niobium, Titanium and Tungsten, and refractory elements which comprises: coating the exposed surfaces of said metal material with a polymerizable resin composition; curing said polymerizable resin composition to form a coated metal material that is coated with a layer of cured resin material; applying a coating of light sensitive photoresist composition upon said coated metal material; exposing said light-sensitive photoresist composition to a light source in said predetermined pattern; chemically removing only said photoresist composition in accordance with said predetermined pattern to thereby expose cured resin material in those same areas where said photoresist material has been removed; chemically removing only said exposed cured resin material without removal of metal or photoresist material to thereby expose metal material in those same areas where said photoresist and resin materials have been previously removed; chemically etching said exposed metal material in the said predetermined pattern with an etchant selected from the group consisting predominately of aqua regia and aqua regia plus hydrofluoric acid at temperatures of between about 140° F. to 180° F. but without removal of cured resin material by said etchant; and stripping said photoresist composition and cured resin material to completely expose said metal material etched in said predetermined pattern.
Claim 3
Dependent Claim
36 words
The process of claim 1 wherein said photoresist composition is an organic polymerizable system containing solvent and said solvent is removed and said system cured prior to exposure of said photoresist composition to a light source.
Claim 4
Dependent Claim
27 words
The process of claim 1 wherein said polymerizable resin composition is selected from the group consisting of epoxy resin compositions, polyester resin compositions and polyurethane resin compositions.
Claim 5
Dependent Claim
20 words
The process of claim 1 wherein said polymerizable resin composition has a thickness of between about 1.5 and 10 milliinches.
Claim 6
Dependent Claim
25 words
The process of claim 1 wherein said light-sensitive photoresist composition is an organic resin composition polymerizable in the presence of an ultraviolet source of light.
Claim 7
Dependent Claim
55 words
The process of claim 1 wherein said exposed cured resin material is chemically removed by reaction with sulphuric acid having a concentration of between about 83% and 98%, for a period of between 30 seconds and five (5) minutes depending upon the concentration, and at a temperature of between about 60° F. and 120° F.
Claim 8
Dependent Claim
70 words
The process of claim 1 wherein said exposed metal material in the said predetermined pattern, is chemically etched at a temperature of between 140° F. and 160° F. without removing any material of said cured resin layer, by means of an etchant having the following composition: 32° Baume Muriatic Acid: 9 Gal. 40° Baume Nitric Acid: 1 Gal. 70° Hydrofluoric Acid: 0.2 Gal. Anhydrous FeCl 3 to specific gravity: 1.26.
Claim 9
Dependent Claim
22 words
The process of claim 1 wherein said photoresist composition is polymerizable and is first cured prior to exposure to a light source.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-17 | 1985-02-16 | 1985-08-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-17 | 1989-02-16 | 1989-08-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-17 | 1993-02-16 | 1993-08-18 | $7700.00 | Window Closed / Lapsed |