Support, catalyst and process for polymerizing olefins
Assignee: Dow Chemical Co
•
Filing: 1980-06-17
•
Granted: 1981-08-11
•
Expires: 2000-06-17
Abstract
Abstract Olefins are polymerized in the presence of a catalyst which is prepared by the controlled reaction of an aliphatic alcohol such as n-propyl alcohol and a mixture of an alkyl magnesium compound such as n-butyl, sec-butyl magnesium and a silicon tetrahalide such as SiCl 4 . After washing the precipitate several times with a hydrocarbon such as hexane, it is suspended in a hydrocarbon such as hexane and a titanium compound such as TiCl 4 is added after which a suitable reducing agent such as diethyl aluminum chloride is added. The thus formed solid catalyst is washed several times with a hydrocarbon solvent such as hexane.
Inventors
- 👤 Ronald L. Gibbs
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 18:50
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
236 words
A process for the polymerization of one or more alpha olefins under conditions characteristic of Ziegler polymerization which process comprises employing as a polymerization catalyst a composition resulting from the addition of a reducing agent to a mixture of a support suspended in an inert liquid hydrocarbon and a transition metal compound of Groups 4b, 5b, 6b, 7b, or 8 of Mendeleev's Periodic Table under conditions so as to provide a catalytically active solid product and in such proportions that the magnesium:transition metal atomic ratio is from about 0.1:1 to about 30:1 followed by washing the resultant solid catalyst product with an inert liquid hydrocarbon wherein said support comprises the reaction product of (1) a mixture of an organomagnesium compound represented by the formula MgR 2 and a silcon halide represented by the formula R' 4-n SiX n , said mixture being in a non-polar solvent, with (2) an alcohol represented by the formula R"OH; wherein the organomagnesium compound is or can be rendered hydrocarbon soluble and wherein each R, R' and R" is independently a hydrocarbyl group having from 1 to about 20 carbon atoms, X is C1, Br or I, n has a value of from 1 to 4 and wherein the molar ratio of R"OH:MgR 2 is at least 2:1 and the molar ratio of R"OH:R' 4-n SiX n is sufficient so as to provide at least one X group per OH group.
Claim 2
Dependent Claim
236 words
A process for the polymerization of one or more alpha olefins under conditions characteristic of Ziegler polymerization which process comprises employing as a polymerization catalyst a composition resulting from the addition of a reducing agent to a mixture of a support suspended in an inert liquid hydrocarbon and a transition metal compound of Groups 4b, 5b, 6b, 7b, or 8 of Mendeleev's Periodic Table under conditions so as to provide a catalytically active solid product and in such proportions that the magnesium:transition metal atomic ratio is from about 0.1:1 to about 30:1 followed by washing the resultant solid catalyst product with an inert liquid hydrocarbon wherein said support comprises the reaction product of (1) a mixture of an organomagnesium compound represented by the formula MgR 2 and a silcon halide represented by the formula R' 4-n SiX n , said mixture being in a non-polar solvent, with (2) an alcohol represented by the formula R"OH; wherein the organomagnesium compound is or can be rendered hydrocarbon soluble and wherein each R, R' and R" is independently a hydrocarbyl group having from 1 to about 20 carbon atoms, X is C1, Br or I, n has a value of from 1 to 4 and wherein the molar ratio of R"OH:MgR 2 is at least 2:1 and the molar ratio of R"OH:R' 4-n SiX n is sufficient so as to provide at least one X group per OH group.
Claim 3
Dependent Claim
76 words
The process of claim 1 wherein R has from about 2 to about 8 carbon atoms, each R' and R" independently has from about 1 to about 6 carbon atoms, X is chlorine or bromine; wherein the ratio of R"OH:R' 4-n SiX n is sufficient so as to provide from 2 to about 3 X groups per OH group; and wherein said non-polar solvent is a hydrocarbon having from about 5 to about 10 carbon atoms.
Claim 4
Dependent Claim
105 words
The process of claim 2, wherein the organomagnesium compound is selected from the group consisting of dibutyl magnesium, butyl isobutyl magnesium, dihexyl magnesium, ethyl hexyl magnesium, dioctyl magnesium and mixtures thereof: the alcohol is selected from the group consisting of ethanol, n-propanol, isopropanol, n-butanol, sec-butanol and mixtures thereof; the silicon halide is selected from the group consisting of SiCl 4 , CH 3 SiCl 3 , (CH 3 ) 2 SiCl 2 , (CH 3 ) 3 SiCl, SiBr 4 , (Et)SiCl 3 and mixtures thereof; the transition metal compound is that of a metal selected from Groups 4b or 5b of the Periodic Table.
Claim 5
Dependent Claim
25 words
The process of claim 3 wherein the transition metal is titanium or vanadium and the magnesium:transition metal ratio is from about 0.2:1 to about 3:1.
Claim 6
Dependent Claim
56 words
The process of claim 4 which additionally employs a metallic compound as a cocatalyst which is a halide, hydride or totally alkylated derivative of the metal of Groups 1a, 2a, 2b, 3a or 4a of the Periodic Table and is present in quantities such that the metal:transition metal ratio is from about 1:1 to about 200:1.
Claim 7
Dependent Claim
12 words
The process of claim 5 wherein said cocatalyst is an aluminum compound.
Claim 8
Dependent Claim
18 words
The process of claim 6 wherein the transition metal compound is titanium tetrachloride and the cocatalyst is triisobutylaluminum.
Claim 9
Dependent Claim
31 words
The process of claims 1, 2, 3, 4, 5, 6 or 7 wherein the α-olefin is ethylene or a mixture of ethylene and at least one other polymerizable ethylenically unsaturated compound.
Claim 10
Dependent Claim
33 words
The process of claims 1, 2, 3, 4, 5, 6 or 7 wherein component (2) is added in a controlled manner to component (1) at a temperature of about 100° C. or less.
Claim 11
Dependent Claim
17 words
The process of claim 9 wherein the temperature is from about 0° C. to about 70° C.
Claim 12
Dependent Claim
16 words
The process of claim 9 wherein component (2) is said alcohol dissolved in a non-polar solvent.
Claim 13
Dependent Claim
59 words
The process of claim 8 wherein component (1) is added in a controlled manner to component (2) at a temperature of about 100° C. or less and the reducing agent is added at a temperature below about 100° C., such temperature during addition of the reducing agent being below the boiling point of the diluent at the pressure employed.
Claim 14
Dependent Claim
39 words
The process of claim 12 wherein component (1) is added at a temperature of from about 0° C. to about 70° C. and the reducing agent is added in a controlled manner at a temperature below about 70° C.
Claim 15
Dependent Claim
14 words
The process of claim 12 wherein said alcohol is dissolved in a non-polar solvent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-10 | 1985-02-09 | 1985-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-10 | 1989-02-09 | 1989-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-10 | 1993-02-09 | 1993-08-11 | $7700.00 | Window Closed / Lapsed |