Siloxane-modified epoxy resin composition
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1980-03-03
•
Granted: 1981-08-11
•
Expires: 2000-03-03
Abstract
Abstract Compositions containing siloxane-modified epoxy resins, alkoxy functional organopolysiloxane and conventional epoxy curing agents are described which have improved resistance to degradation of electrical properties by boiling water and moisture. The compositions consist essentially of (A) siloxane-modified epoxy resin, (B) alkoxy functional organopolysiloxane such as polymethylmethoxysiloxane and (C) curing agents such as carboxylic acid anhydrides.
Inventors
- 👤 Ryuzo Mikami
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 01:04
CPC Classifications
C; C08; C08L; C08L63/00; C08G; C08G59/00; C08G59/18; C08G59/40; C08G59/4007; C08G59/4085; C08K; C08K5/00; C08K5/04; C08K5/09; C08L83/00; C08L83/04; C08L83/10
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
165 words
A siloxane-modified epoxy resin composition consisting essentially of (A) 100 parts by weight of a siloxane-modified epoxy resin prepared by reacting (1) 5 to 70 parts by weight of an alkylphenylpolysiloxane of the general unit formula ##EQU4## wherein each R is an alkyl or a phenyl radical such that the ratio of alkyl radicals to phenyl radicals in the alkylphenylpolysiloxane is 0.3 to 3.0, X is an alkoxy radical or a hydroxyl radical, a is 0.9 to 1.8, and b is 0.01 to 2 with (2) 95 to 30 parts by weight of an epoxy resin having at least two epoxy groups per molecule, (B) 0.01 to 30 parts by weight of an alkoxy group containing organopolysiloxane of the general unit formula ##EQU5## wherein R' is selected from the group consisting of monovalent hydrocarbon radicals and halogen substituted monovalent hydrocarbon radicals, R 2 is an alkyl radical, c is 0.9 to 1.8 and d is 0.01 to 2 and (C) a curing agent for (A).
Claim 2
Dependent Claim
165 words
A siloxane-modified epoxy resin composition consisting essentially of (A) 100 parts by weight of a siloxane-modified epoxy resin prepared by reacting (1) 5 to 70 parts by weight of an alkylphenylpolysiloxane of the general unit formula ##EQU4## wherein each R is an alkyl or a phenyl radical such that the ratio of alkyl radicals to phenyl radicals in the alkylphenylpolysiloxane is 0.3 to 3.0, X is an alkoxy radical or a hydroxyl radical, a is 0.9 to 1.8, and b is 0.01 to 2 with (2) 95 to 30 parts by weight of an epoxy resin having at least two epoxy groups per molecule, (B) 0.01 to 30 parts by weight of an alkoxy group containing organopolysiloxane of the general unit formula ##EQU5## wherein R' is selected from the group consisting of monovalent hydrocarbon radicals and halogen substituted monovalent hydrocarbon radicals, R 2 is an alkyl radical, c is 0.9 to 1.8 and d is 0.01 to 2 and (C) a curing agent for (A).
Claim 3
Dependent Claim
30 words
A siloxane-modified epoxy resin composition according to claim 1 in which epoxy resin (2) is a polydiglycidyl ether of bisphenol A resin with a molecular weight of 340 to 6000.
Claim 4
Dependent Claim
40 words
A siloxane-modified epoxy resin composition according to claim 1 in which siloxane-modified epoxy resin (A) is prepared by reacting 15 to 50 parts by weight (1) with 85 to 50 parts by weight (2) at about 120° to 210° C.
Claim 5
Dependent Claim
18 words
A siloxane-modified epoxy resin composition according to claim 1 containing 0.3 to 20 parts by weight of (B).
Claim 6
Dependent Claim
25 words
A siloxane-modified epoxy resin composition according to claim 4 in which (B) is a polymethylmethoxysiloxane containing an average of 1 methoxy radical per silicon atom.
Claim 7
Dependent Claim
29 words
A siloxane-modified epoxy resin composition according to claim 5 in which curing agent (C) is selected from the group consisting of polyhydric carboxylic acids and polyhydric carboxylic acid anhydrides.
Claim 8
Dependent Claim
18 words
A siloxane-modified epoxy resin composition according to claim 6 in which the curing agent (C) is trimellitic anhydride.
Claim 9
Dependent Claim
18 words
A siloxane-modified epoxy resin composition according to claim 6 in which the curing agent (C) is hexahydrophthalic anhydride.
References Cited (Backward Citations)
US3170962A
Cited
US3154597A
Cited
US3055858A
Cited
US3088847A
Cited
US3358064A
Cited
US3560589A
Cited
US3842141A
Cited
US4141926A
Cited
US4122127A
Cited
US4082719A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-10 | 1985-02-09 | 1985-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-10 | 1989-02-09 | 1989-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-10 | 1993-02-09 | 1993-08-11 | $7700.00 | Window Closed / Lapsed |