Plating on plastics by softening with trichloroethylene and methylene chloride bath
Assignee: Sunbeam Products Inc
•
Filing: 1980-04-03
•
Granted: 1981-07-28
•
Expires: 2000-04-03
Abstract
Abstract An article fabricated from a resin (e.g. ABS, polycarbonates, polyethylenes, polyaryl ether, or polypropylene of platable grades) susceptible to softening when contacted with trichloroethylene or a mixture of trichloroethylene and methylene chloride is dipped into an alkaline detergent, rinsed, and immersed in an agitated bath (by volume, 90 parts of trichloroethylene, 9 to 10 parts of ethanol, and 0 to 1 part of methylene chloride--1 part of methylene chloride if the resin is polypropylene) to which copper or nickel has been added as a powder (50 to 150 microns, 200 to 250 grams per liter) whereupon the article is drained, dipped in an agitated bath of similar composition, and dried. Alternatively, the powder may be sprayed onto the article, after the article has been immersed in such a bath. Next, the article may be dipped in dilute nitric acid, rinsed and immersed in a non-catalytic bath for deposition of nickel.
Inventors
- 👤 Raichur S. Narayan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 22:53
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/18; C23C18/20; C23C18/22; C23C18/26; C08; C08J; C08J7/00; C08J7/02; H; H05; H05K; H05K3/00; H05K3/10; H05K3/18; H05K3/181; H05K3/38; H05K3/381
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
158 words
A process for plating a metal on an article fabricated from a resin susceptible to softening of the resin upon contact of the resin with trichloroethylene or with trichloroethylene and methylene chloride, said process comprising the steps of (a) immersing the article in a bath being agitated as the article is immersed therein and consisting essentially of (1) approximately 90 parts of trichloroethylene by volume, (2) approximately from 9 to 10 parts of ethanol by volume, and (3) approximately from 0 to 1 part of methylene chloride by volume, wherein the bath contains approximately 1 part of methylene chloride if the resin is polypropylene, (b) contacting the article with the metal as a powder of particle sizes of approximately from 50 to 150 microns, and (c) dipping the article in a bath being agitated as the article is dipped therein and consisting essentially of trichloroethylene, ethanol, and methylene chloride in proportions used in the bath for step (a).
Claim 2
Dependent Claim
158 words
A process for plating a metal on an article fabricated from a resin susceptible to softening of the resin upon contact of the resin with trichloroethylene or with trichloroethylene and methylene chloride, said process comprising the steps of (a) immersing the article in a bath being agitated as the article is immersed therein and consisting essentially of (1) approximately 90 parts of trichloroethylene by volume, (2) approximately from 9 to 10 parts of ethanol by volume, and (3) approximately from 0 to 1 part of methylene chloride by volume, wherein the bath contains approximately 1 part of methylene chloride if the resin is polypropylene, (b) contacting the article with the metal as a powder of particle sizes of approximately from 50 to 150 microns, and (c) dipping the article in a bath being agitated as the article is dipped therein and consisting essentially of trichloroethylene, ethanol, and methylene chloride in proportions used in the bath for step (a).
Claim 3
Dependent Claim
87 words
The process of claim 1 wherein the powder has been added, in an amount of approximately from 200 to 250 grams per liter of the bath, to the bath for step (a) and wherein the bath for step (a) is agitated for approximately 15 to 25 seconds after the article has been immersed therein, whereupon agitation of the bath for step (a) is discontinued for approximately 5 seconds while the article remains immersed therein, and whereupon the article is removed gradually from the bath for step (a).
Claim 4
Dependent Claim
17 words
The process of claim 2 wherein the bath for step (a) is agitated in a pulsating manner.
Claim 5
Dependent Claim
22 words
The process of claim 2 wherein the article is drained for approximately from 30 to 40 seconds between steps (b) and (c).
Claim 6
Dependent Claim
32 words
The process of claim 2 wherein the article is dried in a current of air at a temperature of approximately from 20° to 40° C. for approximately 60 seconds after step (c).
Claim 7
Dependent Claim
22 words
The process of claim 2 comprising prior steps of dipping the article into an alkaline cleaner and rinsing the article in water.
Claim 8
Dependent Claim
20 words
The process of claim 2 wherein each bath is maintained at a temperature of approximately from 20° to 30° C.
Claim 9
Dependent Claim
12 words
The process of claim 2 wherein the metal is copper or nickel.
Claim 10
Dependent Claim
34 words
The process of any of claims 1 through 8 wherein the resin is selected from the group consisting of epoxy resins, phenylene oxide-based resins, polyacrylics including acrylonitrile-butadiene-styrene copolymers, polyaryl ethers, polypropylene, polystyrene, and polysulfones.
Claim 11
Dependent Claim
107 words
The process of claim 9 comprising later steps of (d) immersing the article for approximately 15 seconds in an aqueous solution of nitric acid in an amount of approximately 10% by volume, (e) rinsing the article in water, and (f) immersing the article for approximately 15 minutes in an aqueous solution of (1) nickel sulfate in an amount of approximately from 50 to 60 grams per liter, (2) ammonium sulfate in an amount of approximately from 50 to 60 grams per liter, and (3) sodium thiosulfate in an amount of approximately from 100 to 120 grams per liter, at a temperature of approximately 20° to 30° C.
Claim 12
Dependent Claim
49 words
The process of claim 1 wherein the bath for step (a) is agitated while the article is immersed therein for approximately from 20 to 30 seconds, whereupon the article is drained, and whereupon the article is sprayed with the powder so as to contact the article with the powder.
Claim 13
Dependent Claim
20 words
The process of claim 11 wherein the bath for step (a) and the bath for step (c) are separate baths.
Claim 14
Dependent Claim
20 words
The process of claim 11 wherein the bath for step (a) and the bath for step (c) are one bath.
Claim 15
Dependent Claim
25 words
The process of claim 11 wherein the article is drained for approximately from 30 to 40 seconds before the article is sprayed with the powder.
Claim 16
Dependent Claim
32 words
The process of claim 11 wherein the article is dried in a current of air at a temperature of approximately from 20° to 40° C. for approximately 60 seconds after step (c).
Claim 17
Dependent Claim
22 words
The process of claim 11 comprising prior steps of dipping the article into an alkaline cleaner and rinsing the article in water.
Claim 18
Dependent Claim
20 words
The process of claim 11 wherein each bath is maintained at a temperature of approximately from 20° to 30° C.
Claim 19
Dependent Claim
12 words
The process of claim 11 wherein the metal is copper or nickel.
Claim 20
Dependent Claim
34 words
The process of any of claims 11 through 18 wherein the resin is selected from the group consisting of epoxy resins, phenylene oxide-based resins, polyacrylics including acrylonitrile-butadiene-styrene copolymers, polyaryl ethers, polypropylene, polystyrene, and polysulfones.
Claim 21
Dependent Claim
107 words
The process of claim 19 comprising later steps of (d) immersing the article for approximately 15 seconds in an aqueous solution of nitric acid in an amount of approximately 10% by volume, (e) rinsing the article in water, and (f) immersing the article for approximately 15 minutes in an aqueous solution of (1) nickel sulfate in an amount of approximately from 50 to 60 grams per liter, (2) ammonium sulfate in an amount of approximately from 50 to 60 grams per liter, and (3) sodium thiosulfate in an amount of approximately from 100 to 120 grams per liter, at a temperature of approximately 20° to 30° C.
References Cited (Backward Citations)
US3466229A
Cited
US3524754A
Cited
US3647512A
Cited
US3650708A
Cited
US3754976A
Cited
US4078097A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-27 | 1985-01-26 | 1985-07-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-27 | 1989-01-26 | 1989-07-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-27 | 1993-01-26 | 1993-07-28 | $7700.00 | Window Closed / Lapsed |