Electrochemical sensor for oxygen concentration determination in gases and method of making the same
Assignee: Robert Bosch GmbH
•
Filing: 1980-03-14
•
Granted: 1981-07-28
•
Expires: 2000-03-14
Abstract
Abstract To decrease the quantity of catalytically active noble metal used in a Cermet (ceramic-metal) electrode, particularly one containing platinum, the electrode has a non-uniform noble metal concentration, with respect to its cross section, so that the outer region thereof consists essentially only of ceramic material, protecting the softer noble metal which is subject to erosion, and permitting a higher concentration of noble metal close to the solid electrolyte body where it is most needed. This type of electrode can be applied, for example, by concurrent spraying of an aqueous suspension of noble metal-and-ceramic from one nozzle, and a suspension of only ceramic from another nozzle, and varying the throughput through the two nozzles, first only spraying the metal-ceramic mixture and then starting the ceramic-only suspension while decreasing the mixture suspension until only ceramic material is sprayed; in accordance with another method, the solid electrolyte body can, for example, be dipped in sequential suspensions or have sequential suspensions applied thereto by dripping-on, painting-on, or the like. The electrode and the solid electrolyte body, for example zirconium dioxide, are then sintered.
Inventors
- 👤 Karl-Hermann Friese
- 👤 Wolf-Dieter Haecker
- 👤 Burkhard Pfeiffer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 14:28
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4077; H; H01; H01M; H01M8/00; H01M8/10; H01M8/12; H01M8/1213; H01M4/00; H01M4/86; H01M4/90; H01M4/9016; H01M4/9025; H01M4/9033; H01M4/9041; H01M4/905; H01M4/9066; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
119 words
Electrochemical sensor for determination of the concentration of oxygen in gases, particularly in gases resulting from combustion processes, such as exhaust gases from internal combustion engines, having an ion conductive solid electrolyte body (10) and an electrode (11) applied to a surface thereof, adapted to be exposed to the gases, said electrode comprising a mixture of a ceramic and a noble metal which catalyzes the thermodynamic equilibrium of the gases with respect to a reference, wherein, in accordance with the invention, the concentration of noble metal in the electrode is non-uniform, in cross section, and decreases in the direction away from the surface of the solid electrolyte body (10) towards the surface of the electrode exposed to the gases.
Claim 2
Dependent Claim
119 words
Electrochemical sensor for determination of the concentration of oxygen in gases, particularly in gases resulting from combustion processes, such as exhaust gases from internal combustion engines, having an ion conductive solid electrolyte body (10) and an electrode (11) applied to a surface thereof, adapted to be exposed to the gases, said electrode comprising a mixture of a ceramic and a noble metal which catalyzes the thermodynamic equilibrium of the gases with respect to a reference, wherein, in accordance with the invention, the concentration of noble metal in the electrode is non-uniform, in cross section, and decreases in the direction away from the surface of the solid electrolyte body (10) towards the surface of the electrode exposed to the gases.
Claim 3
Dependent Claim
13 words
Sensor according to claim 1, wherein the concentration of noble metal decreases continuously.
Claim 4
Dependent Claim
61 words
Sensor according to claim 1, wherein the noble metal comprises at least one of the materials selected from the group consisting of platinum and platinum alloy; and the ceramic comprises at least one of the materials selected from the group consisting of magnesium spinel, aluminum oxide, partially stabilized zirconium dioxide, fully stabilized zirconium dioxide, titanium dioxide, and a high melting glass.
Claim 5
Dependent Claim
18 words
Sensor according to claim 1, wherein the electrode further includes electron conductive metals which are essentially catalytically inactive.
Claim 6
Dependent Claim
46 words
Sensor according to claim 4, wherein the electrode comprises at least one material of the group consisting of: palladium, gold, nickel, an iron-chromium-nickel alloy; doped La-Co-oxide; Perowskite; Ni x Fe 3-x O 4 wherein x has a value of 0 or 1 or any value inbetween;
Claim 7
Dependent Claim
60 words
Sensor according to claim 5, wherein the noble metal comprises at least one of the materials of the group consisting of platinum and platinum alloy; and the ceramic comprises at least one of the materials selected from the group consisting of magnesium spinel, aluminum oxide, partially stabilized zirconium dioxide, fully stabilized zirconium dioxide, titanium dioxide, and a high melting glass.
Claim 8
Dependent Claim
10 words
Sensor according to claim 5 wherein the carbide is SiC.
Claim 9
Dependent Claim
14 words
Sensor according to claim 4, wherein the electron conductive metal comprises a nickel alloy.
Claim 10
Dependent Claim
13 words
Sensor according to claim 4, wherein the electrode comprises an electron conductive oxide.
Claim 11
Dependent Claim
26 words
Sensor according to claim 1, wherein the noble metal comprises at least one of the materials selected from the group consisting of platinum and platinum alloy.
Claim 12
Dependent Claim
11 words
Sensor according to claim 1, wherein the noble metal comprises platinum-rhodium.
Claim 13
Dependent Claim
48 words
Sensor according to claim 1 or 5 or 6 or 10 or 11 or 8, wherein the ceramic comprises at least one of the materials selected from the group consisting of magnesium spinel, aluminum oxide, partially stabilized zirconium dioxide, fully stabilized zirconium dioxide, titanium dioxide, a high-melting glass.
Claim 14
Dependent Claim
22 words
Sensor according to claim 1 or 5 or 6 or 10 or 11 or 8, wherein the ceramic material comprises barium-aluminum-silicate glass.
Claim 15
Dependent Claim
206 words
Method of manufacturing an electrochemical sensor for the determination of oxygen concentration in gases, particularly in gases resulting from a combustion process, such as exhaust gases from an internal combustion engine, having an ion conductive solid electrolyte body (10); and an electrode applied to a surface thereof adapted to be exposed to the gases, and which is composed of a mixture of a ceramic and a noble metal which catalyzes the thermodynamic equilibrium of the gases with respect to a reference, and which is characterized in that the concentration of nobel metal, in cross section, is non-uniform and decreases in the direction away from the surface of the solid electrolyte body (10) towards the surface exposed to the gases, said method comprising the steps of providing a first suspension comprising an aqueous mixture of the noble metal powder, and a powder of a ceramic material; providing a second aqueous suspension of the powder of the ceramic material alone; applying said first suspension to the surface of the solid electrolyte material where the electrode is to be applied and decreasing the rate of application of said first suspension while beginning to apply the second suspension at an increasing rate until the requisite electrode layer thickness is reached.
Claim 16
Dependent Claim
206 words
Method of manufacturing an electrochemical sensor for the determination of oxygen concentration in gases, particularly in gases resulting from a combustion process, such as exhaust gases from an internal combustion engine, having an ion conductive solid electrolyte body (10); and an electrode applied to a surface thereof adapted to be exposed to the gases, and which is composed of a mixture of a ceramic and a noble metal which catalyzes the thermodynamic equilibrium of the gases with respect to a reference, and which is characterized in that the concentration of nobel metal, in cross section, is non-uniform and decreases in the direction away from the surface of the solid electrolyte body (10) towards the surface exposed to the gases, said method comprising the steps of providing a first suspension comprising an aqueous mixture of the noble metal powder, and a powder of a ceramic material; providing a second aqueous suspension of the powder of the ceramic material alone; applying said first suspension to the surface of the solid electrolyte material where the electrode is to be applied and decreasing the rate of application of said first suspension while beginning to apply the second suspension at an increasing rate until the requisite electrode layer thickness is reached.
Claim 17
Dependent Claim
43 words
Method according to claim 14, wherein the change in the rate of application of the first suspension, and of the second suspension, respectively, is selected such that, when the requisite thickness of the electrode is reached, application of the first suspension has terminated.
Claim 18
Dependent Claim
16 words
Method according to claim 15, wherein the change in the rate of application is uniformly continuous.
Claim 19
Dependent Claim
16 words
Method according to claim 15, wherein the change in the rate of application is in steps.
Claim 20
Dependent Claim
18 words
Method according to claim 15, wherein the application step comprises applying said suspensions through spray nozzles (14, 15).
Claim 21
Dependent Claim
98 words
Method according to claim 14, wherein said first suspension comprises an aqueous mixture of 50% platinum and 50% presintered pulverized ceramic (both by volume) comprising 92 mol-% ZrO 2 and 8 mol-% Y 2 O 3 ; said second suspension comprises a presintered pulverized aqueous mixture of 92 mol-% ZrO 2 and 8 mol-% Y 2 O 3 ; said application step comprises spraying said mixtures on the surface of the solid electrolyte body; and further comprising the step of sintering the solid electrolyte body, with the applied mixtures, at a temperature of between 1400° to 1700° C.
Claim 22
Dependent Claim
77 words
Method according to claim 19, wherein the spraying step comprises first only spraying the first suspension onto the solid electrolyte body, and then continuously decreasing the quantity of the first suspension being sprayed on the solid electrolyte body while continuously increasing the quantity of the second suspension, and finally spraying only said second suspension; and wherein said solid electrolyte body (10) is partially sintered or presintered, and said sintering step comprises finally sintering said solid electrolyte body.
Claim 23
Dependent Claim
52 words
Method according to claim 14, wherein said solid electrolyte body is completely sintered; and said first suspension comprises a mixture of (by volume) 50% platinum and 50% pulverized barium-aluminum-silicate glass; and further including the step of sintering the solid electrolyte body with the suspensions applied at a temperature of about 1100° C.
Claim 24
Dependent Claim
54 words
Method according to claim 21, wherein the spraying step comprises first only spraying the first suspension onto the solid electrolyte body, and then continuously decreasing the quantity of the first suspension being sprayed on the solid electrolyte body while continuously increasing the quantity of the second suspension, and finally spraying only said second suspension.
Claim 25
Dependent Claim
78 words
Method according to claim 14, wherein said application step comprises first applying a first suspension having a first ratio of concentration of catalytically active noble metal and ceramic material; before applying said second suspension applying at least one intermediate layer of a third suspension having a lesser concentration of catalytically active noble metal powder, and a higher content of ceramic powder therein; and further including the step of sintering said layers of suspensions and the solid electrolyte body.
Claim 26
Dependent Claim
16 words
Method according to claim 23, wherein the second suspension is devoid of catalytically active noble metal.
References Cited (Backward Citations)
US3978006A
Cited
US4021326A
Cited
US3843400A
Cited
US4097353A
Cited
DE2631721C3
Cited
US4170530A
Cited
US4080276A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-27 | 1985-01-26 | 1985-07-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-27 | 1989-01-26 | 1989-07-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-27 | 1993-01-26 | 1993-07-28 | $7700.00 | Window Closed / Lapsed |