Polyvinyl alcohol semi-permeable membrane and method for producing same
Assignee: Kuraray Co Ltd
•
Filing: 1979-05-21
•
Granted: 1981-07-21
•
Expires: 1999-05-21
Abstract
Abstract A polyvinyl alcohol (PVA) microporous membrane is disclosed which is prepared by a process which comprises forming a PVA membrane containing fine silica particles therein and substantially extracting said silica particles from said membrane, thereby forming a plurality of micropores therein with an average diameter of 0.01 to 50 microns and a porosity of at least 60%.
Inventors
- 👤 Akinori Sueoka
- 👤 Takehiko Okamoto
- 👤 Akio Ohmori
- 👤 Syuji Kawai
- 👤 Minoru Ueda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:42
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0002; B01D67/0023; B01D67/003; B01D69/00; B01D69/08; B01D71/00; B01D71/06; B01D71/38; B01D71/381; C; C08; C08J; C08J9/00; C08J9/26; B01D2323/00; B01D2323/08; B01D2323/081; B01D2323/30; C08J2329/00; C08J2329/02; C08J2329/04
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
194 words
A polyvinyl alcohol (PVA) microporous membrane having a porosity of at least 60% and prepared by a process which comprises preparing a PVA composition containing therein fine silica particles with an average particle size of from 50 Angstrom units to 10 microns in an amount of from 50 to 500 parts by weight per 100 parts of PVA, optionally adjusting the particle size of said silica by aggregating at least a portion of the silica in the composition, coagulating said composition in a coagulation bath to form a PVA membrane, and substantially extracting said silica particles from said membrane, thereby forming a PVA membrane with a microporous layer of controlled uniform pore size, which comprises a plurality of micropores with an average diameter (r) of 0.01 to 50 microns and exists in (1) either the whole thickness of the membrane or (2) in from 80 to 20% of the whole thickness of the membrane with a supporting layer which comprises a plurality of vacuoles with an average longitudinal length (l) of more than 10 microns being the remainder of the whole thickness of the membrane, wherein the ratio of l/r is at least 5.
Claim 2
Dependent Claim
194 words
A polyvinyl alcohol (PVA) microporous membrane having a porosity of at least 60% and prepared by a process which comprises preparing a PVA composition containing therein fine silica particles with an average particle size of from 50 Angstrom units to 10 microns in an amount of from 50 to 500 parts by weight per 100 parts of PVA, optionally adjusting the particle size of said silica by aggregating at least a portion of the silica in the composition, coagulating said composition in a coagulation bath to form a PVA membrane, and substantially extracting said silica particles from said membrane, thereby forming a PVA membrane with a microporous layer of controlled uniform pore size, which comprises a plurality of micropores with an average diameter (r) of 0.01 to 50 microns and exists in (1) either the whole thickness of the membrane or (2) in from 80 to 20% of the whole thickness of the membrane with a supporting layer which comprises a plurality of vacuoles with an average longitudinal length (l) of more than 10 microns being the remainder of the whole thickness of the membrane, wherein the ratio of l/r is at least 5.
Claim 3
Dependent Claim
22 words
A polyvinyl alcohol microporous membrane as defined in claim 1 wherein at least about 90% of said silica particles are extracted therefrom.
Claim 4
Dependent Claim
22 words
A polyvinyl alcohol microporous membrane as defined in claim 2 wherein at least about 99% of said silica particles are extracted therefrom.
Claim 5
Dependent Claim
24 words
A polyvinyl alcohol microporous membrane as defined in claim 1 wherein the micropores formed therein exhibit an average diameter of 0.05 to 20 microns.
Claim 6
Dependent Claim
20 words
A polyvinyl alcohol microporous membrane as defined in claim 1 wherein the membrane has a porosity of at least 70%.
Claim 7
Dependent Claim
39 words
A polyvinyl alcohol microporous membrane as defined in claim 1 wherein said fine silica particles are present in the membrane, prior to extraction, in an amount of 80 to 300 parts by weight per 100 parts by weight PVA.
Claim 8
Dependent Claim
32 words
A polyvinyl alcohol microporous membrane as defined in claim 1,2,3,4,5 or 6 wherein the PVA membrane comprises a plurality of uniform micropores therein with an average diameter of 0.01 to 50 microns.
Claim 9
Dependent Claim
95 words
A polyvinyl alcohol microporous hollow-fiber membrane as defined in claim 1, 2, 3, 5 or 6 wherein the PVA membrane comprises a uniform microporous layer comprising a plurality of micropores with an average diameter (r) of 0.01 to 50 microns and existing in 80 to 20% of the whole thickness of the membrane and a supporting layer comprising a plurality of vacuoles with an average longitudinal length (l) of more than 10 microns and existing in 20 to 80% of the whole thickness of the membrane, and the ratio of l/r is at least 5.
Claim 10
Independent Claim
125 words
A method for preparing a semi-permeable polyvinyl alcohol (PVA) membrane which comprises preparing a PVA composition containing fine silica particles having an average particle size of 50 Angstrom units to 10 microns in an amount of 50 to 500 parts by weight per 100 parts by weight of PVA, optionally adjusting the particle size of said silica by aggregating at least a portion of the silica in the composition, coagulating said composition in a coagulation bath to form a PVA membrane and substantially extracting the silica particles from the resultant membrane with an aqueous or alcoholic alkali solution during and/or after the coagulation of said membrane, thereby obtaining a plurality of micropores of controlled uniform size with an average diameter of 0.01 to 50 microns.
Claim 11
Independent Claim
125 words
A method for preparing a semi-permeable polyvinyl alcohol (PVA) membrane which comprises preparing a PVA composition containing fine silica particles having an average particle size of 50 Angstrom units to 10 microns in an amount of 50 to 500 parts by weight per 100 parts by weight of PVA, optionally adjusting the particle size of said silica by aggregating at least a portion of the silica in the composition, coagulating said composition in a coagulation bath to form a PVA membrane and substantially extracting the silica particles from the resultant membrane with an aqueous or alcoholic alkali solution during and/or after the coagulation of said membrane, thereby obtaining a plurality of micropores of controlled uniform size with an average diameter of 0.01 to 50 microns.
Claim 12
Dependent Claim
21 words
A method as defined in claim 9 wherein at least about 90% of said silica particles are extracted from said membrane.
Claim 13
Dependent Claim
25 words
A method as defined in claim 9 wherein the silica particles are colloidal silica and the particle size thereof ranges from 0.005 to 0.1 micron.
Claim 14
Dependent Claim
25 words
A method as defined in claim 9 wherein the silica particles are silica powder and the particle size thereof ranges from 0.005 to 10 microns.
Claim 15
Dependent Claim
32 words
A method as defined in claim 9 wherein the particle size of said fine silica particles is adjusted by effecting aggregation of at least a portion of said particles in said composition.
Claim 16
Dependent Claim
38 words
A method as defined in claim 9 wherein the fine silica particles are colloidal silica and, with aggregation thereof inhibited, a plurality of micropores are formed in the membrane having an average diameter of 0.01 to 1 micron.
Claim 17
Dependent Claim
33 words
A method as defined in claim 14 except that aggregation is effected resulting in the formation of a membrane containing a plurality of micropores having an average diameter of 0.1 to 50 microns.
Claim 18
Dependent Claim
23 words
A method as defined in claim 15 wherein aggregation is effected by adjusting the pH of the PVA composition to an acidic pH.
Claim 19
Dependent Claim
64 words
A method as defined in claim 16 wherein a PVA composition containing fine silica particles and a boric acid or a water-soluble salt thereof in an amount of 5 to 30% based on the weight of PVA is prepared and said PVA composition is coagulated in a coagulation bath containing an alkali in an amount of 0.5 to 250 g/l and a dehydrating salt.
Claim 20
Dependent Claim
28 words
A method as defined in either of claim 15 or 16 wherein aggregation is effected by addition of NaCl or Na 2 SO 4 to the PVA composition.
Claim 21
Dependent Claim
64 words
A method as defined in claim 18 wherein a PVA composition containing fine silica particles and a boric acid or a water-soluble salt thereof in an amount of 5 to 30% based on the weight of PVA is prepared and said PVA composition is coagulated in a coagulation bath containing an alkali in an amount of 0.5 to 250 g/l and a dehydrating salt.
Claim 22
Dependent Claim
38 words
A method as defined in claim 9 wherein the fine silica particles are silica powder and, with aggregation thereof inhibited, a plurality of micropores are formed in the membrane having an average diameter of 0.01 to 10 microns.
Claim 23
Dependent Claim
33 words
A method as defined in claim 20 except that aggregation is effected resulting in the formation of a membrane containing a plurality of micropores having an average diameter of 0.1 to 50 microns.
Claim 24
Dependent Claim
73 words
A method as defined in claim 9, 10, 11, 12, 13, 14, 15, 20 or 21 wherein a PVA composition containing fine silica particles and a boric acid or a water-soluble salt thereof in an amount of 5 to 30% based on the weight of PVA is prepared and said PVA composition is coagulated in a coagulation bath containing an alkali in an amount of 0.5 to 250 g/l and a dehydrating salt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-20 | 1985-01-19 | 1985-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-20 | 1989-01-19 | 1989-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-20 | 1993-01-19 | 1993-07-21 | $7700.00 | Window Closed / Lapsed |