Production of carbon fiber-tantalum carbide composites
Assignee: Individual
•
Filing: 1979-11-19
•
Granted: 1981-07-14
•
Expires: 1999-11-19
Abstract
Abstract Carbon fiber reinforced tantalum carbide composites are produced by vacuum infiltration of omni-weave carbon, e.g. three dimensional graphite, yarn preforms with an aqueous saturated solution containing tantalum fluoride and sucrose. Anhydrous ammonia is added under pressure, forming ammonium fluoride, which is removed by vacuum sublimation by application of heat. The resulting preform containing tantalum pentoxide and partially pyrolyzed sucrose is heated at high temperature and reduced pressure to decompose the sucrose to yield active carbon which reacts with the tantalum pentoxide to yield tantalum carbide and carbon monoxide. After repeated multiple infiltrations and processing, a composite is produced having a matrix of tantalum carbide or tantalum carbide and carbon, which is reinforced in three or more directions with high strength-high modulus carbon or graphite yarn, the amount of carbon in the matrix phase being a function of the amount of sucrose present in the aqueous solution of tantalum fluoride.
Inventors
- 👤 James O. Gibson
- 👤 Mark G. Gibson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:29
CPC Classifications
C; C04; C04B; C04B35/00; C04B35/515; C04B35/56; C04B35/5607; C04B35/71; C04B35/78; C04B35/80; D; D01; D01F; D01F11/00; D01F11/10; D01F11/12; D01F11/126; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2918; Y10T428/292; Y10T428/2933; Y10T428/2938; Y10T428/294; Y10T428/2958; Y10T428/30
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
67 words
An erosion resistant high strength composite consisting essentially of carbon fibers impregnated or coated with a first coating of tantalum carbide and carbon, a second coating of tantalum carbide overlying said first coating and a third continuous phase coating of a refractory metal overlying said second coating and forming the matrix of said composite, said refractory metal selected from the group consisting of tantalum, rhenium and tungsten.
Claim 2
Dependent Claim
67 words
An erosion resistant high strength composite consisting essentially of carbon fibers impregnated or coated with a first coating of tantalum carbide and carbon, a second coating of tantalum carbide overlying said first coating and a third continuous phase coating of a refractory metal overlying said second coating and forming the matrix of said composite, said refractory metal selected from the group consisting of tantalum, rhenium and tungsten.
Claim 3
Dependent Claim
20 words
The composite as defined in claim 1, said carbon fiber being in the form of a multidirectional carbon fiber preform.
Claim 4
Dependent Claim
22 words
The composite as defined in claim 1, said carbon fiber being in the form of a three dimensional orthogonal carbon yarn preform.
Claim 5
Dependent Claim
12 words
The composite as defined in claim 2, said refractory metal being tantalum.
Claim 6
Dependent Claim
12 words
The composite as defined in claim 3, said refractory metal being tantalum.
Claim 7
Dependent Claim
12 words
The composite as defined in claim 1, said refractory metal being tantalum.
Claim 8
Dependent Claim
12 words
The composite as defined in claim 1, said refractory metal being rhenium.
Claim 9
Dependent Claim
12 words
The composite as defined in claim 1, said refractory metal being tungsten.
Claim 10
Dependent Claim
17 words
The composite as defined in claim 1, said refractory metal being a mixture of rhenium and tungsten.
Claim 11
Dependent Claim
55 words
An erosion resistant high strength composite consisting essentially of carbon fibers impregnated or coated with a first coating of tantalum carbide and a second continuous phase coating of a refractory metal overlying said first coating, and forming the matrix of said composite, said refractory metal selected from the group consisting of tantalum, rhenium and tungsten.
Claim 12
Dependent Claim
55 words
An erosion resistant high strength composite consisting essentially of carbon fibers impregnated or coated with a first coating of tantalum carbide and a second continuous phase coating of a refractory metal overlying said first coating, and forming the matrix of said composite, said refractory metal selected from the group consisting of tantalum, rhenium and tungsten.
Claim 13
Dependent Claim
12 words
The composite as defined in claim 10, said refractory metal being tantalum.
Claim 14
Dependent Claim
70 words
An erosion resistant high strength composite comprising a matrix of a refractory metal selected from the group consisting of tantalum, rhenium and tungsten, and a multiplicity of carbon fibers in said matrix, said carbon fibers impregnated or coated with a first coating of tantalum carbide and carbon, and a second coating of tantalum carbide overlying said first coating, said matrix metal forming a continuous phase coating over said second coating.
Claim 15
Dependent Claim
70 words
An erosion resistant high strength composite comprising a matrix of a refractory metal selected from the group consisting of tantalum, rhenium and tungsten, and a multiplicity of carbon fibers in said matrix, said carbon fibers impregnated or coated with a first coating of tantalum carbide and carbon, and a second coating of tantalum carbide overlying said first coating, said matrix metal forming a continuous phase coating over said second coating.
Claim 16
Dependent Claim
57 words
An erosion resistant high strength composite comprising a matrix of a refractory metal selected from the group consisting of tantalum, rhenium and tungsten, and a multiplicity of carbon fibers in said matrix, said carbon fibers impregnated or coated with a coating of tantalum carbide, said matrix metal forming a continuous phase coating over said tantalum carbide coating.
Claim 17
Dependent Claim
57 words
An erosion resistant high strength composite comprising a matrix of a refractory metal selected from the group consisting of tantalum, rhenium and tungsten, and a multiplicity of carbon fibers in said matrix, said carbon fibers impregnated or coated with a coating of tantalum carbide, said matrix metal forming a continuous phase coating over said tantalum carbide coating.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-13 | 1985-01-12 | 1985-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-13 | 1989-01-12 | 1989-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-13 | 1993-01-12 | 1993-07-14 | $7700.00 | Window Closed / Lapsed |