Sealing compositions for minimizing soluble iron migration
Assignee: WR Grace and Co Conn
•
Filing: 1980-01-11
•
Granted: 1981-07-14
•
Expires: 2000-01-11
Abstract
Abstract Composition and method for sealing containers containing vegetable based beverages, i.e. beer, ale, wine, fruit and vegetable juices.
Inventors
- 👤 Charles A. Billings
- 👤 Robert H. Hofeldt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 23:24
CPC Classifications
C; C09; C09K; C09K3/00; C09K3/10; C08; C08K; C08K3/00; C08K3/18; C08K3/20; C08K3/22; C09K2200/00; C09K2200/02; C09K2200/0217; C09K2200/023; C09K2200/0239; C09K2200/0243; C09K2200/0252; C09K2200/04; C09K2200/0447; C09K2200/06; C09K2200/0615; C09K2200/0622; C09K2200/0635; Y; Y10; Y10T; Y10T428/00; Y10T428/21; Y10T428/214; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31699
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
93 words
A plastisol sealing composition for inhibiting iron migration in acid packs consisting essentially of a polyvinyl chloride resin, between about 50 and 300 parts by weight of a plasticizer for the resin per 100 parts of said resin and the improvement therein comprising from about 0.1 to about 50 parts by weight of a metal oxide iron migration inhibitor per 100 parts of said resin, said inhibitor being selected from the group consisting of aluminum oxide, zinc oxide, magnesium oxide, calcium oxide, copper oxide, silver oxide, nickel oxide, chromium oxide, and mixtures thereof.
Claim 2
Dependent Claim
93 words
A plastisol sealing composition for inhibiting iron migration in acid packs consisting essentially of a polyvinyl chloride resin, between about 50 and 300 parts by weight of a plasticizer for the resin per 100 parts of said resin and the improvement therein comprising from about 0.1 to about 50 parts by weight of a metal oxide iron migration inhibitor per 100 parts of said resin, said inhibitor being selected from the group consisting of aluminum oxide, zinc oxide, magnesium oxide, calcium oxide, copper oxide, silver oxide, nickel oxide, chromium oxide, and mixtures thereof.
Claim 3
Dependent Claim
13 words
The composition of claim 1 wherein the vinyl chloride resin is a homopolymer.
Claim 4
Dependent Claim
19 words
The composition of claim 1 wherein the polyvinyl chloride resin is a copolymer of vinyl chloride and vinyl acetate.
Claim 5
Dependent Claim
28 words
The composition of claim 1 wherein the polyvinyl chloride resin is an emulsion grade resin containing up to about 50% by weight of a polyvinyl chloride blending resin.
Claim 6
Dependent Claim
36 words
The composition of claim 2 or 3 wherein the plasticizer is selected from the group consisting of dioctyl phthalate, di-2-ethylhexyl adipate, di-isodecyl phthalate, di-isooctyl phthalate, epoxidized soybean oil, 2-ethylhexyl diphenyl phosphate, white oil and mixtures thereof.
Claim 7
Dependent Claim
61 words
The composition of claim 2 or 3 including from about 50 up to about 700 parts of filler per 100 parts of resin, said filler being selected from the group consisting of barium sulfate (barytes), talc, calcium carbonate, titanium dioxide, mica, clay (diatomaceous earth), calcium carbonated coated with calcium stearate, magnesium silicate, calcium silicate, calcium sulfate, zinc carbonate and mixtures thereof.
Claim 8
Dependent Claim
149 words
A container closure comprising a cap having deposited therein a resinous mass which functions as a gasket when the closure is in sealing relationship with the container and as an inhibitor to decrease iron migration from said cap and resinous mass, said resinous mass comprising a fluxed plastisol of a composition containing (a) 100 parts by weight of a polyvinyl chloride resin component selected from the group consisting of an emulsion grade polyvinyl chloride resin and an emulsion grade polyvinyl chloride resin admixed with up to about 50% by weight of a polyvinyl chloride blending resin, (b) from about 50 to about 300 parts of a plasticizer for said resin component per 100 parts of said resin component, and the improvement comprising, (c) an iron migration inhibiting amount of a metal oxide selected from the group consisting of aluminum oxide, zinc oxide, magnesium oxide, calcium oxide and mixtures thereof.
Claim 9
Dependent Claim
149 words
A container closure comprising a cap having deposited therein a resinous mass which functions as a gasket when the closure is in sealing relationship with the container and as an inhibitor to decrease iron migration from said cap and resinous mass, said resinous mass comprising a fluxed plastisol of a composition containing (a) 100 parts by weight of a polyvinyl chloride resin component selected from the group consisting of an emulsion grade polyvinyl chloride resin and an emulsion grade polyvinyl chloride resin admixed with up to about 50% by weight of a polyvinyl chloride blending resin, (b) from about 50 to about 300 parts of a plasticizer for said resin component per 100 parts of said resin component, and the improvement comprising, (c) an iron migration inhibiting amount of a metal oxide selected from the group consisting of aluminum oxide, zinc oxide, magnesium oxide, calcium oxide and mixtures thereof.
Claim 10
Dependent Claim
51 words
The container closure of claim 7 wherein said resinous mass includes from about 200 to about 400 parts of a filler selected from the group consisting of barium sulfate (barytes) talc, calcium carbonate, titanium dioxide, mica, clay, calcium carbonate coated with calcium stearate and mixtures thereof per 100 parts of resin.
Claim 11
Dependent Claim
35 words
The container closure of claim 8 wherein the plasticizer is selected from the group consisting of dioctyl phthalate, di-2-ethylhexyl adipate, di-isodecyl phthalate, di-isooctyl phthalate, epoxidized soybean oil, 2-ethylhexyl diphenyl, phosphate white oil and mixtures thereof.
Claim 12
Independent Claim
157 words
A method for improving the iron migration resistance of plasticized vinyl chloride polymer composition consisting essentially of (a) a vinyl chloride homopolymer or a copolymer wherein at least 50% of the repeating units are derived from vinyl chloride, the remaining repeating units being derived from one or more ethylenically unsaturated compounds which are copolymerizable with vinyl chloride, (b) between about 50 and 300 parts by weight of a plasticizer for vinyl chloride polymers per 100 parts of said homopolymer or copolymer, the method comprising (1) adding to said polymer composition between about 0.1 to about 50 parts of a metal oxide per 100 parts of homopolymer or copolymer, said metal oxide being selected from the group consisting of aluminum oxide, zinc oxide, magnesium oxide, calcium oxide, copper oxide, silver oxide, nickel oxide, chromium oxide, and mixtures thereof and (2) subsequently converting said composition into a product selected from the group consisting of shaped articles, films and coatings.
Claim 13
Independent Claim
157 words
A method for improving the iron migration resistance of plasticized vinyl chloride polymer composition consisting essentially of (a) a vinyl chloride homopolymer or a copolymer wherein at least 50% of the repeating units are derived from vinyl chloride, the remaining repeating units being derived from one or more ethylenically unsaturated compounds which are copolymerizable with vinyl chloride, (b) between about 50 and 300 parts by weight of a plasticizer for vinyl chloride polymers per 100 parts of said homopolymer or copolymer, the method comprising (1) adding to said polymer composition between about 0.1 to about 50 parts of a metal oxide per 100 parts of homopolymer or copolymer, said metal oxide being selected from the group consisting of aluminum oxide, zinc oxide, magnesium oxide, calcium oxide, copper oxide, silver oxide, nickel oxide, chromium oxide, and mixtures thereof and (2) subsequently converting said composition into a product selected from the group consisting of shaped articles, films and coatings.
Claim 14
Dependent Claim
34 words
The method of claim 10 wherein the plasticizer is selected from the group consisting of dioctyl phthalate, di-2-ethylhexyl adipate, di-isodecyl phthalate, di-isooctyl phthalate, epoxidized soybean oil, 2-ethylhexyl diphenyl phosphate white oil and mixtures thereof.
Claim 15
Dependent Claim
57 words
The method of claim 11 wherein the polymer composition includes from about 200 to about 400 parts, per 100 parts homopolymer or copolymer, of a filler material selected from the group consisting of barium sulfate (barytes) talc, calcium carbonate, titanium dioxide, mica, clay, calcium carbonate coated with calcium stearate, and mixtures thereof per 100 parts of resin.
Claim 16
Independent Claim
100 words
The method of forming a resinous gasket in a container closure comprising (a) depositing an amount of a plastisol in said closure, said plastisol composition comprising (1) 100 parts of a vinyl chloride resin component, (2) 50-300 parts of a plasticizer for said resin component, and (3) 0.1 to 50 parts of a metal oxide selected from the group consisting of aluminum oxide, zinc oxide, magnesium oxide, calcium oxide and mixtures thereof per 100 parts of resin component, and (b) heating the deposited plastisol composition to advance the plastisol to a fluxed state to form a gasket in said closure.
Claim 17
Independent Claim
100 words
The method of forming a resinous gasket in a container closure comprising (a) depositing an amount of a plastisol in said closure, said plastisol composition comprising (1) 100 parts of a vinyl chloride resin component, (2) 50-300 parts of a plasticizer for said resin component, and (3) 0.1 to 50 parts of a metal oxide selected from the group consisting of aluminum oxide, zinc oxide, magnesium oxide, calcium oxide and mixtures thereof per 100 parts of resin component, and (b) heating the deposited plastisol composition to advance the plastisol to a fluxed state to form a gasket in said closure.
Claim 18
Dependent Claim
34 words
The method of claim 13 wherein the plasticizer is selected from the group consisting of dioctyl phthalate, di-2-ethylhexyl adipate, di-isodecyl phthalate, di-isooctyl phthalate, epoxidized soybean oil, 2-ethylhexyl diphenyl phosphate, white oil and mixtures thereof.
Claim 19
Dependent Claim
60 words
The method of claim 14 wherein the plastisol composition also includes from about 200 to about 400 parts of a filler per 100 parts of resin component, said filler being selected from the group consisting of barium sulfate (barytes) talc, calcium carbonate, titanium dioxide, mica, clay, calcium carbonate coated with calcium stearate and mixtures thereof per 100 parts of resin.
References Cited (Backward Citations)
US2716092A
Cited
US3131081A
Cited
US3171560A
Cited
US3555122A
Cited
US3557030A
Cited
US3563936A
Cited
US3696956A
Cited
US3562191A
Cited
US4041014A
Cited
US3695477A
Cited
US3931909A
Cited
US3751525A
Cited
US3917550A
Cited
US3941737A
Cited
US4010138A
Cited
US4058471A
Cited
US3983086A
Cited
US3957723A
Cited
US4134857A
Cited
US4155480A
Cited
US4134517A
Cited
US4124139A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-13 | 1985-01-12 | 1985-07-14 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-13 | 1989-01-12 | 1989-07-14 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-13 | 1993-01-12 | 1993-07-14 | $7700.00 | Window Closed / Lapsed |