Claim 2

An aqueous alkaline coating solution which is effective in forming corrosion-resistant coatings on surfaces of zinc or alloys of zinc, said solution having a pH of no greater than about 10.2 and consisting essentially of one or more of the following metals in solution: cobalt, nickel, iron and tin, the total amount of said metal or mixture of said metals in the solution being about 0.01 to about 1 g/l; and a complexing material in an amount effective to maintain the metal in solution, said complexing material being selected from the group consisting of pyrophosphate, nitrilotriacetic acid, a salt of nitrilotriacetic acid, and a mixture of two or more of said complexing materials.

Claim 3

A coating solution according to claim 1 wherein said complexing material is pyrophosphate.

Claim 4

A coating solution according to claim 2 including an alkali metal pyrophosphate.

Claim 5

A coating solution according to claim 1 including a reducing agent.

Claim 6

A coating solution according to claim 4 wherein the reducing agent is a sulfite.

Claim 7

An aqueous alkaline coating solution which is effective in forming corrosion-resistant coatings on surfaces of zinc or alloys thereof, said solution having a pH of no greater than about 10.2 and consisting essentially of a metal, namely cobalt, nickel, iron, or tin, or a mixture of two or more of said metals, said metal or mixture being present in the solution at a concentration of about 0.01 to about 1 g/l, and a pyrophosphate complexing agent, said complexing agent being present at a concentration of no greater than about 25 g/l.

Claim 8

An aqueous alkaline coating solution which is effective in forming corrosion-resistant coatings on surfaces of zinc or alloys thereof, said solution having a pH of no greater than about 10.2 and consisting essentially of a metal, namely cobalt, nickel, iron, or tin, or a mixture of two or more of said metals, said metal or mixture being present in the solution at a concentration of about 0.01 to about 1 g/l, and a pyrophosphate complexing agent, said complexing agent being present at a concentration of no greater than about 25 g/l.

Claim 9

A solution according to claim 6 wherein the amount of said metal or mixture is about 0.2 to about 1 g/l, the amount of said complexing agent is no greater than about 10 g/l and the pH of the solution is about 9.4 to about 9.6.

Claim 10

A solution according to claim 6 including sulfite in an amount equivalent to about 1 to about 10 g/l of sodium sulfite.

Claim 11

An aqueous concentrate having a pH of about 9.5 to about 10.4 and being such that an aqueous coating solution containing about 5 to about 25 volume percent of the concentrate consists essentially of: (A) about 0.01 to about 1 g/l of cobalt, nickel, iron or tin, or a mixture of two or more of said metals; and (B) a complexing material selected from the group consisting of pyrophosphate, nitrilotriacetic acid, a salt of nitrilotriacetic acid, and a mixture of two or more of said complexing materials, said complexing material being present in an amount effective to maintain the metal in solution, and wherein said coating solution is effective in forming a corrosion-resistant coating on surfaces of zinc or alloys of zinc.

Claim 12

An aqueous concentrate having a pH of about 9.5 to about 10.4 and being such that an aqueous coating solution containing about 5 to about 25 volume percent of the concentrate consists essentially of: (A) about 0.01 to about 1 g/l of cobalt, nickel, iron or tin, or a mixture of two or more of said metals; and (B) a complexing material selected from the group consisting of pyrophosphate, nitrilotriacetic acid, a salt of nitrilotriacetic acid, and a mixture of two or more of said complexing materials, said complexing material being present in an amount effective to maintain the metal in solution, and wherein said coating solution is effective in forming a corrosion-resistant coating on surfaces of zinc or alloys of zinc.

Claim 13

An aqueous concentrate having a pH of about 9.5 to about 10.4 and being such that an aqueous coating solution containing about 5 to about 25 volume percent of the concentrate consists essentially of: about 0.1 to about 10 g/l of ferric nitrate·9H 2 O, about 0.01 to about 10 g/l of cobalt nitrate·6H 2 O, and about 1 to about 100 g/l of tetra potassium pyrophosphate.

Claim 14

An aqueous concentrate having a pH of about 9.5 to about 10.4 and being such that an aqueous coating solution containing about 5 to about 25 volume percent of the concentrate consists essentially of: about 0.1 to about 10 g/l of ferric nitrate·9H 2 O, about 0.01 to about 10 g/l of cobalt nitrate·6H 2 O, and about 1 to about 100 g/l of tetra potassium pyrophosphate.

Claim 15

A replenishing composition for use in replenishing an aqueous alkaline coating solution, which solution is effective in forming a corrosion-resistant coating on surfaces of zinc or alloys of zinc, said composition having a pH of about 6.8 to about 7.2 and consisting essentially of about 1 to about 10 g/l of dissolved cobalt, nickel, iron or tin, or a mixture of of two or more of said metals and about 10 to about 100 g/l of dissolved inorganic complexing agent, said complexing agent being a pyrophosphate.

Claim 16

A replenishing composition for use in replenishing an aqueous alkaline coating solution, which solution is effective in forming a corrosion-resistant coating on surfaces of zinc or alloys of zinc, said composition having a pH of about 6.8 to about 7.2 and consisting essentially of about 1 to about 10 g/l of dissolved cobalt, nickel, iron or tin, or a mixture of of two or more of said metals and about 10 to about 100 g/l of dissolved inorganic complexing agent, said complexing agent being a pyrophosphate.

Claim 17

A composition according to claim 11 including cobalt or iron or a mixture thereof and about 5 to about 20 g/l of an organic complexing agent selected from the group consisting of nitrilotriacetic acid and a salt thereof.

Claim 18

A composition according to claim 12 wherein the organic complexing agent is nitrilotriacetic acid.

Claim 19

A composition according to claim 11 wherein said inorganic complexing agent is an alkali metal pyrophosphate.

Claim 20

An aqueous alkaline coating solution which is effective in forming a corrosion-resistant coating on surfaces of zinc or alloys of zinc, said solution consisting essentially of about 5 to about 25 g/l of K 4 P 2 O 7 , and a metal compound selected from the group consisting of Fe(NO 3 ) 3 .9H 2 O, Co(NO 3 ) 2 .6H 2 O and mixtures thereof, and wherein the concentration of said Fe(NO 3 ) 3 .9H 2 O is from about 0.1 to about 5 g/l and the concentration of said Co(NO 3 ) 2 .6H 2 O is from about 0.1 to about 2.5 g/l.

Claim 21

An aqueous alkaline coating solution which is effective in forming a corrosion-resistant coating on surfaces of zinc or alloys of zinc, said solution consisting essentially of about 5 to about 25 g/l of K 4 P 2 O 7 , and a metal compound selected from the group consisting of Fe(NO 3 ) 3 .9H 2 O, Co(NO 3 ) 2 .6H 2 O and mixtures thereof, and wherein the concentration of said Fe(NO 3 ) 3 .9H 2 O is from about 0.1 to about 5 g/l and the concentration of said Co(NO 3 ) 2 .6H 2 O is from about 0.1 to about 2.5 g/l.

Claim 22

The coating solution of claim 15 wherein the Fe(NO 3 ) 3 .9H 2 O is present in solution at about 1 g/l, the Co(NO 3 ) 2 .6H 2 O is present in solution at about 0.5 g/l and the K 4 P 2 O 7 is present in solution at about 10 g/l.

Claim 23

The coating solution of claim 15 including about 1 to about 50 g/l of sodium sulfite.

Claim 24

A process for treating a zinc surface comprising forming thereon a coating by contacting said surface with a solution according to claim 1, 2, 3, 4, 5, 6, 7, 8, 15, 16 or 17.