Aqueous cationic thermosetting urethane resin coating compositions
Assignee: Dai Nippon Toryo Co Ltd
•
Filing: 1980-02-11
•
Granted: 1981-07-07
•
Expires: 2000-02-11
Abstract
Abstract The present invention relates to an aqueous thermosetting coating composition comprising (A) a cationic thermosetting urethane resin, (B) a water-insoluble resol-type phenolic resin, (C) an acid as a neutralizing agent and (D) water as a diluent.
Inventors
- 👤 Masaaki Hayashi
- 👤 Koichi Nagami
- 👤 Kazuyoshi Tsuneta
- 👤 Nobuhiro Kenmotusu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 11:48
CPC Classifications
C; C09; C09D; C09D5/00; C09D5/44; C09D5/4419; Y; Y10; Y10S; Y10S524/00; Y10S524/901
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
164 words
An aqueous thermosetting resin coating composition comprising (A) a cationic thermosetting urethane resin, (B) a water-insoluble resol type phenolic resin, (C) an acid as a neutralizing agent and (D) water as a diluent, wherein the cationic thermosetting urethane resin (A) is a thermosetting resin formed by reaction between hydroxyl groups in a reaction product of a polyurethane prepolymer having a terminal isocyanate group with a tertiary amine having at least 2 hydroxyl groups in the molecule and isocyanate groups in a reaction product of equimolar amounts of an organic diisocyanate and a monofunctional blocking agent, the water-insoluble resol type phenolic resin (B) is a thermosetting resin formed by reacting an aldehyde with a phenol at an aldehyde/phenol molar ratio of from 1.0 to 2.5 in the presence of an alkaline catalyst and the mixing weight ratio (based on the solids) of the cationic thermosetting urethane resin (A) to the water-insoluble resol type phenolic resin (B) is in the range of from 99/1 to 70.30.
Claim 2
Dependent Claim
164 words
An aqueous thermosetting resin coating composition comprising (A) a cationic thermosetting urethane resin, (B) a water-insoluble resol type phenolic resin, (C) an acid as a neutralizing agent and (D) water as a diluent, wherein the cationic thermosetting urethane resin (A) is a thermosetting resin formed by reaction between hydroxyl groups in a reaction product of a polyurethane prepolymer having a terminal isocyanate group with a tertiary amine having at least 2 hydroxyl groups in the molecule and isocyanate groups in a reaction product of equimolar amounts of an organic diisocyanate and a monofunctional blocking agent, the water-insoluble resol type phenolic resin (B) is a thermosetting resin formed by reacting an aldehyde with a phenol at an aldehyde/phenol molar ratio of from 1.0 to 2.5 in the presence of an alkaline catalyst and the mixing weight ratio (based on the solids) of the cationic thermosetting urethane resin (A) to the water-insoluble resol type phenolic resin (B) is in the range of from 99/1 to 70.30.
Claim 3
Dependent Claim
62 words
An aqueous thermosetting resin coating composition as set forth in claim 1 wherein the water-insoluble resol type phenolic resin (B) is a thermosetting resin formed by reacting an aldehyde with a phenol at an aldehyde/phenol molar ratio of from 1.0 to 2.5 in the presence of a catalyst selected from the group consisting of ammonia, primary amines, secondary amines and metal hydroxides.
Claim 4
Dependent Claim
27 words
An aqueous thermosetting resin coating composition as set forth in claim 1 wherein the water-insoluble resol type phenolic resin (B) is a magnesium-modified resol type phenolic resin.
Claim 5
Dependent Claim
60 words
An aqueous thermosetting resin coating composition as set forth in claim 3 wherein the magnesium-modified resol type phenolic resin (B) is a modified thermosetting resin formed by reacting an aldehyde with a phenol at an aldehyde/phenol molar ratio of from 1.0 to 2.5 in the presence of an alkaline catalyst and chelating the resulting reaction product with a magnesium compound.
Claim 6
Dependent Claim
45 words
An aqueous thermosetting resin coating composition as set forth in claim 3 wherein the mixing weight ratio (based on the solids) of the cationic thermosetting urethane resin (A) to the magnesium-modified resol type phenolic resin (B) is in the range of from 99/1 to 70/30.
Claim 7
Dependent Claim
73 words
An aqueous thermosetting resin coating composition as set forth in claim 3 wherein the magnesium-modified resol type phenolic resin (B) is a modified thermosetting resin formed by reacting an aldehyde with a phenol at an aldehyde/phenol molar ratio of from 1.0 to 2.5 in the presence of a catalyst selected from the group consisting of ammonia, primary amines, secondary amines and metal hydroxides and chelating the resulting reaction product with a magnesium compound.
Claim 8
Dependent Claim
25 words
An aqueous thermosetting resin coating composition as set forth in claim 3 wherein the magnesium is magnesium oxide, magnesium acetate, magnesium hydroxide or magnesium chloride.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-06 | 1985-01-05 | 1985-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-06 | 1989-01-05 | 1989-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-06 | 1993-01-05 | 1993-07-07 | $7700.00 | Window Closed / Lapsed |