Catalyst-forming components, process for preparing same, and catalysts for stereospecifically polymerizing olefins prepared therefrom
Assignee: Montedison SpA
•
Filing: 1979-05-29
•
Granted: 1981-07-07
•
Expires: 1999-05-29
Abstract
Abstract A solid catalyst-forming component based on titanium trichloride is prepared by reducing TiCl4 to TiCl3 with an organic aluminum compound, at low temperature, and in a suspension of finely dispersed siliceous material in a mixture of inert hydrocarbon solvent and TiCl4. Catalysts prepared from the solid component and useful in the stereospecific polymerization of alpha-olefins to highly isotactic polymers are also disclosed. More specifically, the disclosed process for preparing the solid catalyst-forming component comprises the following operations: (1) preparing a suspension of finely dispersed siliceous material of the diatomite type (diatomaceous earth) in a mixture of inert hydrocarbon solvent and of TiCl4; (2) reducing TiCl4 in said mixture to TiCl3 with an organic aluminum compound at low temperature; and (3) washing the solid catalytic component so obtained with a hydrocarbon solvent, optionally after an activation step at 40 DEG -150 DEG C. in the presence of an ether as complexing agent.
Inventors
- 👤 Cornelio Caldo
- 👤 Luigi Basili
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 10:12
CPC Classifications
C; C08; C08F; C08F10/00
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
116 words
Process for preparing a solid catalyst-forming component based on titanium trichloride, useful in the stereo-specific polymerization of olefins, characterized in that the catalyst component is obtained by: (a) dispersing a siliceous material of the diatomite type having a silica content higher than 50% by weight in a mixture of an inert hydrocarbon solvent and TiCl 4 , in an amount of from 2 to 100 g/gram mole of TiCl 4 ; (b) reducing TiCl 4 , in the presence of said siliceous material, to TiCl 3 by means of aluminum-organic compounds, at temperatures ranging from -20° C. to +20° C.; and (c) washing with the hydrocarbon solvent, filtering, and drying the solid catalyst-forming component so obtained.
Claim 2
Dependent Claim
116 words
Process for preparing a solid catalyst-forming component based on titanium trichloride, useful in the stereo-specific polymerization of olefins, characterized in that the catalyst component is obtained by: (a) dispersing a siliceous material of the diatomite type having a silica content higher than 50% by weight in a mixture of an inert hydrocarbon solvent and TiCl 4 , in an amount of from 2 to 100 g/gram mole of TiCl 4 ; (b) reducing TiCl 4 , in the presence of said siliceous material, to TiCl 3 by means of aluminum-organic compounds, at temperatures ranging from -20° C. to +20° C.; and (c) washing with the hydrocarbon solvent, filtering, and drying the solid catalyst-forming component so obtained.
Claim 3
Dependent Claim
26 words
The process of claim 1, in which the resulting catalyst-forming component is subjected to a heat treatment at temperatures ranging from 40° C. to 150° C.
Claim 4
Dependent Claim
64 words
The process of claim 1, in which the catalyst-forming component obtained is subjected to a heat treatment at temperatures ranging from 40° C. to 150° C., in the presence of a complexing agent consisting of an aliphatic or aromatic ether, and then to a washing with hydrocarbon solvents in order to remove a substantial portion of the AlCl 3 bound to the catalyst-forming component.
Claim 5
Dependent Claim
16 words
The process of claim 3, in which the ether is used in mixture with hydrocarbon solvent.
Claim 6
Dependent Claim
52 words
The process of claim 3, in which the complexing agents are aliphatic or aromatic ethers of the formula R--O--R', wherein R and R', like or unlike each other, are methyl, ethyl, n-propyl, n-butyl, sec.-butyl, tert.-butyl, n-amyl or isoamyl, and are used in an amount of 20-200 g/100 g of catalyst-forming component treated.
Claim 7
Dependent Claim
73 words
A solid catalyst-forming component for stereo-specifically polymerizing olefins, said component being characterized in having a surface area comprised between 20 and 100 m 2 /g, a porosity higher than 0.05 cc/g, a molar composition TiCl 3 .1/ 3 AlCl 3 and supported on a siliceous material of the diatomite type in an amount equal to 2-100 g/mole of TiCl 3 , said siliceous material having a silica content higher than 50% by weight.
Claim 8
Dependent Claim
73 words
A solid catalyst-forming component for stereo-specifically polymerizing olefins, said component being characterized in having a surface area comprised between 20 and 100 m 2 /g, a porosity higher than 0.05 cc/g, a molar composition TiCl 3 .1/ 3 AlCl 3 and supported on a siliceous material of the diatomite type in an amount equal to 2-100 g/mole of TiCl 3 , said siliceous material having a silica content higher than 50% by weight.
Claim 9
Dependent Claim
104 words
A solid catalyst-forming component for stereo-specifically polymerizing olefins, and being characterized in having the following molar composition: TiCl 3 .(AlCl 3 ) 0 .05-0.2.(ether) 0 .01-0.3, in being supported on a siliceous material of the diatomite type having a silica content higher than 50% by weight and used in an amount of from 2 to 100 g/mole of TiCl 3 , in having a surface area comprised between 50 and 150 m 2 /g, and a porosity higher than >0.10 cc/g, and the X-rays spectrum of which shows a crystalline "delta" structure and a diffraction line at 4.13 A, typical of the diatomite support.
Claim 10
Dependent Claim
104 words
A solid catalyst-forming component for stereo-specifically polymerizing olefins, and being characterized in having the following molar composition: TiCl 3 .(AlCl 3 ) 0 .05-0.2.(ether) 0 .01-0.3, in being supported on a siliceous material of the diatomite type having a silica content higher than 50% by weight and used in an amount of from 2 to 100 g/mole of TiCl 3 , in having a surface area comprised between 50 and 150 m 2 /g, and a porosity higher than >0.10 cc/g, and the X-rays spectrum of which shows a crystalline "delta" structure and a diffraction line at 4.13 A, typical of the diatomite support.
Claim 11
Dependent Claim
19 words
Catalyst for polymerizing olefins, obtained by mixing an organometallic aluminum compound with the solid catalyst component of claim 6.
Claim 12
Dependent Claim
22 words
The catalyst of claim 8, in which the organometallic aluminum compound is utilized in the form of a complex with electron-donor compounds.
Claim 13
Dependent Claim
19 words
Catalyst for polymerizing olefins, obtained by mixing an organometallic aluminum compound with the solid catalyst component of claim 8.
Claim 14
Dependent Claim
21 words
The catalyst of claim 10, in which the organometallic compound is utilized in the form of a complex with electron-donor compounds.
References Cited (Backward Citations)
US2981725A
Cited
US3061600A
Cited
AU222426B2
Cited
US2989516A
Cited
US3166542A
Cited
US3345351A
Cited
US3594330A
Cited
US3883492A
Cited
US3591656A
Cited
US3787384A
Cited
US3769233A
Cited
US4098979A
Cited
US3953414A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-06 | 1985-01-05 | 1985-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-06 | 1989-01-05 | 1989-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-06 | 1993-01-05 | 1993-07-07 | $7700.00 | Window Closed / Lapsed |