Assignee: Individual
•
Filing: 1979-08-20
•
Granted: 1981-07-07
•
Expires: 1999-08-20
Abstract
Abstract A method of growing a diamond crystal which comprises bombarding the diamond with a flux of carbon ions of sufficient energy to penetrate the diamond crystal and cause crystal growth which is at least predominantly internal, the temperature of the crystal being at least 400° C. and less than the graphitization temperature, such that the diamond crystal structure is maintained during growth.
Inventors
- 👤 Richard S. Nelson
- 👤 John A. Hudson
- 👤 David J. Mazey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 08:07
CPC Classifications
C; C30; C30B; C30B29/00; C30B29/02; C30B29/04; C30B1/00
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
87 words
A method of producing a diamond crystal of altered electrical conductivity which comprises bombarding the diamond with a flux of carbon ions containing an ionic impurity whereby the crystal is doped with an impurity which alters the electrical conductivity thereof, said flux being of sufficient energy to penetrate the diamond crystal and cause crystal growth which is at least predominantly internal, the temperature of the crystal being at least 400° C. and less than the graphitisation temperature, such that the diamond crystal structure is maintained during growth.
Claim 2
Independent Claim
87 words
A method of producing a diamond crystal of altered electrical conductivity which comprises bombarding the diamond with a flux of carbon ions containing an ionic impurity whereby the crystal is doped with an impurity which alters the electrical conductivity thereof, said flux being of sufficient energy to penetrate the diamond crystal and cause crystal growth which is at least predominantly internal, the temperature of the crystal being at least 400° C. and less than the graphitisation temperature, such that the diamond crystal structure is maintained during growth.
Claim 3
Dependent Claim
16 words
A method according to claim 1, in which the crystal temperature does not exceed 1075° C.
Claim 4
Dependent Claim
27 words
A method according to claim 1, in which the ion beam passes through a vacuum chamber in which the pressure is no greater than 10 -4 torr.
Claim 5
Dependent Claim
22 words
A method according to claim 1, in which the flux of carbon ions contains no more than 3% of the ionic impurity.
Claim 6
Dependent Claim
19 words
A method according to claim 1, in which the ion flux contains no more than 1% of the impurity.
Claim 7
Dependent Claim
18 words
A method according to claim 1, in which the ionic impurity is an ion of boron or phosphorus.
Claim 8
Dependent Claim
59 words
A method according to claim 1, in which the carbon ion flux contains an ionic impurity which gives rise to either P- or N-type conductivity in the crystal following which the crystal is doped with a different ionic impurity which gives rise to the other type of conductivity so as to produce an P N junction in the crystal.
Claim 9
Dependent Claim
16 words
A method according to claim 7, in which doping is carried out simultaneously with crystal growth.
Claim 10
Dependent Claim
41 words
A method according to claim 1, in which the carbon ion flux is emitted from a first ion source and a flux of impurity ions is emitted from a second ion source, said fluxes merging before impingement on the crystal surface.
Claim 11
Dependent Claim
26 words
A method according to claim 1, in which one or more diamonds are subjected to vibration during bombardment so that directionally uniform growth thereof is maintained.
Claim 12
Dependent Claim
36 words
A method according to claim 1, in which a plurality of diamonds are supported in close mutual proximity during bombardment and in which lateral growth thereof is promoted so that the diamonds form a polycrystalline mass.
Claim 13
Dependent Claim
26 words
A method according to claim 11, in which lateral growth is promoted by variation in the orientation of the diamonds with respect to the ion flux.
References Cited (Backward Citations)
CA727830A
Cited
US3148161A
Cited
US3142595A
Cited
US3383567A
Cited
GB1205288A
Cited
US3630679A
Cited
GB1334520A
Cited
US3961103A
Cited
US4191735A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-06 | 1985-01-05 | 1985-07-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-06 | 1989-01-05 | 1989-07-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-06 | 1993-01-05 | 1993-07-07 | $7700.00 | Window Closed / Lapsed |