Oxygen electrode and method for preparation thereof
Assignee: University of Missouri–St. Louis
•
Filing: 1980-02-20
•
Granted: 1981-06-30
•
Expires: 2000-02-20
Abstract
Abstract An oxygen electrode adapted for use for polarographic, galvanometric or amperometric analyses, that is resistant to poisoning and effective for accurate,reproducible current and voltage measurements. The electrode comprises a conductor constituted of a metal which catalyzes the cathodic reduction of oxygen, an electrical lead electrically connected to the conductor, and an insulating jacket covering all of the conductor except a working surface thereof that is adapted to communicate with an oxygen-containing environment for the cathodic reduction of oxygen. The conductor has a layer of an oxide of the aforesaid metal at its working surface. There is a thin polymeric coating over said oxide layer and securely adhered to the working surface. The coating comprises a polymer produced by glow discharge polymerization of an aliphatic hydrocarbon and has such properties to permit the reduction of oxygen at the electrode by electrons supplied at the working surface through the lead and conductor. A method for preparing the electrode is also disclosed.
Inventors
- 👤 Allen W. Hahn
- 👤 Michael F. Nichols
- 👤 Ashok K. Sharma
- 👤 Eckhard W. Hellmuth
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:53
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/404; G01N27/416; G01N27/48; Y; Y10; Y10S; Y10S205/00; Y10S205/917
Claims Analysis
Total Claims: 39
Claim 1
Independent Claim
142 words
An oxygen electrode, adapted for use in polarography, galvanometry or amperometry, that is resistant to poisoning and effective for accurate, reproducible current and voltage measurements, comprising a conductor constituted of a metal which catalyzes the cathodic reduction of oxygen, an electrical lead electrically connected to said conductor, an insulating jacket covering all of said conductor except a working surface thereof that is adapted to communicate with an oxygen-containing environment for the cathodic reduction of oxygen, said conductor having a layer of an oxide of said metal at said surface, and a thin polymeric coating over said oxide layer and securely adhered to said surface, said coating comprising a polymer produced by glow discharge polymerization of an aliphatic hydrocarbon and having such properties as to permit reduction of oxygen at said electrode by electrons supplied at said surface through said lead and conductor.
Claim 2
Dependent Claim
142 words
An oxygen electrode, adapted for use in polarography, galvanometry or amperometry, that is resistant to poisoning and effective for accurate, reproducible current and voltage measurements, comprising a conductor constituted of a metal which catalyzes the cathodic reduction of oxygen, an electrical lead electrically connected to said conductor, an insulating jacket covering all of said conductor except a working surface thereof that is adapted to communicate with an oxygen-containing environment for the cathodic reduction of oxygen, said conductor having a layer of an oxide of said metal at said surface, and a thin polymeric coating over said oxide layer and securely adhered to said surface, said coating comprising a polymer produced by glow discharge polymerization of an aliphatic hydrocarbon and having such properties as to permit reduction of oxygen at said electrode by electrons supplied at said surface through said lead and conductor.
Claim 3
Dependent Claim
23 words
An oxygen electrode as set forth in claim 1 wherein said coating has a thickness of between about 500 Angstroms and 0.3 μm.
Claim 4
Dependent Claim
23 words
An oxygen electrode as set forth in claim 2 wherein said coating has a thickness of between about 0.1 and about 0.15 μm.
Claim 5
Dependent Claim
25 words
An oxygen electrode as set forth in claim 2 wherein said metal is selected from the group consisting of platinum, gold, palladium, tantalum and iridium.
Claim 6
Dependent Claim
14 words
An oxygen electrode as set forth in claim 4 wherein said metal comprises platinum.
Claim 7
Dependent Claim
18 words
An oxygen electrode as set forth in claim 5 wherein said oxide layer is predominantly comprised of PtO.
Claim 8
Dependent Claim
17 words
An oxygen electrode as set forth in claim 2 wherein said oxide layer is formed by anodization.
Claim 9
Dependent Claim
36 words
An oxygen electrode as set forth in claim 2 wherein said polymeric coating is produced by glow discharge polymerization of a monomer selected from the group consisting of ethylene, propylene, butene, methane, ethane, propane and butane.
Claim 10
Dependent Claim
14 words
An oxygen electrode as set forth in claim 8 wherein said polymer is cross-linked.
Claim 11
Dependent Claim
17 words
An oxygen electrode as set forth in claim 9 wherein said polymer comprises glow discharge polymerized propylene.
Claim 12
Dependent Claim
14 words
An oxygen electrode as set forth in claim 10 wherein said polymer contains oxygen.
Claim 13
Dependent Claim
36 words
An oxygen electrode as set forth in claim 11 wherein said polymer conforms to the average empirical formula: (C.sub.1 H.sub.x O.sub.y) where x is at least about 1.4 and y is no greater than about 0.2.
Claim 14
Dependent Claim
25 words
An oxygen electrode as set forth in claim 2 wherein said coating is of uniform thickness and conforms to the contours of said oxidized surface.
Claim 15
Dependent Claim
34 words
An oxygen electrode as set forth in claim 2 wherein said conductor comprises a wire having the crossectional face of one end thereof uncovered by said insulating jacket so as to constitute said surface.
Claim 16
Dependent Claim
22 words
An oxygen electrode as set forth in claim 14 wherein said wire has a diameter of not more than about 500 μm.
Claim 17
Dependent Claim
20 words
An oxygen electrode as set forth in claim 15 having an overall diameter of not more than about 1.5 mm.
Claim 18
Dependent Claim
17 words
An oxygen electrode as set forth in claim 14 wherein said insulating jacket is comprised of glass.
Claim 19
Dependent Claim
30 words
An electrode as set forth in claim 2 wherein said coating is produced by deposition at a rate of between about 25 and about 40 Angstroms of thickness per minute.
Claim 20
Dependent Claim
44 words
An electrode as set forth in claim 18 wherein said coating is deposited in said surface in a tubular reactor for which electromagnetic power is generated at a rate of between about 0.2 and about 0.9 KWH per gram of monomer continuously fed thereto.
Claim 21
Dependent Claim
45 words
An electrode as set forth in claim 18 wherein said coating is deposited on said surface in a Bell jar reactor for which electromagnetic power is generated at a rate of between about 5 and about 15 KWH per gram of monomer continuously fed thereto.
Claim 22
Independent Claim
149 words
A method for producing an oxygen electrode, adapted for use in polarography, galvanometry or amperometry, that is resistant to poisoning and effective for accurate, reproducible current and voltage measurement, the method comprising the steps of: generating a plasma from a gas in a low pressure chamber containing the working surface of an oxygen electrode, said electrode comprising a conductor constituted of a metal which catalyzes the cathodic reduction of oxygen, and an insulating jacket that covers all of said conductor except said working surface that is adapted to communicate with an oxygen-containing environment for the cathodic reduction of oxygen, said conductor having a layer of an oxide of said metal at said surface; introducing an aliphatic hydrocarbon gas into said low pressure chamber; polymerizing said hydrocarbon by action of said plasma thereon; and depositing a thin adherent coating of said polymer over said oxide layer on said working surface.
Claim 23
Independent Claim
149 words
A method for producing an oxygen electrode, adapted for use in polarography, galvanometry or amperometry, that is resistant to poisoning and effective for accurate, reproducible current and voltage measurement, the method comprising the steps of: generating a plasma from a gas in a low pressure chamber containing the working surface of an oxygen electrode, said electrode comprising a conductor constituted of a metal which catalyzes the cathodic reduction of oxygen, and an insulating jacket that covers all of said conductor except said working surface that is adapted to communicate with an oxygen-containing environment for the cathodic reduction of oxygen, said conductor having a layer of an oxide of said metal at said surface; introducing an aliphatic hydrocarbon gas into said low pressure chamber; polymerizing said hydrocarbon by action of said plasma thereon; and depositing a thin adherent coating of said polymer over said oxide layer on said working surface.
Claim 24
Dependent Claim
30 words
A method as set forth in claim 21 wherein said polymerization reaction is terminated when the thickness of said polymer coating is between about 500 Angstroms and about 0.3 μm.
Claim 25
Dependent Claim
30 words
A method as set forth in claim 22 wherein said polymerization reaction is terminated when the thickness of said polymer coating is between about 0.1 μm and about 0.15 μm.
Claim 26
Dependent Claim
21 words
A method as set forth in claim 21 wherein said plasma is generated by introduction of electromagnetic energy into said chamber.
Claim 27
Dependent Claim
28 words
A method as set forth in claim 24 wherein said coating is deposited at a rate of between about 25 and about 40 Angstroms of thickness per minute.
Claim 28
Dependent Claim
43 words
A method as set forth in claim 25 wherein the polymerization is carried out in a tubular reactor and during polymerization electromagnetic power is generated at a rate of between about 0.2 and about 0.9 KWH per gram of monomer continuously fed thereto.
Claim 29
Dependent Claim
44 words
A method as set forth in claim 25 wherein the polymerization is carried out in a Bell jar reactor and during polymerization electromagnetic power is generated at a rate of between about 5 and about 15 KWH per gram of monomer continuously fed thereto.
Claim 30
Dependent Claim
28 words
A method as set forth in claim 24 wherein said plasma is generated by inductive coupling at a frequency of between about 1 kilohertz and about 40,000 megahertz.
Claim 31
Dependent Claim
31 words
A method as set forth in claim 24 wherein the pressure in said chamber is maintained at between about 10 and about 30 pascals absolute during the polymerization of said hydrocarbon.
Claim 32
Dependent Claim
13 words
A method as set forth in claim 24 wherein said gas comprises argon.
Claim 33
Dependent Claim
27 words
A method as set forth in claim 21 wherein said aliphatic hydrocarbon is selected from the group consisting of ethylene, propylene, butane, methane, ethane, propane and butane.
Claim 34
Dependent Claim
14 words
A method as set forth in claim 31 wherein said aliphatic hydrocarbon comprises propylene.
Claim 35
Dependent Claim
18 words
A method as set forth in claim 22 wherein said oxide layer is provided by anodizing said surface.
Claim 36
Dependent Claim
25 words
A method as set forth in claim 33 wherein said surface is anodized in a strong oxidizing electrolyte that is substantially free of chloride ion.
Claim 37
Dependent Claim
47 words
A method as set forth in claim 34 wherein said surface is anodized in sulfuric acid having a normality of between about 0.5 and about 2.0 at a voltage of between about 1 and about 4 volts D.C. for between about 30 sec. and about 5 minutes.
Claim 38
Dependent Claim
29 words
A method as set forth in claim 21 wherein said surface is cleaned and etched by exposure of the surface to argon plasma prior to deposition of said coating.
Claim 39
Dependent Claim
26 words
A method as set forth in claim 21 wherein said coating is etched to increase its stability and hydrophilicity by exposing it to an oxygen plasma.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-29 | 1984-12-29 | 1985-06-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-29 | 1988-12-29 | 1989-06-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-29 | 1992-12-29 | 1993-06-30 | $7700.00 | Window Closed / Lapsed |