Preparation of high surface area metal fluorides and metal oxyfluorides, especially aluminum fluoride extrudates
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1978-01-16
•
Granted: 1981-06-23
•
Expires: 1998-01-16
Abstract
Abstract A method is described for the preparation of high surface area metal fluorides and metal oxyfluorides comprising reacting high surface area metal oxides with a fluorocarbon vapor wherein the fluorocarbon is selected from the group consisting of CH4-QFQ wherein Q is 1 to 3 and totally or partially fluorinated C2-C6 alkanes, alkenes and alkynes and C5-C6 cyclic alkanes, preferably fluoroform (CHF3) wherein the metal oxides and the fluorocarbon vapors are contacted at a temperature of from about 300 DEG to about 800 DEG C., for a time sufficient to effect the essentially complete conversion of the metal oxides into metal fluorides or the partial conversion of the metal oxides into metal oxyfluorides. The metal oxides converted into metal fluorides may be selected from the group consisting of the oxides of sodium, potassium, lithium, cesium, magnesium, calcium, barium, strontium, tin, antimony, bismuth, titanium, zirconium, vanadium, chromium, manganese, iron, cobalt, rhodium, mercury, nickel, copper, silver, zinc, cadmium, lead, uranium, europium, idium, lutetium, neodymium, thallium and mixtures thereof. The metal oxides converted into metal oxyfluorides may be selected from the group recited above and further include silicon, niobium, hafnium, tantalum, molybdenum, tungsten, technetium, rhenium, osmium, iridium, lanthanum and ruthenium. The above metal oxides may also be utilized in combination with alumina and silica. The fluorocarbon partial pressure in the treatment vapor may be in the range of from about 0.001 to about 100 atmosphere. By the practice of the instant invention high surface area metal fluoride extrudates are prepared by the conversion of metal oxide extrudate, particularly aluminum fluoride extrudates from alumina extrudates.
Inventors
- 👤 Gary B. McVicker
- 👤 Joseph J. Eggert
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 00:43
CPC Classifications
C; C01; C01G; C01G35/00; C01G35/02; B; B01; B01J; B01J27/00; B01J27/06; B01J27/08; B01J27/12; C01B; C01B11/00; C01B11/24; C01B9/00; C01B9/08; C01F; C01F5/00; C01F5/26; C01F5/28; C01F7/00; C01F7/48; C01F7/50; C01G1/00; C01G1/06; C01G23/00; C01G23/02; C01G23/028; C01G43/00; C01G43/04; C01G43/06
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
144 words
A process for the preparation of high surface area metal fluorides comprising reacting a metal oxide selected from the group consisting of the oxides of sodium, potassium, lithium, cesium, magnesium, calcium, barium, strontium, tin, antimony, bismuth, titanium, zirconium, vanadium, chromium, manganese, iron, cobalt, rhodium, mercury, nickel, copper, silver, zinc, cadmium, lead, uranium, europium, indium, lutetium, neodymium, thallium and mixtures thereof with a fluorocarbon selected from the group consisting of CH 4-Q F Q wherein Q is 1 to 3 and partially and totally fluoridated C 2 -C 6 alkanes, alkenes, alkynes and C 5 -C 6 cyclic alkanes wherein the metal oxide and the fluorocarbon are contacted at a temperature of from 300° to 800° C. at a fluorocarbon partial pressure of from 0.001 to 100 atmospheres, for a time sufficient to effect the substantially complete conversion of the metal oxide into metal fluoride.
Claim 2
Dependent Claim
144 words
A process for the preparation of high surface area metal fluorides comprising reacting a metal oxide selected from the group consisting of the oxides of sodium, potassium, lithium, cesium, magnesium, calcium, barium, strontium, tin, antimony, bismuth, titanium, zirconium, vanadium, chromium, manganese, iron, cobalt, rhodium, mercury, nickel, copper, silver, zinc, cadmium, lead, uranium, europium, indium, lutetium, neodymium, thallium and mixtures thereof with a fluorocarbon selected from the group consisting of CH 4-Q F Q wherein Q is 1 to 3 and partially and totally fluoridated C 2 -C 6 alkanes, alkenes, alkynes and C 5 -C 6 cyclic alkanes wherein the metal oxide and the fluorocarbon are contacted at a temperature of from 300° to 800° C. at a fluorocarbon partial pressure of from 0.001 to 100 atmospheres, for a time sufficient to effect the substantially complete conversion of the metal oxide into metal fluoride.
Claim 3
Dependent Claim
85 words
The process of claim 1 wherein the fluorocarbon is selected from the group consisting of CH 4-Q F Q wherein Q is 1 to 3 and straight and branch chain C 2 -C 6 fluorocarbons of the general formula C.sub.A H.sub.2A+2-B F.sub.B wherein A is an integer ranging from 2-6 inclusive and B is an integer ranging from 1-14, and cyclic fluorocarbon of the formula C.sub.X H.sub.2X-C F.sub.C wherein X is 5 or 6 and C is an integer ranging from 1 to 12 inclusive.
Claim 4
Dependent Claim
26 words
The process of claim 1 wherein the metal oxide is selected from the group consisting of the oxides of titanium, magnesium, uranium, nickel, cobalt and zirconium.
Claim 5
Dependent Claim
14 words
The process of claim 1 wherein the metal oxide is the oxides of titanium.
Claim 6
Dependent Claim
12 words
The process of claim 2 wherein A ranges from 2 to 3.
Claim 7
Dependent Claim
10 words
The process of claim 1 wherein the fluorocarbon is trifluoromethane.
Claim 8
Dependent Claim
18 words
The process of claim 1 further comprising the use of alumina in combination with the enumerated metal oxides.
Claim 9
Dependent Claim
14 words
The process of claim 1 wherein the temperature ranges from 300° to 600° C.
Claim 10
Dependent Claim
14 words
The process of claim 1 wherein the temperature ranges from 350° to 550° C.
Claim 11
Dependent Claim
16 words
The process of claim 1 wherein the fluorocarbon partial pressure ranges from 0.1 to 1.0 atmospheres.
Claim 12
Dependent Claim
102 words
A process for the preparation of high surface area aluminum fluoride extrudates comprising reacting a high surface area alumina extrudate with a fluorocarbon selected from the group consisting of CH 4-Q F Q wherein Q is 1-3 and partially and totally fluoridated C 2 -C 6 alkanes, alkenes, alkynes and C 5 -C 6 cyclic alkane wherein the alumina extrudate and the fluorocarbon are contacted at a temperature of from 300° to 800° C. at a fluorocarbon pressure ranging from 0.001 to 100 atm for a time sufficient to affect the essentially complete conversion of the alumina to an aluminum fluoride extrudate.
Claim 13
Dependent Claim
102 words
A process for the preparation of high surface area aluminum fluoride extrudates comprising reacting a high surface area alumina extrudate with a fluorocarbon selected from the group consisting of CH 4-Q F Q wherein Q is 1-3 and partially and totally fluoridated C 2 -C 6 alkanes, alkenes, alkynes and C 5 -C 6 cyclic alkane wherein the alumina extrudate and the fluorocarbon are contacted at a temperature of from 300° to 800° C. at a fluorocarbon pressure ranging from 0.001 to 100 atm for a time sufficient to affect the essentially complete conversion of the alumina to an aluminum fluoride extrudate.
Claim 14
Dependent Claim
83 words
The process of claim 11 wherein the fluorocarbon is selected from the group consisting of CH 4-y F y wherein y is 1-3 and straight and branch chain C 2 -C 6 fluorocarbons of the general formulae C.sub.A H.sub.2A+2-B F.sub.B wherein A is an integer ranging from 2-6 inclusive and B is an integer ranging from 1-14, the cyclic fluorocarbons of the formula C.sub.X H.sub.2X-C F.sub.C wherein X is 5 or 6 and C is an integer ranging from 1 to 12 inclusive.
Claim 15
Dependent Claim
10 words
The process of claim 11 wherein the fluorocarbon is trifluoromethane.
Claim 16
Dependent Claim
14 words
The process of claim 11 wherein the temperature is from 300° to 600° C.
Claim 17
Dependent Claim
16 words
The process of claim 11 wherein the fluorocarbon partial pressure ranges from 0.1 to 1.0 atmospheres.
Claim 18
Dependent Claim
17 words
The process of claim 11 wherein the conversion of alumina to aluminum fluoride is greater than 90%.
Claim 19
Dependent Claim
23 words
The process of claim 11 wherein the aluminum fluoride extrudate has a surface area of from 10 to over 50 m 2 /gm.
Claim 20
Dependent Claim
105 words
High surface area aluminum fluoride extrudates prepared by reacting a high surface area alumina extrudate with a fluorocarbon selected from the group consisting of CH 4-Q F Q wherein Q is 1 to 3 and partially and totally fluoridated C 2 -C 6 alkanes, alkenes, alkynes and C 5 -C 6 cyclic alkanes wherein the alumina extrudate and the fluorocarbon are contacted at a temperature of from about 300° to about 800° C. at a fluorocarbon partial pressure of from about 0.001 to about 1 atmosphere for a time sufficient to effect the substantially complete conversion of the alumina extrudate into the aluminum fluoride extrudate.
Claim 21
Dependent Claim
105 words
High surface area aluminum fluoride extrudates prepared by reacting a high surface area alumina extrudate with a fluorocarbon selected from the group consisting of CH 4-Q F Q wherein Q is 1 to 3 and partially and totally fluoridated C 2 -C 6 alkanes, alkenes, alkynes and C 5 -C 6 cyclic alkanes wherein the alumina extrudate and the fluorocarbon are contacted at a temperature of from about 300° to about 800° C. at a fluorocarbon partial pressure of from about 0.001 to about 1 atmosphere for a time sufficient to effect the substantially complete conversion of the alumina extrudate into the aluminum fluoride extrudate.
Claim 22
Dependent Claim
85 words
The high surface area aluminum fluoride extrudates prepared as in claim 18 wherein the fluorocarbon is selected from the group consisting of fluoroform, straight and branch chain C 2 -C 6 fluorocarbons of the general formula C.sub.A H.sub.2A+2-B F.sub.B wherein A is an integer ranging from 2 to 6 inclusive and B is an integer ranging from 1 to 14 and cyclic fluorocarbons of the formula C.sub.X H.sub.2X-C F.sub.C wherein X is 5 or 6 and C is an integer ranging from 1 to 12.
Claim 23
Dependent Claim
14 words
The aluminum fluoride extrudates of claim 19 wherein A ranges from 2 to 3.
Claim 24
Dependent Claim
12 words
The aluminum fluoride extrudates of claim 18 wherein the fluorocarbon is fluoroform.
Claim 25
Dependent Claim
18 words
The aluminum fluoride extrudates of claim 18 wherein the temperature ranges from about 300° to about 600° C.
Claim 26
Dependent Claim
20 words
The aluminum fluoride extrudates of claim 18 wherein the fluorocarbon partial pressure ranges from about 0.1 to about 1 atmosphere.
Claim 27
Dependent Claim
149 words
High surface area mixed metal-aluminum fluorides prepared by reacting a metal oxide selected from the group consisting of the oxides of sodium, potassium, lithium, cesium, magnesium, calcium, barium, strontium, tin, antimony, bismuth, titanium, zirconium, vandium, chromium, manganese, iron, cobalt, rhodium, mercury, nickel, copper silver, zinc, cadmium, lead, uranium, europium, indium, lutetium, neodymium and thallium in combination with alumina with a fluorocarbon selected from the group consisting of CH 4-Q F Q wherein Q is 1 to 3 and partially and totally fluoridated C 2 -C 6 alkanes, alkenes, alkynes and C 5 -C 6 cyclic alkanes wherein the metal oxide and the fluorocarbon are contacted at a temperature of from about 300° to about 800° C. at a fluorocarbon partial pressure of from about 0.001 to about 1 atmosphere for a time sufficient to effect the substantially complete conversion of the mixed metal-aluminum oxide into the mixed metal-aluminum fluoride.
Claim 28
Dependent Claim
149 words
High surface area mixed metal-aluminum fluorides prepared by reacting a metal oxide selected from the group consisting of the oxides of sodium, potassium, lithium, cesium, magnesium, calcium, barium, strontium, tin, antimony, bismuth, titanium, zirconium, vandium, chromium, manganese, iron, cobalt, rhodium, mercury, nickel, copper silver, zinc, cadmium, lead, uranium, europium, indium, lutetium, neodymium and thallium in combination with alumina with a fluorocarbon selected from the group consisting of CH 4-Q F Q wherein Q is 1 to 3 and partially and totally fluoridated C 2 -C 6 alkanes, alkenes, alkynes and C 5 -C 6 cyclic alkanes wherein the metal oxide and the fluorocarbon are contacted at a temperature of from about 300° to about 800° C. at a fluorocarbon partial pressure of from about 0.001 to about 1 atmosphere for a time sufficient to effect the substantially complete conversion of the mixed metal-aluminum oxide into the mixed metal-aluminum fluoride.
Claim 29
Dependent Claim
84 words
The high surface area mixed metal-aluminum fluorides prepared as in claim 24 wherein the fluorocarbon is selected from the group consisting of fluoroform, straight and branch chain C 2 -C 6 fluorocarbons of the general formula C.sub.A H.sub.2A+2-B F.sub.B wherein A is an integer ranging from 2 to 6 inclusive and B is an integer ranging from 1 to 14 cyclic fluorocarbons of the formula C.sub.X H.sub.2X-C F.sub.C wherein X is 5 or 6 and C is an integer ranging from 1 to 12.
References Cited (Backward Citations)
US1314571A
Cited
US2899269A
Cited
US2972513A
Cited
GB897187A
Cited
GB969863A
Cited
US3130168A
Cited
GB995186A
Cited
US3235618A
Cited
US3305300A
Cited
GB1135838A
Cited
US3494729A
Cited
US3717586A
Cited
CA936331A
Cited
SU416317A1
Cited
US3956147A
Cited
US3821356A
Cited
DE2424852A1
Cited
US4034070A
Cited
US4128589A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-22 | 1984-12-22 | 1985-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-22 | 1988-12-22 | 1989-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-22 | 1992-12-22 | 1993-06-23 | $7700.00 | Window Closed / Lapsed |