Manufacturing glass with a bushing having a directionally aligned dispersion strengthened tip plate
Assignee: Owens Corning Fiberglas Technology Inc
•
Filing: 1979-08-17
•
Granted: 1981-06-23
•
Expires: 1999-08-17
Abstract
Abstract An improvement in the manufacture of fibrous glass products is provided by employing a bushing in which the bottom wall, or tip plate, is fabricated of a properly aligned dispersion strengthened precious metal, or alloy thereof.
Inventors
- 👤 Dennis L. McGarry
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 22:03
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/08; C03B37/083; C03B37/095
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
80 words
In a fibrous glass manufacturing process comprising maintaining a pool of molten glass in a glass feeder having a foraminous bottom plate with a transverse axis shorter than a longitudinal axis thereof, and attenuating a glass stream issuing from said foraminous bottom plate into a glass fiber, said plate being formed of a dispersion strengthened precious metal, or alloy thereof, the improvement wherein said dispersion strengthened plate has a smaller creep rate along its transverse axis than its longitudinal axis.
Claim 2
Dependent Claim
80 words
In a fibrous glass manufacturing process comprising maintaining a pool of molten glass in a glass feeder having a foraminous bottom plate with a transverse axis shorter than a longitudinal axis thereof, and attenuating a glass stream issuing from said foraminous bottom plate into a glass fiber, said plate being formed of a dispersion strengthened precious metal, or alloy thereof, the improvement wherein said dispersion strengthened plate has a smaller creep rate along its transverse axis than its longitudinal axis.
Claim 3
Dependent Claim
28 words
The improvement of claim 1 wherein said plate is formed by a process which includes rolling, the rolling direction of said plate being parallel to said transverse axis.
Claim 4
Dependent Claim
43 words
The improvement of claim 2 wherein said plate consists essentially of platinum, or a platinum-rhodium alloy, as the dispersing medium and an effective dispersion strengthening amount of a metal oxide or carbide or boride or silicide or nitride or sulfide as the dispersoid.
Claim 5
Dependent Claim
111 words
In a fibrous glass manufacturing apparatus comprising glass feeding means for maintaining a pool of molten glass and for issuing a stream of glass therefrom, said means including a dispersion strengthened foraminous bottom plate, of platinum or a platinum-rhodium alloy, with a transverse axis shorter than a longitudinal axis thereof, and means for attenuating said glass stream into a glass fiber, the improvement wherein said bottom plate is anisotropic with respect to its creep rate, the axis with the smaller creep rate corresponding to the transverse axis of the bottom plate of said feeding means and the axis with the larger creep rate corresponding to longitudinal axis of said bottom plate.
Claim 6
Dependent Claim
111 words
In a fibrous glass manufacturing apparatus comprising glass feeding means for maintaining a pool of molten glass and for issuing a stream of glass therefrom, said means including a dispersion strengthened foraminous bottom plate, of platinum or a platinum-rhodium alloy, with a transverse axis shorter than a longitudinal axis thereof, and means for attenuating said glass stream into a glass fiber, the improvement wherein said bottom plate is anisotropic with respect to its creep rate, the axis with the smaller creep rate corresponding to the transverse axis of the bottom plate of said feeding means and the axis with the larger creep rate corresponding to longitudinal axis of said bottom plate.
Claim 7
Dependent Claim
28 words
The improvement of claim 1 wherein said plate has a stress rupture life, along its transverse axis, of at least 48 hours (at 1400° C. and 1000 psi).
Claim 8
Dependent Claim
36 words
The improvement of claim 1 wherein the creep rate of said plate along its transverse axis is less than about 5×10 -5 inch per inch per hour (at 2,800° F. and a stress of 800 p.s.i.)
Claim 9
Dependent Claim
10 words
The improvement of claim 4 wherein said dispersoid is zirconia.
Claim 10
Dependent Claim
27 words
The improvement of claim 6 wherein the ratio of the creep rate along the transverse axis to that along the longitudinal axis is greater than about 2.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-22 | 1984-12-22 | 1985-06-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-22 | 1988-12-22 | 1989-06-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-22 | 1992-12-22 | 1993-06-23 | $7700.00 | Window Closed / Lapsed |