Moldable plastic orthopedic cast
Assignee: Hexcel Corp
•
Filing: 1979-12-10
•
Granted: 1981-06-16
•
Expires: 1999-12-10
Abstract
Abstract Orthopedic structures are prepared from a thermal softening resin (e.g. polycaprolactone) impregnated large mesh knit fabric carrier having relatively large diameter strands and having a relatively high weight ratio of the polycaprolactone or equivalent resin composition to the fabric carrier. The impregnated fabric can be formed in rolls which may be warmed above the softening temperature of the resin. The thermally softened impregnated fabric becomes highly flexible and pliant and may then be wrapped in multiple layers about the limb to be immobilized. The large knit fabric carrier allows for twisting of the fabric, forming and reforming, so as to obtain the desired shape and degree of support. The overlapping layers of impregnated fabric bond to each other during wrapping and whereafter the impregnated fabric rapidly cools to a hard structurally stable cast, which is porous so as to minimize maceration or other deleterious skin conditions from developing.
Inventors
- 👤 Kenneth M. Holland
- 👤 Milton F. Custer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 21:04
CPC Classifications
A; A61; A61F; A61F13/00; A61F13/04; A61L; A61L15/00; A61L15/07; A61L15/12; A61B; A61B17/00; A61B2017/00831; A61B2017/00902
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
182 words
A bandage material for forming in place an orthopedic cast, comprising a pliant, large mesh fabric carrier formed from a knit having bulky strands of high structural stability and low density, each strand being formed from a plurality of fibers, said strands being porous and of relatively bulky and high heat insulating material, the fabric carrier having openings of relatively large transverse dimension, the strands having a raw diameter of between 0.013 and 0.040 inches, each strand being coated and only partially impregnated with a polymer composition having a heat softening point of not less than 125° F. and not greater than 165° F., said polymer coated strands defining openings having an area of not less than 0.020 square inches and not greater than about 0.25 square inches, whereby said openings are sufficiently large so that the polymer composition does not form air impervious blocks across the openings, said coated strands being sufficiently large so as to have a plurality of air voids providing increased insulating properties for said bandage material after the strands have been partially impregnated with said polymer composition.
Claim 2
Dependent Claim
182 words
A bandage material for forming in place an orthopedic cast, comprising a pliant, large mesh fabric carrier formed from a knit having bulky strands of high structural stability and low density, each strand being formed from a plurality of fibers, said strands being porous and of relatively bulky and high heat insulating material, the fabric carrier having openings of relatively large transverse dimension, the strands having a raw diameter of between 0.013 and 0.040 inches, each strand being coated and only partially impregnated with a polymer composition having a heat softening point of not less than 125° F. and not greater than 165° F., said polymer coated strands defining openings having an area of not less than 0.020 square inches and not greater than about 0.25 square inches, whereby said openings are sufficiently large so that the polymer composition does not form air impervious blocks across the openings, said coated strands being sufficiently large so as to have a plurality of air voids providing increased insulating properties for said bandage material after the strands have been partially impregnated with said polymer composition.
Claim 3
Dependent Claim
15 words
A bandage material according to claim 1 wherein the openings are approximately 0.025 sq. in.
Claim 4
Dependent Claim
19 words
A bandage material according to claim 1 wherein the outside fluff diameter is between 0.030 in. and 0.20 in.
Claim 5
Dependent Claim
17 words
A bandage according to claim 3 wherein the carrier is a cotton knit formed of staple fiber.
Claim 6
Dependent Claim
21 words
A bandage according to claim 1 wherein said carrier comprises a Raschel type substantially cotton knit of staple fiber bulky strands.
Claim 7
Dependent Claim
19 words
A bandage according to claim 1 wherein the polymer coated strands have a diameter between 0.010 to 0.260 in.
Claim 8
Dependent Claim
19 words
A bandage according to claim 1 wherein the coated strands have a diameter between 0.075 in. and 0.160 in.
Claim 9
Dependent Claim
115 words
A bandage according to claim 1 where the polymer composition comprises a solid crystalline cyclic ester polymer having at least a major amount of recurring structural units of the formula: ##STR2## wherein each R, individually, is selected from the group consisting of halogen, alkyl, halo and alkoxy; A is the oxy group; X is an integer from 1 to 4; Y is an integer from 1 to 4; Z is an integer of 0 or 1; provided that (a) the sum of X plus Y plus Z is at least 4 and not greater than 7, and (b) that the total number of R variables which are substituents other than hydrogen does not exceed 3.
Claim 10
Dependent Claim
18 words
A bandage according to claim 8 and wherein said polymer composition comprises in major proportions a poly-S-caprolactone polymer.
Claim 11
Dependent Claim
19 words
A bandage according to claim 9 wherein the poly-ε-caprolactone polymer has a molecular weight average of at least 30,000.
Claim 12
Dependent Claim
16 words
A bandage according to claim 10 wherein the molecular weight of the poly-ε-caprolactone is about 40,000.
Claim 13
Dependent Claim
165 words
A bandage material for forming in place an orthopedic cast, comprising a pliant, large mesh fabric carrier having a high structural stability and Rascheal type substantially cotton knit of staple bulky strands, each strand being formed from a plurality of fibers and being coated and only partially impregnated with a polymer composition having a heat softening point of not less than 125° F. and not greater than 165° F., each coated strand having a diameter between about 0.010 to about 0.260 inches, said polymer coated strands defining openings having an area of not less than about 0.020 square inches and not greater than about 0.25 square inches, whereby said openings are sufficiently large so that the polymer composition does not form impervious blocks across the openings, said strands having a raw diameter of between 0.013 inches and 0.040 inches to cause the coated strands to be sufficiently large so as to have a plurality of air voids providing increased insulating properties to said bandage material.
Claim 14
Dependent Claim
165 words
A bandage material for forming in place an orthopedic cast, comprising a pliant, large mesh fabric carrier having a high structural stability and Rascheal type substantially cotton knit of staple bulky strands, each strand being formed from a plurality of fibers and being coated and only partially impregnated with a polymer composition having a heat softening point of not less than 125° F. and not greater than 165° F., each coated strand having a diameter between about 0.010 to about 0.260 inches, said polymer coated strands defining openings having an area of not less than about 0.020 square inches and not greater than about 0.25 square inches, whereby said openings are sufficiently large so that the polymer composition does not form impervious blocks across the openings, said strands having a raw diameter of between 0.013 inches and 0.040 inches to cause the coated strands to be sufficiently large so as to have a plurality of air voids providing increased insulating properties to said bandage material.
Claim 15
Dependent Claim
26 words
A bandage according to claim 12 wherein the polymer composition comprises in major proportions a poly-ε-caprolactone polymer having a molecular weight average of at least 30,000.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-15 | 1984-12-15 | 1985-06-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-15 | 1988-12-15 | 1989-06-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-15 | 1992-12-15 | 1993-06-16 | $7700.00 | Window Closed / Lapsed |