US4272464A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preventing plasticizer bleeding on polyvinyl chloride shaped articles
Assignee: Shin-Etsu Chemical Co Ltd
•
Filing: 1979-06-22
•
Granted: 1981-06-09
•
Expires: 1999-06-22
Abstract
Abstract A method for preventing bleeding of plasticizers on the surface of shaped articles of plasticized polyvinyl chloride resins. The method comprises the steps of (a) blending a urethane elastomer with the polyvinyl chloride resin together with the plasticizer and other optional additives prior to fabrication of the polyvinyl chloride resin composition into shaped articles, (b) fabricating the resin composition into desired shaped articles, and (c) subjecting the thus shaped article to a treatment with low temperature plasma of a gas. Carbon monoxide is preferred as the gas for the plasma atmosphere.
Inventors
- 👤 Michihiko Asai
- 👤 Yoshio Suda
- 👤 Kiyoshi Imada
- 👤 Susumu Ueno
- 👤 Hirokazu Nomura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:13
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/123; C08J2327/00; C08J2327/02; C08J2327/04; C08J2327/06
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
88 words
A method for preventing bleeding of a plasticizer on the surface of a shaped article of a plasticized polyvinyl chloride resin which comprises (a) combining the polyvinyl chloride resin with a plasticizer, (b) blending a urethane elastomer with the polyvinyl chloride resin prior to the fabrication of the polyvinyl chloride resin into a shaped article, (c) fabricating the polyvinyl chloride resin with plasticizer admixed with the urethane elastomer into a shaped article and (d) subjecting the shaped article to a treatment with low temperature plasma of a gas.
Claim 2
Independent Claim
88 words
A method for preventing bleeding of a plasticizer on the surface of a shaped article of a plasticized polyvinyl chloride resin which comprises (a) combining the polyvinyl chloride resin with a plasticizer, (b) blending a urethane elastomer with the polyvinyl chloride resin prior to the fabrication of the polyvinyl chloride resin into a shaped article, (c) fabricating the polyvinyl chloride resin with plasticizer admixed with the urethane elastomer into a shaped article and (d) subjecting the shaped article to a treatment with low temperature plasma of a gas.
Claim 3
Dependent Claim
35 words
The method as claimed in claim 1 wherein the amount of the urethane elastomer is in the range from 5 to 120 parts by weight per 100 parts by weight of the polyvinyl chloride resin.
Claim 4
Dependent Claim
50 words
The method as claimed in claim 1 wherein the gas for the low temperature plasma is selected from the group consisting of helium, neon, argon, nitrogen, nitrous oxide, nitrogen dioxide, oxygen, air, carbon monoxide, carbon dioxide, hydrogen, halogens, halogen compounds, olefins, halogenated hydrocarbons, aromatic hydrocarbons, heterocyclic organic compounds and organosilanes.
Claim 5
Dependent Claim
25 words
The method as claimed in claim 1 wherein the gas for the low temperature plasma is carbon monoxide or a mixed gas containing carbon monoxide.
Claim 6
Dependent Claim
23 words
The method as claimed in claim 1 wherein the pressure of the gas is in the range from 0.001 Torr to 10 Torr.
Claim 7
Independent Claim
147 words
A method for preventing bleeding of a plasticizer on the surface of a shaped article made of plasticized polyvinyl chloride resin comprising; blending a polyvinyl chloride resin with a urethane elastomer in an amount of 5 to 120 parts by weight of the urethane elastomer to 100 parts by weight of the polyvinyl chloride resin; combining the polyvinyl chloride with a plasticizer fabricating the blend of polyvinyl chloride resin, plasticizer and urethane elastomer into a shaped article; and subjecting the shaped article to treatment with a low temperature plasma of a gas, the plasma produced by electrical current and the gas selected from the group consisting of helium, neon, argon, nitrogen, nitrous oxide, nitrogen dioxide, oxygen, air, carbon monoxide, carbon dioxide, hydrogen, halogens, halogen compounds, olefins, halogenated hydrocarbons, aromatic hydrocarbons, heterocyclic organic compounds and organosilanes, with the pressure of the gas being from 0.001 to 10 torr.
Claim 8
Independent Claim
147 words
A method for preventing bleeding of a plasticizer on the surface of a shaped article made of plasticized polyvinyl chloride resin comprising; blending a polyvinyl chloride resin with a urethane elastomer in an amount of 5 to 120 parts by weight of the urethane elastomer to 100 parts by weight of the polyvinyl chloride resin; combining the polyvinyl chloride with a plasticizer fabricating the blend of polyvinyl chloride resin, plasticizer and urethane elastomer into a shaped article; and subjecting the shaped article to treatment with a low temperature plasma of a gas, the plasma produced by electrical current and the gas selected from the group consisting of helium, neon, argon, nitrogen, nitrous oxide, nitrogen dioxide, oxygen, air, carbon monoxide, carbon dioxide, hydrogen, halogens, halogen compounds, olefins, halogenated hydrocarbons, aromatic hydrocarbons, heterocyclic organic compounds and organosilanes, with the pressure of the gas being from 0.001 to 10 torr.
Claim 9
Dependent Claim
67 words
A method according to claim 6, wherein the plasticizer which is prevented from bleeding on the surface of the shaped article is chosen from the group consisting of dioctyl phthalate, dibutyl phthalate, dioctyl adipate, dibutyl sebacate, esters of pentaerithritol, diethyleneglycol, dibenzoate, acetylricinoleic, tricresyl phosphate, triphenyl phospate, epoxidated soy bean oil, epoxidated linseed oil, bisphenol-based epoxy resins, acetyltributyl citrate, acetyltreoctyl citrate, trialkyl trimallitate, tetra-n-octyl, pyromellitate, and polypropylene adipate.
Claim 10
Dependent Claim
35 words
A method according to claim 7, wherein the amount of plasticizer to polyvinyl chloride resin compositions is in the range of 30 to 70 parts by weight per 100 parts by weight of the resin.
Claim 11
Dependent Claim
31 words
A method according to claim 6, further including additional additives selected from the group consisting of: fillers, anti-oxidants, ultra-violet light absorbers, stabilizers, anti-static agents, anti-fogging agents, pigments, dyestuffs, and crosslinking aids.
Claim 12
Dependent Claim
28 words
A method according to claim 6, further including the addition of rubbery elastomers in the amount of less than 120 parts per 100 parts of polyvinyl chloride resin.
Claim 13
Dependent Claim
50 words
A shaped article of plasticized polyvinyl chloride resin which does not bleed plasticizer from its surface made according to the method of claim 6 comprising a fabricated blend of urethane elastomer with the polyvinyl chloride resin and plasticizer which is exposed to treatment with low temperature plasma of a gas.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-08 | 1984-12-08 | 1985-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-08 | 1988-12-08 | 1989-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-08 | 1992-12-08 | 1993-06-09 | $7700.00 | Window Closed / Lapsed |