Abstract
Abstract In the fabrication of semiconductor integrated circuits which include recessed oxide isolation regions (29), formation of the undesired "bird's head" and "bird's beak" is avoided by reducing the rate of oxide growth from the sidewalls of isotropically etched recesses (22) while oxide is being grown from the bottoms of the recess regions. A silicon nitride mask (24) formed selectively on each of the sidewalls which has previously been coated with a thin silicon dioxide layer (23) reduces the rate of oxide growth therefrom, so that the oxidized recess regions have substantially planar surfaces after termination of the oxide growth.
Inventors
- 👤 Dawon Kahng
- 👤 Theodore A. Shankoff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 20:29
CPC Classifications
H; H10; H10P; H10P14/00; H10P14/60; H10P14/61; H10W; H10W10/00; H10W10/01; H10W10/011; H10W10/012; H10W10/0121; H10W10/0124; H10W10/10; H10W10/13; Y; Y10; Y10S; Y10S148/00; Y10S148/117; Y10S148/143; Y10S438/00; Y10S438/942; Y10S438/944
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
130 words
A method for fabricating semiconductor circuits in a semiconductive silicon body (10) comprising a process for forming an oxide isolation region (29) in the body (10) by thermal oxide growth in a recess region (22) in said body (10) while the rate of such growth on a sidewall of said recess region (22), as compared with growth on the bottom of said recess region (22), is reduced by a mask (24) on said sidewall, characterized in that said sidewall is coated with a thermally grown silicon dioxide layer (23) on which said mask (24) is formed prior to the oxide growth in the recess region (22), said recess region having been formed by substantially isotropic etching of a restricted portion of an originally substantially planar surface of the body (10).
Claim 2
Independent Claim
130 words
A method for fabricating semiconductor circuits in a semiconductive silicon body (10) comprising a process for forming an oxide isolation region (29) in the body (10) by thermal oxide growth in a recess region (22) in said body (10) while the rate of such growth on a sidewall of said recess region (22), as compared with growth on the bottom of said recess region (22), is reduced by a mask (24) on said sidewall, characterized in that said sidewall is coated with a thermally grown silicon dioxide layer (23) on which said mask (24) is formed prior to the oxide growth in the recess region (22), said recess region having been formed by substantially isotropic etching of a restricted portion of an originally substantially planar surface of the body (10).
Claim 3
Dependent Claim
48 words
The method recited in claim 1 in which the thickness of the silicon dioxide layer (23) is in the range of about 50 to 300 angstroms and in which the mask (24) is a layer of silicon nitride which covers an entire sidewall of said recess region (22).
Claim 4
Dependent Claim
44 words
The method recited in claim 1 in which the thickness of the silicon dioxide layer (23) is about 100 angstroms and in which the mask (24) is a layer of silicon nitride having a thickness in the range of about 500 to 800 angstroms.
Claim 5
Dependent Claim
36 words
The method of claim 1 in which the entire surface of said recess region (22) is covered with a masking material which effectively is removed from all but the said sidewall to form said mask (24).
Claim 6
Dependent Claim
38 words
The method recited in claim 4 in which the thickness of the silicon dioxide layer (23) is in the range of about 50 to 300 angstroms and in which the mask (24) is a layer of silicon nitride.
Claim 7
Dependent Claim
44 words
The method recited in claim 4 in which the thickness of the silicon dioxide layer (23) is about 100 angstroms and in which the mask (24) is a layer of silicon nitride having a thickness in the range of about 500 to 800 angstroms.
Claim 8
Independent Claim
115 words
A method for manufacturing semiconductor devices having oxide isolation region (29) for electrically isolating different semiconductor circuit portions formed in a semiconductive silicon body (10) comprising the steps of: (a) forming recess regions (22) in said body at an originally planar major surface thereof by means of substantially isotropic etching thereof; (b) coating the sidewalls of said recess region (22) with a layer (23) of thermally grown silicon dioxide and a masking layer (24) on said thermally grown layer (23) which reduces the rate of thermal oxide growth from silicon, said masking layer (24); not coating the bottoms of said recess region (22); and (c) thermally growing silicon dioxide to fill said recess regions (22).
Claim 9
Independent Claim
115 words
A method for manufacturing semiconductor devices having oxide isolation region (29) for electrically isolating different semiconductor circuit portions formed in a semiconductive silicon body (10) comprising the steps of: (a) forming recess regions (22) in said body at an originally planar major surface thereof by means of substantially isotropic etching thereof; (b) coating the sidewalls of said recess region (22) with a layer (23) of thermally grown silicon dioxide and a masking layer (24) on said thermally grown layer (23) which reduces the rate of thermal oxide growth from silicon, said masking layer (24); not coating the bottoms of said recess region (22); and (c) thermally growing silicon dioxide to fill said recess regions (22).
Claim 10
Dependent Claim
36 words
The method of claim 7 in which said masking layer (24) is essentially silicon nitride and in which the thickness of the silicon dioxide layer (23) is in the range of about 50 to 300 Angstroms.
Claim 11
Independent Claim
37 words
The method of claims 7 or 8 in which the material of said masking layer is first deposited over the entire surface of the recess regions (22) and is then selectively removed from the said bottoms thereof.
Claim 12
Dependent Claim
45 words
The method of claim 9 in which said removal includes the step of ion etching the masking layer material at said bottoms of the recess, using an overhanging film at the edges of the recess regions (22) as a shadow mask against said ion etching.
Claim 13
Dependent Claim
14 words
The method of claim 10 in which said ion etching is reactive ion etching.
References Cited (Backward Citations)
US3761327A
Cited
US3958040A
Cited
US4002511A
Cited
US4088516A
Cited
US4219369A
Cited
US4209349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-06-08 | 1984-12-08 | 1985-06-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-06-08 | 1988-12-08 | 1989-06-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-06-08 | 1992-12-08 | 1993-06-09 | $7700.00 | Window Closed / Lapsed |