Fused, thermoplastic partitioning agent and preparation of crumb rubber coated therewith

Claim 2

The process of producing an elastomeric crumb, coated with a fused resinous partitioning agent which adheres to the crumb without substantial cohesion of the coated particles to one another, which process comprises coating a tacky polymer crumb, the particles of which measure 1 to 50 mm. across, using a latex blend of 0.1 to 10 percent solids content which is a blend of (a) 50 to 80 parts by weight of a styrene-butadiene copolymer resin with a styrene content of substantially 80 to 99 percent and (b) 50 to 20 parts by weight of a polymethyl methacrylate resin, the weight of the resin blend being 1 to 25 percent of the weight of the elastomeric crumb, using sufficient of the latex blend at a temperature substantially as high as 85° C. to coat the crumb, adding the resin latex blend containing a coagulant to a slurry of the rubber particles in water at a temperature of 90°-95° C. to coagulate the blend, and drying the coated crumb at a final temperature of at least 85° C. and not more than 95° C. whereby the coating adheres to the crumb without substantial cohesion of the coated particles.

Claim 3

In the process of applying a partitioning agent to a slurry of elastomeric particles and drying without substantial cohesion of the particles, the improvement which comprises preparing a dilute latex blend of (a) 50 to 80 parts by weight of a styrene-butadiene copolymer resin with a styrene content of substantially 80 to 99 percent and (b) 50 to 20 parts by weight of a polymethyl methacrylate resin, said latex blend having a solids content of 0.1 to 10 percent, coagulating a latex of the elastomer to form particles which measure 1 to 50 mm. across in an aqueous medium containing coagulant in slight excess of that necessary to coagulate the elastomeric particles; mixing the two resin latices to produce the blend, using sufficient of the latex blend at a temperature above 85° C. to coat the elastomeric particles sufficiently to prevent the agglomeration of the coated particles during drying, coagulating the latex blend and drying the coated particles using a final temperature of at least 85° C. and not more than 95° C. wherby the coating adheres to the particles without substantial cohesion of the coated particles.

Claim 4

In the process of applying a partitioning agent to a slurry of elastomeric particles and drying without substantial cohesion of the particles, the improvement which comprises preparing a dilute latex blend of (a) 50 to 80 parts by weight of a styrene-butadiene copolymer resin with a styrene content of substantially 80 to 99 percent and (b) 50 to 20 parts by weight of a polymethyl methacrylate resin, said latex blend having a solids content of 0.1 to 10 percent, coagulating a latex of the elastomer to form particles which measure 1 to 50 mm. across in an aqueous medium containing coagulant in slight excess of that necessary to coagulate the elastomeric particles; mixing the two resin latices to produce the blend, using sufficient of the latex blend at a temperature above 85° C. to coat the elastomeric particles sufficiently to prevent the agglomeration of the coated particles during drying, coagulating the latex blend and drying the coated particles using a final temperature of at least 85° C. and not more than 95° C. wherby the coating adheres to the particles without substantial cohesion of the coated particles.

Claim 5

The process in claim 1 in which the polymer from which the crumb is produced is a butadiene-styrene rubber.

Claim 6

The process of claim 1 in which the polymer from which the crumb is produced has black masterbatch composition.

Claim 7

The process of claim 1 in which the polymer from which the crumb is produced has an oil masterbatch composition.

Claim 8

The process of claim 1 in which the polymer from which the crumb is produced has an oil black masterbatch composition.

Claim 9

The process of claim 2 in which the partitioning agent is a blend of substantially 70 parts of the copolymer and 30 parts of the polymethyl methacrylate, and the final drying temperature of at least 85° C. and no more than 110° C.

Claim 10

The process of claim 2 in which the concentration of the components in the latex of the partitioning agent was not over 2 percent by weight.

Claim 11

The process of claim 1 in which the polymer crumb is extruded as a strand measuring no more than substantially 50 mm. in the largest dimension, dividing the strand into lengths no more than substantially 50 mm. in length, forming an aqueous slurry therefrom, and coating the resulting crumb particles with the blend.

Claim 12

The process of claim 1 in which the crumb is obtained by grinding, forming a slurry from the ground particles and coating the particles.

Claim 13

The process of claim 1 in which the polymer crumb is coated and dried in a continuous process.

Claim 14

The process of claim 1 in which the polymer crumb is obtained in a continuous coagulation process and is then coated and dried in a continuous process.

Claim 15

The process of claim 1 in which the weight of the resin blend is 2 to 10 percent of the weight of the polymer crumb.

Claim 16

The process of claim 2 in which the solids content of the latex blend is 2 to 10 percent of the weight of the latex.

Claim 17

The process of claim 2 in which the styrene content of the copolymer does not exceed 85 percent.

Claim 18

In the process of applying a fused, resinous partitioning agent to a slurry of elastomeric particles whereby the partitioning agent adheres as a coating to the particles without substantial cohesion of the coated particles, the improvement which comprises coagulating a latex of the elastomer to form particles which measure 1 to 50 mm. in diameter in an aqueous medium containing coagulant in slight excess of that necessary to coagulate the elastomeric particles and heating the coagulated slurry to a temperature above 85° C., preparing a dilute latex blend of (a) 50 to 80 parts by weight of a styrenebutadiene copolymer resin with a styrene content of substantially 80 to 99 percent and (b) 50 to 20 parts by weight of a polymethyl methacrylate resin, said latex blend having a solids content of 0.1 to 10 percent, heating the resin latex blend to a temperature of at least 85° C.; adding this hot latex blend to a hot slurry of elastomeric particles to coagulate the resin and fuse it on the surface of the particles thereby coating them with resin amounting to 1 to 25 percent of the weight of the elastomer; and drying the coated particles using a final temperature of at least 85° C. and not more than 110° C. whereby the partitioning agent adheres to the particles without substantial cohesion of the particles.

Claim 19

In the process of applying a fused, resinous partitioning agent to a slurry of elastomeric particles whereby the partitioning agent adheres as a coating to the particles without substantial cohesion of the coated particles, the improvement which comprises coagulating a latex of the elastomer to form particles which measure 1 to 50 mm. in diameter in an aqueous medium containing coagulant in slight excess of that necessary to coagulate the elastomeric particles and heating the coagulated slurry to a temperature above 85° C., preparing a dilute latex blend of (a) 50 to 80 parts by weight of a styrenebutadiene copolymer resin with a styrene content of substantially 80 to 99 percent and (b) 50 to 20 parts by weight of a polymethyl methacrylate resin, said latex blend having a solids content of 0.1 to 10 percent, heating the resin latex blend to a temperature of at least 85° C.; adding this hot latex blend to a hot slurry of elastomeric particles to coagulate the resin and fuse it on the surface of the particles thereby coating them with resin amounting to 1 to 25 percent of the weight of the elastomer; and drying the coated particles using a final temperature of at least 85° C. and not more than 110° C. whereby the partitioning agent adheres to the particles without substantial cohesion of the particles.