Process for making dual-material self-bonding lip seal
Assignee: Caterpillar Inc
•
Filing: 1977-08-12
•
Granted: 1981-05-26
•
Expires: 1997-08-12
Abstract
Abstract The invention is concerned with a process for forming a unitary seal comprising a support section formed of a high modulus, i.e. rigid high impact strength plastic and a sealing section formed of an elastomeric material, the support and sealing section being directly bonded together without the use of an adhesive therebetween to form the unitary seal. The process comprises contacting a surface portion of the support section directly with a surface portion of the sealing section, under sufficient pressure to assure a pressed contact therebetween, with the sections at a temperature of 50° C.-400° C. for a time sufficient to cause bonding between the contacting surface portions to form the unitary seal.
Inventors
- 👤 Terry D. Linne
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 03:09
CPC Classifications
B; B29; B29D; B29D99/00; B29D99/0053; B29C; B29C45/00; B29C45/16; B29C45/1657; B29C45/1676; F; F16; F16J; F16J15/00; F16J15/16; F16J15/32; F16J15/328; F16J15/3284; B29K; B29K2021/00; B29L; B29L2031/00; B29L2031/26
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
225 words
A process for the injection molding of a unitary seal having a support section formed of a high modulus rigid polycarbonate plastic and a sealing section formed of a polyurethane elastomeric material, consisting essentially of: injecting sufficient polycarbonate, heated on a temperature from about 200° C. to about 400° C., into a first injection mold to fill said first injection mold; retaining said polycarbonate in said first injection mold for a time sufficient to allow solidification of said polycarbonate and formation thereof into said support section; forming a second injection mold with a surface portion of said support section defining a portion of the surface of said second injection mold; injecting polyurethane elastomer, heated to a temperature from about 150° C. to about 300° C., into said second injection mold in a sufficient amount to fill said second injection mold; confining said polyurethane elastomer in said second injection mold for a time sufficient to allow solidification thereof into said sealing section; and retaining said second mold intact under sufficient pressure to retain a pressed contact between said surface portion of said support section and a mating surface portion of said sealing section, while maintaining said sections at a temperature from about 50° C. to about 400° C. for a time sufficient to cause a bonding between said contacting surface portions to form said unitary seal.
Claim 2
Dependent Claim
225 words
A process for the injection molding of a unitary seal having a support section formed of a high modulus rigid polycarbonate plastic and a sealing section formed of a polyurethane elastomeric material, consisting essentially of: injecting sufficient polycarbonate, heated on a temperature from about 200° C. to about 400° C., into a first injection mold to fill said first injection mold; retaining said polycarbonate in said first injection mold for a time sufficient to allow solidification of said polycarbonate and formation thereof into said support section; forming a second injection mold with a surface portion of said support section defining a portion of the surface of said second injection mold; injecting polyurethane elastomer, heated to a temperature from about 150° C. to about 300° C., into said second injection mold in a sufficient amount to fill said second injection mold; confining said polyurethane elastomer in said second injection mold for a time sufficient to allow solidification thereof into said sealing section; and retaining said second mold intact under sufficient pressure to retain a pressed contact between said surface portion of said support section and a mating surface portion of said sealing section, while maintaining said sections at a temperature from about 50° C. to about 400° C. for a time sufficient to cause a bonding between said contacting surface portions to form said unitary seal.
Claim 3
Dependent Claim
71 words
A process as in claim 1, wherein said first injection mold includes a first mold portion and a second mold portion, and said forming step includes maintaining said support section in contact with said first mold portion while separating said second mold portion from both said first mold portion and said support section and then contacting a third mold portion with said first mold portion to form said second injection mold.
Claim 4
Dependent Claim
62 words
A process as in claim 1, wherein said pressed contacting time is at least about 0.5 seconds and including as an added step after said pressed contacting maintaining said unitary seal at a temperature which falls within a range from about 50° C. to about 200° C. for a time sufficient to post-cure and thereby strengthen the bond between the surface portions.
Claim 5
Dependent Claim
32 words
A process as in claim 3, wherein said contacting time falls within a range from about 0.5 seconds to about 30 seconds and said post-curing time is at least about two hours.
Claim 6
Dependent Claim
22 words
A process as in claim 4, wherein said post-curing time falls within a range from about four hours to about forty-eight hours.
Claim 7
Dependent Claim
32 words
A process as in claim 5, wherein the polyurethane elastomer is injected into said second mold at a pressure which falls within a range of about 14 MPa to about 207 MPa.
Claim 8
Dependent Claim
105 words
A process as in claim 6, wherein said sealing section forming temperature falls within a range from about 175° C. to about 225° C., said sealing section forming time falls within a range from about 1 second to about 30 seconds, said support section forming temperature falls within a range from about 260° C. to about 315° C., and said support section forming time falls within a range from about 1 second to about 30 seconds and wherein said second mold is maintained at a temperature which falls within a range from about 40° C. to about 175° C. during injection of said polyurethane elastomer.
Claim 9
Dependent Claim
43 words
A process as in claim 7, wherein said post-curing is at a temperature which falls within a range from about 90° C. to about 125° C. and for a time which falls within a range from about sixteen hours to about twenty-four hours.
Claim 10
Dependent Claim
25 words
A process as in claim 8, wherein the pressure of polyurethane elastomer injection is within a range from about 17 MPa to about 34 MPa.
Claim 11
Dependent Claim
19 words
A process as in claim 9, including removing the unitary seal from the second mold prior to post-curing thereof.
References Cited (Backward Citations)
US2899402A
Cited
US2950266A
Cited
US2976543A
Cited
US3069287A
Cited
US3167323A
Cited
US3271038A
Cited
US3144153A
Cited
US3428725A
Cited
US3413389A
Cited
US3528669A
Cited
US3413183A
Cited
US3443845A
Cited
US3469854A
Cited
US3552755A
Cited
US3657057A
Cited
US3709507A
Cited
US3622427A
Cited
US3822107A
Cited
US3765690A
Cited
US3823577A
Cited
US3919448A
Cited
US3957278A
Cited
US3837660A
Cited
US3771801A
Cited
US3995868A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-25 | 1984-11-24 | 1985-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-25 | 1988-11-24 | 1989-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-25 | 1992-11-24 | 1993-05-26 | $7700.00 | Window Closed / Lapsed |