US4269753A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Siloxane compositions which can be ceramified at high temperatures
Assignee: DuPont Toray Specialty Materials KK
•
Filing: 1980-01-28
•
Granted: 1981-05-26
•
Expires: 2000-01-28
Abstract
Abstract This invention deals with siloxane compositions which can be readily converted to elastomers or resins at normal curing temperatures but will ceramify upon firing to higher temperatures to give flexible ceramics having electrical insulating properties and excellent physical properties.
Inventors
- 👤 Katsutoshi Mine
- 👤 Tsuneo Maruyama
- 👤 Kazuhide Takeshita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 05:43
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/46; C; C08; C08K; C08K3/00; C08K3/01; C08K3/013; C08L; C08L83/00; C08L83/04; C08G; C08G77/00; C08G77/04; C08G77/12; C08G77/14; C08G77/18; C08G77/20; C08G77/42; C08G77/44
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
178 words
A composition of matter consisting essentially of (A) 100 parts by weight of a siloxane copolymer consisting essentially of R 3 SiO 1/2 units and SiO 4/2 units wherein R is a monovalent organic radical having 1-10 carbon atoms and containing at least two unsaturated groups and at least two alkoxy groups bound to silicon atoms per molecule, (B) 0-600 parts by weight of a linear or branched organopolysiloxane polymer having at least two unsaturated groups bound to silicon atoms per molecule, (C) an organopolysiloxane having at least two hydrogen atoms bonded to silicon atoms per molecule, (D) 3-300 parts by weight of a ceramic forming filler substance and, (E) a catalytic amount of an addition reaction catalyst wherein in the components (A), (B) and (C) the mole ratio of hydrogen atoms bound to silicon atoms to unsaturated groups bound to silicon is from 0.5/1 to 10/1 and the total number of unsaturated groups in component (A) and component (B) and the total numer of hydrogen atoms bonded to silicon atoms in component (C) is at least five.
Claim 2
Dependent Claim
178 words
A composition of matter consisting essentially of (A) 100 parts by weight of a siloxane copolymer consisting essentially of R 3 SiO 1/2 units and SiO 4/2 units wherein R is a monovalent organic radical having 1-10 carbon atoms and containing at least two unsaturated groups and at least two alkoxy groups bound to silicon atoms per molecule, (B) 0-600 parts by weight of a linear or branched organopolysiloxane polymer having at least two unsaturated groups bound to silicon atoms per molecule, (C) an organopolysiloxane having at least two hydrogen atoms bonded to silicon atoms per molecule, (D) 3-300 parts by weight of a ceramic forming filler substance and, (E) a catalytic amount of an addition reaction catalyst wherein in the components (A), (B) and (C) the mole ratio of hydrogen atoms bound to silicon atoms to unsaturated groups bound to silicon is from 0.5/1 to 10/1 and the total number of unsaturated groups in component (A) and component (B) and the total numer of hydrogen atoms bonded to silicon atoms in component (C) is at least five.
Claim 3
Dependent Claim
58 words
The composition of claim 1 wherein for every 100 parts by weight of component (A) there is present 0-30 parts by weight of component (B), 5 parts of component (C), 20 to 100 parts by weight of component (D) and 1 part by weight of a one percent solution of chloroplatinic acid in isopropyl alcohol as component (E).
Claim 4
Dependent Claim
99 words
The composition as claimed in claim 1 wherein component (A) is a copolymer consisting essentially of 43 mol% SiO 4/2 units, 30 mol% of (CH 3 ) 3 SiO 1/2 units, 15 mol% of (CH 3 ) 2 (CH 2 ═CH)SiO 1/2 units and 12 mol% CH 2 ═CH(CH 3 O) 2 SiO 1/2 units; component (B) is a vinyldimethyl endblocked polydimethylsiloxane; component (C) is a methylhydrogensiloxane-dimethylsiloxane copolymer; component (D) is selected from a group consisting of zinc oxide powder, alumina powder and mica powder and component (E) is a catalytic amount of chloroplatinic acid in an alcohol solvent.
Claim 5
Dependent Claim
33 words
The composition claimed in claim 3 wherein component (B) is ##STR3## and component (C) is {(CH 3 ) 3 Si} 2 O{(CH 3 ) 2 SiO } 12 (CH 3 HSiO) 6 .
Claim 6
Dependent Claim
10 words
A solid substrate coated with the composition of claim 1.
Claim 7
Dependent Claim
19 words
A solid substrate coated with the composition as claimed in claim 1 and heated in excess of 500° C.
Claim 8
Dependent Claim
17 words
A solid substrate as claimed in claim 5 which is in the form of wire or cable.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-25 | 1984-11-24 | 1985-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-25 | 1988-11-24 | 1989-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-25 | 1992-11-24 | 1993-05-26 | $7700.00 | Window Closed / Lapsed |