Abstract
Abstract A porous fuel cell component, such as an electrode substrate, has a densified edge which forms an improved gas seal during operation when soaked with electrolyte. The edges are made from the same composition as the rest of the component and are made by compressing an increased thickness of this material along the edges during the fabrication process.
Inventors
- 👤 Anthony J. DeCasperis
- 👤 Richard J. Roethlein
- 👤 Richard D. Breault
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 17:29
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/86; H01M4/8636; H01M4/8605; H01M4/861; H01M4/96; H01M8/00; H01M8/02; H01M8/0202; H01M8/023; H01M8/0234; H01M8/0271; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y10; Y10T; Y10T156/00; Y10T156/10; Y10T156/1089; Y10T156/109; Y10T428/00; Y10T428/24; Y10T428/24777; Y10T428/30
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
187 words
In a process for fabricating a fuel cell component comprising a fully graphitized gas porous, resin bonded carbon fiber sheet having first and second oppositely facing surfaces and a pair of parallel edge portions separated by a central portion, wherein said edge portions are more dense than said central portion, the steps of: forming an intermediate product comprising a homogeneous layer of carbon fibers and thermosetting resin, wherein the resin in said intermediate product has not been thermoset, said intermediate product including a pair of parallel edge portions separated by a central portion, said step of forming including building up the thickness of said edge portions such that they are thicker than said central portion with a material having substantially the same composition as said central portion; densifying at least said edge portions by compressing said edge portions to a thickness which is substantially the same as the desired final thickness of said central portion, said step of densifying including applying heat to cure said resin; and heating said edge portions and said central portion to carbonize said resin and fully graphitize said resin and carbon fibers.
Claim 2
Dependent Claim
187 words
In a process for fabricating a fuel cell component comprising a fully graphitized gas porous, resin bonded carbon fiber sheet having first and second oppositely facing surfaces and a pair of parallel edge portions separated by a central portion, wherein said edge portions are more dense than said central portion, the steps of: forming an intermediate product comprising a homogeneous layer of carbon fibers and thermosetting resin, wherein the resin in said intermediate product has not been thermoset, said intermediate product including a pair of parallel edge portions separated by a central portion, said step of forming including building up the thickness of said edge portions such that they are thicker than said central portion with a material having substantially the same composition as said central portion; densifying at least said edge portions by compressing said edge portions to a thickness which is substantially the same as the desired final thickness of said central portion, said step of densifying including applying heat to cure said resin; and heating said edge portions and said central portion to carbonize said resin and fully graphitize said resin and carbon fibers.
Claim 3
Dependent Claim
175 words
A process for fabricating a fuel cell component comprising the steps of: disposing a gas porous strip of thermosetting resin bonded carbon fibers along each of two parallel edge portions of the top surface of a gas porous sheet of thermosetting resin bonded carbon fibers, the resin in said strips and sheet having been melted at a temperature high enough to bond the fibers but not high enough to thermoset said resin, the portion of said sheet between said strips being the central portion of said sheet; laminating said strips and said sheet edge portions to a compressed thickness equivalent to the original thickness of said sheet edge portions by simultaneously heating and applying pressure to said strips and edge portions in a direction perpendicular to said top surface and without compressing said central portion of said sheet, said temperature being sufficiently high to thermoset said resin but not high enough to decompose said resin, said pressure and temperature being applied for sufficient time to rigidize the structure; and carbonizing and fully graphitizing said sheet.
Claim 4
Dependent Claim
175 words
A process for fabricating a fuel cell component comprising the steps of: disposing a gas porous strip of thermosetting resin bonded carbon fibers along each of two parallel edge portions of the top surface of a gas porous sheet of thermosetting resin bonded carbon fibers, the resin in said strips and sheet having been melted at a temperature high enough to bond the fibers but not high enough to thermoset said resin, the portion of said sheet between said strips being the central portion of said sheet; laminating said strips and said sheet edge portions to a compressed thickness equivalent to the original thickness of said sheet edge portions by simultaneously heating and applying pressure to said strips and edge portions in a direction perpendicular to said top surface and without compressing said central portion of said sheet, said temperature being sufficiently high to thermoset said resin but not high enough to decompose said resin, said pressure and temperature being applied for sufficient time to rigidize the structure; and carbonizing and fully graphitizing said sheet.
Claim 5
Dependent Claim
34 words
The process according to claim 2 wherein said step of disposing includes applying a small amount of thermosetting resin between said strips and said edge portions to facilitate bonding during the step of laminating.
Claim 6
Dependent Claim
52 words
The process according to claim 2 wherein the uncompressed thickness and density of the strips is selected such that after lamination each laminated edge will have a mean pore size of less than about 10 microns and an 80% pore size range with an upper limit no greater than about 20 microns.
Claim 7
Dependent Claim
46 words
The process according to claim 4 wherein said component is an electrode for a fuel cell including the additional steps of: applying an electrocatalyst layer to either the top or bottom surface of said central portion of said sheet after said step of carbonizing and graphitizing.
Claim 8
Dependent Claim
47 words
The process according to claim 4 including the step of forming a plurality of parallel grooves in the top or bottom surface of said central portion and applying an electrocatalyst layer to the central portion of the nongrooved surface, said grooves being parallel to said edge portions.
Claim 9
Dependent Claim
20 words
The process according to claim 4, 5, or 6 wherein, said strips and said sheet are substantially the same composition.
Claim 10
Dependent Claim
35 words
The process according to claim 7 wherein the pore size distribution through said laminated edge is uniform, and the density of said laminated edge is two to three times the density of said central portion.
Claim 11
Dependent Claim
134 words
A process for fabricating a fuel cell component comprising the steps of: depositing a homogeneous dry powder mixture of thermosetting resin and carbon fibers on a surface to form an intermediate product, said product including two parallel edge portions, the portion of said product between said edge portions being the central portion of said product, the step of depositing including depositing a greater thickness of said powder mixture along said edge portions than in said central portion; simultaneously curing said product and compacting said product perpendicular to said surface to a uniform thickness throughout and to result in said edge portion having a density between two and three times the density in said central portion; and heating said cured product to carbonize said resin and to subsequently fully graphitize said resin and carbon fibers.
Claim 12
Dependent Claim
134 words
A process for fabricating a fuel cell component comprising the steps of: depositing a homogeneous dry powder mixture of thermosetting resin and carbon fibers on a surface to form an intermediate product, said product including two parallel edge portions, the portion of said product between said edge portions being the central portion of said product, the step of depositing including depositing a greater thickness of said powder mixture along said edge portions than in said central portion; simultaneously curing said product and compacting said product perpendicular to said surface to a uniform thickness throughout and to result in said edge portion having a density between two and three times the density in said central portion; and heating said cured product to carbonize said resin and to subsequently fully graphitize said resin and carbon fibers.
Claim 13
Dependent Claim
26 words
The process according to claim 9 wherein the compacted thickness of said layer is substantially the same in said edge portions as in said central portion.
Claim 14
Dependent Claim
45 words
The process according to claim 10 including the step of forming a plurality of parallel grooves in one surface of said central portion, said grooves being parallel to said edge portions, and applying a layer of electrocatalyst to the opposite surface of said central portion.
Claim 15
Dependent Claim
43 words
The process according to claim 9 wherein said graphitized layer has a top surface and bottom surface, and said process includes the steps of applying a layer of electrocatalyst to one of said surfaces over said central portion thereof to form an electrode.
Claim 16
Dependent Claim
43 words
The process according to claim 9 or 11 wherein the edge portions of said graphitized product have a mean pore size of less than about 10 microns and an 80% pore size range with an upper limit no greater than about 20 microns.
References Cited (Backward Citations)
US3055963A
Cited
US3867206A
Cited
US4035551A
Cited
US4115627A
Cited
US4115528A
Cited
US4165349A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-25 | 1984-11-24 | 1985-05-26 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-25 | 1988-11-24 | 1989-05-26 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-25 | 1992-11-24 | 1993-05-26 | $7700.00 | Window Closed / Lapsed |