Vulcanizable rubber composition
Assignee: Zeon Corp
•
Filing: 1978-07-24
•
Granted: 1981-05-19
•
Expires: 1998-07-24
Abstract
Abstract A vulcanizable rubber composition composed of 100 parts by weight of a terpolymer rubber (A) composed of 35 to 80 mole % of epichlorohydrin, 15 to 50 mole % of ethylene oxide and 5 to 15 mole % of an unsaturated epoxide, 0.2 to 10 parts by weight of a non-sulfur vulcanizing agent, and 0 to 10 parts by weight of a vulcanization aid. A vulcanized rubber prepared from this composition has superior sour gasoline resistance (softening resistance and resistance to embrittlement) and cold resistance. A rubber mixture (B) of an epichlorohydrin-ethylene oxide copolymer rubber and an epichlorohydrin-unsaturated epoxide copolymer rubber containing 35 to 80 mole % of epichlorohydrin, 15 to 50 mole % of ethylene oxide and 5 to 15 mole % of an unsaturated epoxide may be substituted for the terpolymer rubber (A).
Inventors
- 👤 Akio Maeda
- 👤 Kinro Hashimoto
- 👤 Masaaki Inagami
- 👤 Hiroshi Fukushima
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 15:59
CPC Classifications
C; C08; C08G; C08G65/00; C08G65/02; C08G65/04; C08G65/22; C08G65/24; C08K; C08K5/00; C08K5/36; C08K5/37
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
171 words
A method of preventing deterioration of vulcanized rubber products which come into contact with sour gasoline which comprises forming said product from a vulcanizable rubber composition comprising (1) 100 parts by weight of a rubber selected from the group consisting of (A) a terpolymer rubber composed of 35 to 80 mole % of epichlorohydrin, 15 to 50 mole % of ethylene oxide and 5 to 15 mole % of an unsaturated epoxide, and (B) a rubber mixture prepared by mixing an epichlorohydrin-ethylene oxide copolymer rubber with an epichlorohydrin-unsaturated epoxide copolymer rubber so that the mixture will contain 35 to 80 mole % of epichlorohydrin, 15 to 50 mole % of ethylene oxide and 5 to 15 mole % of an unsaturated epoxide; (2) 0.2 to 10 parts by weight of a non-sulfur vulcanizing agent selected from the group consisting of 2-mercaptoimidazolines, 2-mercaptopyrimidines, trithiocyanuric acid and trithiocyanuric acid derivatives; and (3) 0 to 10 parts by weight of a vulcanization aid and allowing said product to come into contact with sour gasoline.
Claim 2
Independent Claim
171 words
A method of preventing deterioration of vulcanized rubber products which come into contact with sour gasoline which comprises forming said product from a vulcanizable rubber composition comprising (1) 100 parts by weight of a rubber selected from the group consisting of (A) a terpolymer rubber composed of 35 to 80 mole % of epichlorohydrin, 15 to 50 mole % of ethylene oxide and 5 to 15 mole % of an unsaturated epoxide, and (B) a rubber mixture prepared by mixing an epichlorohydrin-ethylene oxide copolymer rubber with an epichlorohydrin-unsaturated epoxide copolymer rubber so that the mixture will contain 35 to 80 mole % of epichlorohydrin, 15 to 50 mole % of ethylene oxide and 5 to 15 mole % of an unsaturated epoxide; (2) 0.2 to 10 parts by weight of a non-sulfur vulcanizing agent selected from the group consisting of 2-mercaptoimidazolines, 2-mercaptopyrimidines, trithiocyanuric acid and trithiocyanuric acid derivatives; and (3) 0 to 10 parts by weight of a vulcanization aid and allowing said product to come into contact with sour gasoline.
Claim 3
Dependent Claim
15 words
The method of claim 1 wherein the rubber component (1) is the terpolymer rubber (A).
Claim 4
Dependent Claim
15 words
The method of claim 1 wherein the rubber component (1) is the rubber mixture (B).
Claim 5
Dependent Claim
31 words
The method of claim 2 wherein the unsaturated epoxide constituting the terpolymer rubber (A) is selected from the group consisting of allyl glycidyl ether, glycidyl methacrylate, glycidyl acrylate and butadiene monoxide.
Claim 6
Dependent Claim
37 words
The method of claim 3 wherein the unsaturated epoxide constituting the epichlorohydrin-unsaturated epoxide copolymer rubber in the rubber mixture (B) is selected from the group consisting of allyl glycidyl ether, glycidyl acrylate, glycidyl methacrylate and butadiene monoxide.
Claim 7
Dependent Claim
35 words
The method of claim 3 wherein the epichlorohydrin-ethylene oxide copolymer rubber in the rubber mixture (B) is composed of 30 to 70 mole % of epichlorohydrin and 70 to 30 mole % of ethylene oxide.
Claim 8
Dependent Claim
36 words
The method of claim 3 wherein the epichlorohydrin-unsaturated epoxide copolymer rubber in the rubber mixture (B) is composed of 80 to 90 mole % of epichlorohydrin and 20 to 10 mole % of the unsaturated epoxide.
Claim 9
Dependent Claim
38 words
The method of claim 2 wherein the terpolymer rubber (A) is composed of 48 to 74 mole % of epichlorohydrin, 20 to 40 mole % of ethylene oxide and 6 to 12 mole % of the unsaturated epoxide.
Claim 10
Dependent Claim
20 words
The method of claim 1 wherein the non-sulfur vulcanizing agent is selected from the group consisting of 2-mercaptoimidazolines and 2-mercaptopyrimidines.
Claim 11
Dependent Claim
22 words
The method of claim 1 wherein the non-sulfur vulcanizing agent is selected from the group consisting of trithiocyanuric acid and its derivatives.
Claim 12
Dependent Claim
64 words
The method of claim 1 wherein the vulcanization aid is present in an amount up to 10 parts by weight per 100 parts by weight of rubber and is a metal compound selected from the group consisting of aromatic carboxylic acid salts, saturated aliphatic carboxylic acid salts, carbonates, phosphites, silicates and oxides of metals of Groups IIA, IIB and IVA of the periodic table.
Claim 13
Dependent Claim
19 words
The method of claim 11 wherein the non-sulfur vulcanizing agent is 2-mercaptoimidazoline and the vulcanization aid is red lead.
Claim 14
Dependent Claim
29 words
The method of claim 11 wherein the non-sulfur vulcanizing agent is trithiocyanuric acid, and the vulcanization aid is magnesium oxide or a mixture of magnesium oxide and calcium carbonate.
Claim 15
Dependent Claim
37 words
The method of claim 1 in which the rubber product is a fuel system hose adapted to be connected to an internal combustion engine and the sour gasoline is formed from gasoline in said internal combustion engine.
Claim 16
Dependent Claim
37 words
The method of claim 1 in which the rubber product is a diaphragm or packing adapted to be connected to an internal combustion engine and the sour gasoline is formed from gasoline in said internal combustion engine.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-18 | 1984-11-17 | 1985-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-18 | 1988-11-17 | 1989-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-18 | 1992-11-17 | 1993-05-19 | $7700.00 | Window Closed / Lapsed |