US4268465A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of accelerating the cooling of polymeric articles
Assignee: Massachusetts Institute of Technology
•
Filing: 1979-06-22
•
Granted: 1981-05-19
•
Expires: 1999-06-22
Abstract
Abstract A method of accelerating the cooling of articles made from polymeric particles, such as thermoplastic particles, in which compacted particles are subjected to a heat effect so that selected regions thereof are preferentially heated and the remaining regions thereof remain substantially unheated to produce a heterogeneous temperature distribution within the particles. When the heating effect is removed the preferentially heated regions cool in a rapid fashion by heat transfer therefrom to the unheated regions thereof.
Inventors
- 👤 Nam P. Suh
- 👤 II Lewis Erwin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 23:02
CPC Classifications
B; B30; B30B; B30B15/00; B30B15/34; B29; B29C; B29C35/00; B29C35/02; B29C35/12; B29C43/00; B29C43/006; B29C43/32; B29C43/52; H; H05; H05B; H05B6/00; H05B6/46; B29C35/16; B29K; B29K2105/00; B29K2105/25; B29K2105/251
Claims Analysis
Total Claims: 17
Claim 1
Independent Claim
218 words
A method of forming a solid article from a plurality of polymeric particles, each of said particles having at least one selected region substantially responsive to heating by the application of high frequencey wave energy and at least one remaining region substantially unresponsive to the application of said energy, said method comprising: a. applying pressure and said wave energy to all of said particles in a mold, the selected region of each of substantially all of said particles responding to said applied energy substantially simultaneously so that said selected regions are heated substantially simultaneously by said applied energy to a temperature such that the selected regions of adjacent particles are capable of fusing, the remaining region of each of substantially all of said particles being substantially unresponsive to said applied energy so that said remaining regions are only insubstantially heated by said applied energy, whereby a heterogeneous temperature distribution is produced within each of substantially all of said particles, said selected regions of adjacent particles fusing together; and b. stopping the application of said energy to permit said heterogeneous temperature distribution to proceed to equilibrium by internal heat dissipation within each of substantially all of said particles from said selected regions to said remaining regions, so that said particles become firmly bonded together to from said solid article.
Claim 2
Independent Claim
218 words
A method of forming a solid article from a plurality of polymeric particles, each of said particles having at least one selected region substantially responsive to heating by the application of high frequencey wave energy and at least one remaining region substantially unresponsive to the application of said energy, said method comprising: a. applying pressure and said wave energy to all of said particles in a mold, the selected region of each of substantially all of said particles responding to said applied energy substantially simultaneously so that said selected regions are heated substantially simultaneously by said applied energy to a temperature such that the selected regions of adjacent particles are capable of fusing, the remaining region of each of substantially all of said particles being substantially unresponsive to said applied energy so that said remaining regions are only insubstantially heated by said applied energy, whereby a heterogeneous temperature distribution is produced within each of substantially all of said particles, said selected regions of adjacent particles fusing together; and b. stopping the application of said energy to permit said heterogeneous temperature distribution to proceed to equilibrium by internal heat dissipation within each of substantially all of said particles from said selected regions to said remaining regions, so that said particles become firmly bonded together to from said solid article.
Claim 3
Independent Claim
251 words
A method of forming a solid article, having a preselected shape, from a plurality of polymeric particles, comprising the steps of: a. treating the surface region of each of substantially all of said particles to alter the thermal characteristics thereof, to render said surface regions substantially responsive to heating by the application of high frequency wave energy while the interior of each of substantially all of said particles remains substantially unresponsive to the application of said energy; b. placing said particles in a mold having said preselected shape; c. applying pressure and said wave energy to all of said particles in said mold, the surface region of each of substantially all of said particles responding to said applied energy substantially simultaneously so that all of said surface regions are heated substantially simultaneously by said applied energy to a temperature such that the surface regions of adjacent particles are capable of fusing, the interior region of each of substantially all of said particles, being substantially unresponsive to said applied energy is only insubstantially heated by said applied energy, whereby a heterogeneous temperature distribution is produced within each of substantially all of said particles; said surface regions of adjacent particles fusing together; and d. stopping the application of said energy to permit said heterogeneous temperature distribution to proceed to equilibrium by internal heat dissipation within each of substantially all of said particles from said surface regions to said interior regions, so that said particles become firmly bonded together to form said solid article.
Claim 4
Independent Claim
251 words
A method of forming a solid article, having a preselected shape, from a plurality of polymeric particles, comprising the steps of: a. treating the surface region of each of substantially all of said particles to alter the thermal characteristics thereof, to render said surface regions substantially responsive to heating by the application of high frequency wave energy while the interior of each of substantially all of said particles remains substantially unresponsive to the application of said energy; b. placing said particles in a mold having said preselected shape; c. applying pressure and said wave energy to all of said particles in said mold, the surface region of each of substantially all of said particles responding to said applied energy substantially simultaneously so that all of said surface regions are heated substantially simultaneously by said applied energy to a temperature such that the surface regions of adjacent particles are capable of fusing, the interior region of each of substantially all of said particles, being substantially unresponsive to said applied energy is only insubstantially heated by said applied energy, whereby a heterogeneous temperature distribution is produced within each of substantially all of said particles; said surface regions of adjacent particles fusing together; and d. stopping the application of said energy to permit said heterogeneous temperature distribution to proceed to equilibrium by internal heat dissipation within each of substantially all of said particles from said surface regions to said interior regions, so that said particles become firmly bonded together to form said solid article.
Claim 5
Dependent Claim
11 words
The method of claim 2 wherein said particles are thermoplastic particles.
Claim 6
Dependent Claim
35 words
The method of claim 2 wherein said surface treating step comprises coating the surfaces of said particles with a material which is substantially responsive to heating by the application of said high frequency wave energy.
Claim 7
Dependent Claim
21 words
The method of claim 4 wherein said particles are non-polar thermoplastic particles and said coating material is a polar thermoplastic material.
Claim 8
Dependent Claim
30 words
The method of claim 2 wherein said surface treating step comprises subjecting said particles to a chemical reaction to form a chemically reacted layer at each of the surfaces thereof.
Claim 9
Dependent Claim
27 words
The method of claim 6 wherein said surface treating step comprises exposing said particles to chlorine to form a chlorinated layer on each of the surfaces thereof.
Claim 10
Dependent Claim
62 words
The method of claim 2 wherein said thermal characteristics which are altered are the dielectric loss characteristics and further where: in step (a) said treating provides the surface region of each of substantially all of said particles with a higher dielectric loss characteristic therein than that in the untreated interior region; and in step (c) said wave energy includes alternating electric fields.
Claim 11
Dependent Claim
62 words
The method of claim 2 wherein: step (a) comprises treating said surface regions so as to provide magnetic loss characteristics which are higher than the magentic loss characteristics of said interior regions, and step (c) comprises subjecting said particles in said mold under pressure to alternating magnetic fields having sufficient energy to render the treated surfaces of said particles capable of fusing.
Claim 12
Dependent Claim
27 words
The method of claim 1 wherein: step (a) comprises subjecting said particles to sufficient ultrasonic energy to fuse the surface regions of substantially all of said particles.
Claim 13
Dependent Claim
24 words
The method of claim 1 or of claim 2 wherein said particles each have an average diameter which is at least about 0.5 mm.
Claim 14
Dependent Claim
60 words
The method of claim 2 wherein said particles are selected such that said particles each has an average diameter which is at least about 0.5 mm and the ratio of the average radius of the interior region to the average radius of the surface regions of each of said particles lies in a range from about 0.7 to about 0.9.
Claim 15
Dependent Claim
11 words
The method of claim 12 wherein said ratio is about 0.775.
Claim 16
Dependent Claim
11 words
A product made in accordance with the method of claim 1.
Claim 17
Dependent Claim
11 words
A product made in accordance with the method of claim 2.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-05-18 | 1984-11-17 | 1985-05-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-05-18 | 1988-11-17 | 1989-05-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-05-18 | 1992-11-17 | 1993-05-19 | $7700.00 | Window Closed / Lapsed |